Paraffin emulsion with ultrahigh solid content and preparation method thereof

A technology of ultra-high solid content, paraffin wax emulsion, applied in the field of ultra-high solid content paraffin wax emulsion and its preparation, can solve the problems of large amount of small molecule surfactant, low solid content, negative impact on material properties, etc. effect, the effect of increasing the solid content and enhancing the stability

Active Publication Date: 2012-10-03
安徽斯迈特新材料股份有限公司 +1
View PDF3 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The solid content of the existing paraffin emulsions on the market is generally within 50%, which is basically formed by small molecule surfactants for stabilization, which leads to imperfect performance of the existing paraffin emulsions, an...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] 100 parts by weight of paraffin emulsion contains: 40 parts of water, 55 parts of 56# semi-refined paraffin wax, 1.8 parts of Pingpingjia O-20, 1.2 parts of glycerol monooleate, 1 part of KH570 modified nano-silicon nitride (three-phase bonded The antennae are 78°~80°), 1 part of polyvinyl alcohol 17-88.

[0041] The preparation method of above-mentioned paraffin emulsion is as follows:

[0042] a). Stir and melt the 56# semi-refined paraffin wax in the above proportion in the reaction kettle at 90~95°C, and record it as component A;

[0043] b). Dissolve KH570 modified nano-silicon nitride in 1 / 3 of the formula at 80°C to make a dispersion, which is designated as component B;

[0044] c). Dissolve polyvinyl alcohol 17-88 in 1 / 3 of the formula in 80°C water to make a solution, then mix it with component B to obtain component C;

[0045] d). After the component A in the reactor is completely melted and forms a transparent liquid, keep the temperature of the reactor at ...

Embodiment 2

[0051] 100 parts by weight of the paraffin emulsion contain: 35 parts of water, 60 parts of 56# semi-refined paraffin wax, 1.8 parts of Pingpingjia O-25, 1.2 parts of glycerol monostearate, 1 part of octadecanoic acid modified nano-silicon nitride ( The three-phase contact angle is 70°~75°), 1 part of polyvinyl alcohol 17-88.

[0052] The preparation method is the same as in Example 1, and the solid content of the obtained paraffin emulsion is 60%, and the apparent viscosity of the emulsion at room temperature is 220-250 mPa·s.

[0053]

Embodiment 3

[0055] 100 parts by weight of paraffin emulsion contains: 30 parts of water, 65 parts of 56# semi-refined paraffin wax, 1.8 parts of Pingpingjia O-25, 1.2 parts of glycerol monooleate, 0.5 part of KH570 modified nano-silica (three-phase bonded The antennae are 81°~85°), 1.5 parts of hydroxyethyl cellulose.

[0056] The preparation method is the same as in Example 1, and the solid content of the obtained paraffin emulsion is 60%, and the apparent viscosity of the emulsion at room temperature is 290-320 mPa·s.

[0057]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Apparent viscosityaaaaaaaaaa
Apparent viscosityaaaaaaaaaa
Apparent viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a paraffin emulsion with ultrahigh solid content, which comprises 30%-40% of water, 54%-65% of paraffin, 2%-3% of emulsifying agent, 0.5%-1% of amphiphilic nano particle, and 1%-2% of poval or hydroxyethyl cellulose, wherein the emulsifying agent is fatty alcohol-polyoxyethylene ether and/or glycerin fatty acid ester, and the amphiphilic nano particle is hydrophobic modified nanometer silicon dioxide or nanometer silicon nitride. According to the paraffin emulsion, the amphiphilic nano particle and the macromolecular stabilizing agent are added and are used for stabilizing the paraffin emulsion with ultrahigh concentration together with the micro-molecular surface active agent, so that the solid content of the paraffin emulsion is increased, the stability of the paraffin emulsion is enhanced and the viscosity of the paraffin emulsion is reduced. The apparent viscosity of the paraffin emulsion provided by the invention at normal temperature is 200-350mPa.s and is lower than the viscosity of the frequently used paraffin emulsion at present. The dosage of the micro-molecular surface active agent, namely, the emulsifying agent, is reduced.

Description

technical field [0001] The invention relates to a paraffin wax emulsion with ultra-high solid content and a preparation method thereof which is synergistically stabilized by nanoparticles. Background technique [0002] Paraffin emulsion does not need to be melted or dissolved when used, and has excellent properties such as acid resistance, alkali resistance, and hard water resistance, and has the advantages of safety, high efficiency, economy and convenience. Widely used in various industries, such as waterproofing agent in wood-based panel industry; curing agent for reinforced concrete in construction industry; pulp sizing agent in paper industry; mold release agent in rubber and plastic industries, etc. The solid content of the existing paraffin emulsions on the market is generally within 50%, which is basically formed by small molecule surfactants for stabilization, which leads to imperfect performance of the existing paraffin emulsions, and there are still some problems,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L91/06C08L71/02C08L29/04C08L1/26C08K13/06C08K9/06C08K9/04C08K3/36C08K3/34C08K5/103
Inventor 田建国夏茹郝家宝
Owner 安徽斯迈特新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap