Oral liquid rubber plug material and preparation method thereof

A technology for oral liquid and rubber stoppers, which is applied in the field of chemical materials and can solve problems such as the influence of users, difficult processing, and poor performance

Active Publication Date: 2014-11-05
应城市恒天药业包装有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the material performance of the existing rubber stoppers for oral liquids is not good, and there are defects such as large processing difficulty and poor sealing performance, and some of them also release some odors, which affect the mouthfeel of oral liquids and cause certain impacts on users.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] The present invention is formed by mixing the following raw materials according to weight percentage: 40% of butyl rubber, 20% of ethylene-propylene copolymer, 30% of filler, 9% of phenolic resin, 1% of coloring agent, and the filler consists of pottery clay, talcum powder, white carbon Black is mixed in a weight ratio of 2:1:1; the viscosity-average molecular weight of butyl rubber is 80,000, the Mooney viscosity ML1+8 (100 °C) is 40 to 70, and the degree of unsaturation is 0.7~1.5mol%. The melting point of ethylene-propylene copolymer is ≤120°C. The preparation method is that the above-mentioned materials are kneaded in a mixer, mixed at 130°C to 190°C, preferably at 140°C to 160°C, and molded by compression molding or injection molding.

Embodiment 2

[0015] The present invention is formed by mixing the following raw materials according to weight percentage: 30% of butyl rubber, 15% of ethylene-propylene copolymer, 50% of filler, 3.5% of phenolic resin, 1.5% of coloring agent, and the filler consists of clay, talcum powder, white carbon Black is mixed in a weight ratio of 2:1:1; the viscosity-average molecular weight of butyl rubber is 80,000, the Mooney viscosity ML1+8 (100 °C) is 40 to 70, and the degree of unsaturation is 0.7~1.5mol%. The melting point of ethylene-propylene copolymer is ≤120°C. The preparation method is that the above-mentioned materials are kneaded in a mixer, mixed at 130°C to 190°C, preferably at 140°C to 160°C, and molded by compression molding or injection molding.

Embodiment 3

[0017] The present invention is formed by mixing the following raw materials according to weight percentage: 40% of butyl rubber, 10% of styrene-based elastomer, 50% of filler, 9.5% of phenolic resin, 0.5% of colorant, and the filler consists of clay, talcum powder, white carbon Black is mixed in a weight ratio of 2:1:1; the viscosity-average molecular weight of butyl rubber is 80,000, the Mooney viscosity ML1+8 (100 °C) is 40 to 70, and the degree of unsaturation is 0.7~1.5mol%. The melting point of ethylene-propylene copolymer is ≤120°C. The preparation method is that the above-mentioned materials are kneaded in a mixer, mixed at 130°C to 190°C, preferably at 140°C to 160°C, and molded by compression molding or injection molding.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to a rubber material and particularly relates to an oral liquid rubber plug material and a preparation method thereof. The rubber plug material is formed by mixing the following raw materials by weight: 20%-40% of synthetic rubber, 10%-20% of thermoplastic elastomer, 30%-50% of fillers, 3%-10% of cross-linking agents and 0.5%-1.5% of coloring agents, wherein the synthetic rubber is butyl rubber, polyisobutene rubber or halogenated butyl rubber; the thermoplastic elastomer is cinnamenyl elastomer or polyolefin thermoplastic elastomer; the fillers are one or more of syderolite, talc powders and white carbon black; the cross-linking agents are metallic oxides or phenolic resins; and the coloring agents are titanium dioxide, carbon black or a mixture of the titanium dioxide and the carbon black. The prepared oral liquid rubber plug material is good in mechanical strength and elasticity and capable of meeting usage requirements and processing requirements of an oral liquid rubber plug and also meeting requirements of compatibility with contacted liquid drugs after sealing.

Description

technical field [0001] The invention relates to a chemical material, in particular to a rubber stopper material for oral liquid and a preparation method thereof. Background technique [0002] There are many kinds of rubber stoppers for oral liquids currently used in the market, and the materials are various. However, the material properties of the existing rubber stoppers for oral liquids are not good, and there are defects such as high processing difficulty and poor sealing performance, and some of them also release some odors, which affect the mouthfeel of oral liquids and cause certain impacts on users. Contents of the invention [0003] The purpose of the present invention is to provide a new type of oral liquid rubber stopper material for the defects of the existing oral liquid rubber stopper material formula, which can not only meet the use requirements and processing requirements of oral liquid rubber stoppers, but also meet the requirements of the contact surface a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/22C08L23/28C08L25/04C08L23/16C08L61/06C08K3/34C08K3/36C08K3/22C08K3/04
Inventor 夏汉桥黄爱华张雾云
Owner 应城市恒天药业包装有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap