Preparation method of Al2O3/TiO3 ceramic stick for flame spraying

A flame spraying and ceramic rod technology, which is applied in the field of Al2O3/TiO2 ceramic rods for flame spraying and its preparation, can solve the problems of inability to meet industrialized production, low qualified rate of finished products, increase processing cost, etc., achieve good mechanical properties, and reduce waste products. efficiency, improve production efficiency

Active Publication Date: 2013-01-16
HEFEI RUIYONG CERAMIC MATERIAL TECH
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The obtained oxide ceramic rod has good spraying performance, and the ceramic coating formed after spraying has good mechanical properties, and also has good heat insulation, insulation, corrosion resistance, etc., but this patented process There are the following deficiencies: 1. Agate balls and alcohol medium are added during the ball milling, so that the ball milling is more uniform, but at the same time, the original edges and corners of each raw material are ground away, and the cohesion between the materials is reduced. When sintered at high temperature, it is easy to deform, which reduces the pass rate and increases the processing cost;
[0004] 2. When degumming and high-temperature sintering, the hanging sintering method is adopted. This sintering method has strict requirements on the specific gravity of the main raw material. For the main raw material, zirconia ceramic rods with too large specific gravity or aluminum oxide with too light specific gravity / Titanium dioxide ceramic rod material, large specific gravity is easy to fall and break when hanging and firing, and light specific gravity is easy to deform when hanging and firing, resulting in extremely low qualified rate of finished products, very low production efficiency and high scrap rate, which cannot meet the needs of industrial production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of Al2O3/TiO3 ceramic stick for flame spraying
  • Preparation method of Al2O3/TiO3 ceramic stick for flame spraying

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0035] The selected formula is: 60%Al 2 o 3 +1.50%SiO2 2 +0.1%Fe 2 o 3 +37.05%TiO 2 + 0.20%CaO+1%MgO+0.15%NaO 2 Weigh the ingredients, put them into the ball mill tank and carry out dry mixing for 4 hours directly. After the mixed powder is discharged, it is directly added to the high-temperature box-type electric furnace, and it is sintered at 1600°C for 23 hours at a high temperature, and then it is crushed out of the furnace and passed through 280°C. mesh vibrating sieve; mix 75 parts of deionized water with 5 parts of allyloxy hydroxypropyl sodium sulfonate and 6.5 parts of polyethylene glycol 200, stir at high speed until the emulsification is sufficient, then heat up in a water bath until the temperature rises to 75 °C , add 18 parts of styrene, 8 parts of hydroxyethyl methacrylate and 0.4 parts of sodium persulfate completely dissolved in 5 parts of acrylic acid and 25 parts of deionized water, then raise the temperature to 88°C, keep it warm for about one hour, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an Al2O3 / TiO3 ceramic stick for flame spraying. The preparation method comprises the following steps of: weighing ceramic raw materials, and batching; processing via ball milling; then blending in a dry way, so as to obtain mixed powder; adding modification styrene-acrylic emulsion and the like in the powder; mixing the materials; preparing and pugging; transferring the plastic clay block into a vacuum extruder to be extruded and formed; heating to degum through a horizontal burning way; and finally roasting at a certain temperature, thus obtaining the Al2O3 / TiO3 ceramic stick. The preparation method disclosed by the invention is simple in technology, high in product percent of pass, and greatly reduces producing coat. The prepared ceramic stick has a better coating performance; and the coated ceramic coating has a better mechanical property, and synchronously has a better heat insulation property, an insulating property, a corrosion resistance property, an antistatic property and high smoothness of a spray coating layer, and no static generated in friction at high speed, and the like, and has a good application prospect in cotton spinning and chemical fiber industries.

Description

technical field [0001] The invention relates to the field of ceramic preparation, in particular to an Al 2 o 3 / TiO 2 Ceramic rod and its preparation method. Background technique [0002] With the development of science and technology, ceramic printing technology has gradually been widely used. At present, the relatively mature ceramic spraying technology mainly includes plasma spraying and flame spraying technology. Among them, the application of the plasma spraying method in the industry is limited due to reasons such as complex process equipment, high price, inconvenient maintenance, and troublesome operation. Flame spraying technology has simple equipment, strong versatility, and simple process methods, so it has been widely used. According to the different spraying raw materials used, flame spraying technology is divided into powder flame spraying and ceramic rod flame spraying. For powder flame spraying, since the ceramic powder particles are heated by the flame ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/10C04B35/622
Inventor 许太昌
Owner HEFEI RUIYONG CERAMIC MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products