A kind of preparation method of spherical lithium ion battery positive electrode material and its precursor

A technology of lithium ion battery and positive electrode material, which is applied in battery electrodes, circuits, electrical components, etc. to achieve good cycle performance and good charge-discharge reversibility.

Active Publication Date: 2015-08-12
ZHENGZHOU UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this method can be used to prepare spherical lithium ion cathode material precursors, it needs to strictly control the preparation conditions to ensure the uniformity of the material particles.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of spherical lithium ion battery positive electrode material and its precursor
  • A kind of preparation method of spherical lithium ion battery positive electrode material and its precursor
  • A kind of preparation method of spherical lithium ion battery positive electrode material and its precursor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Preparation of nano-nickel hydroxide: 0.015mol of NiCl 2 ·6H 2 0, 0.03mol of NaOH, respectively dissolved in 25mL water to form a solution, mix the two in a reaction kettle, place them in an oven at 180°C for 24 hours, separate and dry to obtain nano-nickel hydroxide .

[0022] Preparation of lithium-ion battery cathode material: 0.25 g of the prepared nano-nickel hydroxide was dispersed in 50 mL of distilled water, and 2.57 g of CoCl 2 ·6H 2 O was dissolved in the above system, and the resulting mixture was placed in a reaction kettle and reacted in an oven at 200 °C for 24 hours. After the reaction was completed, it was naturally cooled to room temperature, centrifuged and dried at 60 °C to obtain spherical lithium-ion battery materials. precursor, whose shape is as figure 1 shown in a. Depend on figure 1 It can be seen that the precursor is in the form of spherical particles, and its particle size distribution is relatively uniform, mainly between 8-10 mi...

Embodiment 2

[0025] 0.25 g of the prepared nano-nickel hydroxide was dispersed in 50 mL of distilled water, and 1.93 g of CoCl 2 ·6H 2 O is dissolved in the above system, and the resulting mixture is placed in a reaction kettle and reacted in an oven at 200 °C for 24 hours. After the reaction is completed, it is naturally cooled to room temperature, centrifuged and dried at 60 °C to obtain a spherical lithium-ion battery material precursors.

[0026] Take 1 g of the lithium-ion battery material precursor prepared in the above steps and grind and mix them with 0.28 g of LiOH. After mixing, program the temperature in a muffle furnace to 500 ° C for 5 hours, then calcinate at 750 ° C for 12 hours, and cool naturally After that, the spherical lithium-ion battery material (LiNi 0.23 co 0.77 o 2 ).

Embodiment 3

[0028] 0.25 g of the prepared nano-nickel hydroxide was dispersed in 50 mL of distilled water, and 1.28 g of CoCl 2 ·6H 2 O was dissolved in the above system, and the resulting mixture was placed in a reaction kettle and reacted in an oven at 200 °C for 24 hours. After the reaction was completed, it was naturally cooled to room temperature, and dried at 60 °C after centrifugation to obtain spherical lithium-ion battery materials. Precursor.

[0029] Take 1 g of the lithium-ion battery material precursor prepared by the above steps and grind and mix them with 0.28 g of LiOH. After mixing, program the muffle furnace to 500 ° C for 5 hours, then calcinate at 750 ° C for 12 hours, and cool naturally After that, the spherical lithium-ion battery material (LiNi 0.44 co 0.56 o 2 ).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a spherical lithium ion battery anode material and a preparation method of a precursor thereof. The preparation method comprises the following steps of: with newly-prepared nano flaky nickel hydroxide as a raw material, dispersing the raw material in an aqueous solution, adding a certain proportion of cobalt salt into the aqueous solution, reacting for several hours in an enclosed vessel to obtain uniform spherical granules which can be used as a precursor for preparing the lithium ion battery anode material; and uniformly mixing the obtained precursor granules and a lithium salt and carrying out high-temperature calcining to finally obtain the spherical lithium ion battery anode material with uniform granule size. The preparation method disclosed by the invention is simple to operate, high in efficiency, easy in obtainment of raw material, low in cost and environment-friendly; and the prepared spherical lithium battery anode material has good electrochemical property.

Description

Technical field [0001] The present invention is a lithium -ion battery technology field, which involves a preparation method for a spherical lithium -ion battery orthophyllum material and its preliminary drive. Background technique [0002] At present, lithium -ion batteries are research hotspots for the power system used by various mobile communication equipment and electric vehicles such as green transportation.The performance of lithium -ion batteries largely depends on the performance of its key materials, and the performance of improved material is a long -term and difficult process. [0003] As a key active material for lithium ion batteries, the shape of the particles directly affects the performance of the material.The spherical shape is the best shape of the active material of commercial batteries. This spherical particle has good liquidity and is convenient for the mixing when preparing poles. In addition, it can also increase the filling of the material and enable the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/525
CPCY02E60/122Y02E60/10
Inventor 陈卫华张建民米立伟王爽姚亚婷郑文露孟阵李绍兰梦
Owner ZHENGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap