Vacuum suction casting equipment and method of high-activity, high-purity and high-melting-point alloy

A vacuum suction casting, high-purity technology, applied in the field of metal material casting metallurgy, can solve the problems of metal type suction casting not suitable for high temperature structure, easy pollution success rate, etc., achieve the effect of short melting time, simple equipment structure and convenient operation

Inactive Publication Date: 2014-09-24
INST OF METAL RESEARCH - CHINESE ACAD OF SCI
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of the above-mentioned deficiencies in the prior art, the technical problem to be solved by the present invention is to provide a pollution-free suction casting equipment for high-activity, high-purity and high-melting point alloys, so as to solve the inapplicability of metal mold suction casting in the prior art. For active high-melting point alloys such as high-temperature structures, intermetallic compounds, and titanium alloys, there are problems such as easy pollution or low success rate during suction casting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Vacuum suction casting equipment and method of high-activity, high-purity and high-melting-point alloy
  • Vacuum suction casting equipment and method of high-activity, high-purity and high-melting-point alloy
  • Vacuum suction casting equipment and method of high-activity, high-purity and high-melting-point alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Put 20-300g of the prepared master alloy ingot 8 into the alloy ingot crucible 4, place the mold 6 in the vacuum chamber 2 directly below it, make the through hole 5 communicate with the upper vacuum chamber and the lower vacuum chamber; close the vacuum chamber 1 and the lower vacuum chamber 2, and simultaneously evacuate to 2×10 -2 Above Pa, then filled with high-purity argon to P 1 Turn on the water circulation 7, turn on the arc torch 9 for argon arc smelting, when the surface layer of the master alloy ingot 8 is completely melted, the through hole 5 will be automatically liquid-sealed to separate the upper vacuum chamber and the lower vacuum chamber; at this time, keep the power of the arc torch unchanged, Continue to fill the vacuum chamber 1 with high-purity argon to P 2 , form the upper and lower pressure difference △P= P 2 -P 1, to ensure that △P is greater than zero; after that, continue to increase the melting power of the arc torch. After a few minutes, t...

Embodiment 2

[0040] According to the mass ratio of the alloy components and the law of burning loss compensation, a 10-100g TiAl alloy package is prepared by using high-purity raw materials in a certain proportion, which is placed in a copper crucible 3 and vacuumed to 5×10 -3 Above Pa, then inject high-purity argon gas with a pressure of 0.02-0.06 MPa; perform low-current arcing under visual conditions, and gradually increase the melting current to avoid splashing of raw materials; melt the alloy package evenly and thoroughly with the assistance of electromagnetic stirring , and the arc is closed and solidified into a master alloy ingot; then it is turned over and smelted, and this process is repeated 3-10 times, thereby obtaining a master alloy ingot 8 with high purity, high uniformity and high precision, such as figure 2 As shown, it can be seen from the figure that the prepared master alloy ingot has a smooth surface and good uniformity. After testing, it has high purity and few impuri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
sizeaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention is a vacuum suction casting equipment and method for alloys with high activity, high purity and high melting point. The equipment includes an upper vacuum chamber and a lower vacuum chamber arranged up and down. An arc torch is arranged on the top of the upper vacuum chamber, and multiple stations are arranged on the bottom. The copper crucible seals the upper vacuum chamber and the lower vacuum chamber. Water cooling; one of the station copper crucibles is tightly fitted with an alloy ingot crucible, and a through hole is left at the bottom to connect the upper vacuum chamber with the lower vacuum chamber. High-melting point alloy ingots with holes at the bottom, good conductivity and large heat capacity are used to replace nozzles such as graphite, embedded in copper crucibles to form an indirect water-cooled structure, combined with automatic suction casting by pressure difference method, which solves the problem of this type of alloy in the existing suction casting There are problems such as easy pollution and low success rate in the equipment. Effectively realize the clean suction casting process of this type of alloy. The melting point of the suction casting alloy can reach 1600-1800°C, and the pollution degree is ≤0.01wt.%.

Description

technical field [0001] The invention relates to the field of casting and metallurgy of metal materials, in particular to a vacuum suction casting equipment and method for alloys with high activity, high purity and high melting point. Background technique [0002] Materials such as high-temperature structures, intermetallic compounds, and titanium alloys have broad application prospects in the fields of energy, medical care, and aerospace. Most of them have the characteristics of high purity, high activity and high melting point, so ingot metallurgy and precision casting of such alloys have become the difficulties and hot spots of applied research. Differential pressure suction casting is a mature and commonly used forming technology, but currently it is mainly aimed at low melting point alloys and amorphous alloys below 1300 °C. As far as the existing mature suction casting equipment is concerned, no matter whether it is gravity suction casting, anti-gravity suction casting...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22D18/06
Inventor 刘荣华崔玉友张德志谭景全刘冬刘羽寅杨锐
Owner INST OF METAL RESEARCH - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap