Preparation method of thick paperboard with high bonding strength between paperboards

A technology of interlayer bonding strength and thick cardboard, applied in paper, papermaking, textiles and papermaking, etc., can solve the problems of easy pulp loss, easy delamination, poor dehydration of formed wet paper pages, etc., to increase bonding points and bonding force , Improve the retention rate, improve the effect of bonding strength

Active Publication Date: 2015-06-17
JIANGXI JIEMEI ELECTRONICS INFORMATION MATERIAL CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing thick cardboard is generally made of pulp with high beating degree, but because the pulp with high beating degree is difficult to filter water in the papermaking wire, the dehydration of the formed wet paper is poor, and it is easy to lose pulp, foam and wrinkles when producing thick cardboard. Paper defects, and more power consumption is required to increase the beating degree, and although the pulp with low beating degree is better in water filtration, due to the poor separation of pulp fibers and poor interweaving force between fibers, the interlayer of the paperboard made Poor bonding strength, easy to delaminate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of thick paperboard with high bonding strength between paperboards

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The specific implementation manner of the present invention will be described in detail below in conjunction with the accompanying drawings.

[0017] Such as figure 1 The preparation method of the cardboard of a kind of high cardboard interlayer bonding strength shown, this method utilizes beating degree to be 20 o SR~35 oSR After the pulp is formed on the Internet to form wet paper sheets, spray the mist adhesive aqueous solution between the wet paper layers, such as spraying the mist adhesive solution after the wet paper sheets are formed on the No. Aqueous mixture solution, the aqueous binder solution is one of starch, modified polyacrylamide or a mixture thereof, and the concentration of the aqueous binder solution is 0.5% to 6.0%. Then enter the return roller, the main pressure roller, and the press roller to be bonded together, and then dry the first part of the dryer for surface treatment, then enter the second part of the dryer for drying, pass through the ca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a thick paperboard, in particular to a preparation method of a thick paperboard with high bonding strength between paperboards. In the preparation method, a fog-like adhesive water solution is sprayed between wet paper layers before the wet paper formed on a net by pulp with beating degree of 20-35oSR are mutually bonded; the adhesive water solution is one of starch, polyacrylamide modified substance or a mixture of starch and the polyacrylamide modified substance; and the concentration of the adhesive water solution is 0.5-6.0%. The preparation method has following advantages that: 1, manufacturing paper with pulp is easy, and energy can be saved; and 2, the effect of improving bonding strength is notable, and a certain effect in improving retention of the pulp and chemical materials is realized. In addition, the preparation method increases bonding point and bonding force between the adhesive and pulp fibers so as to greatly improve bonding strength between the paperboards.

Description

technical field [0001] The invention relates to a method for preparing thick cardboard. Background technique [0002] Existing thick cardboard is generally made of pulp with high beating degree, but because the pulp with high beating degree is difficult to filter water in the papermaking wire, the dehydration of the formed wet paper is poor, and it is easy to lose pulp, foam and wrinkles when producing thick cardboard. Paper defects, and more power consumption is required to increase the beating degree, and although the pulp with low beating degree is better in water filtration, due to the poor separation of pulp fibers and poor interweaving force between fibers, the interlayer of the paperboard made Poor bonding strength, easy to delaminate. Contents of the invention [0003] In order to solve the above-mentioned technical problems, the object of the present invention is to provide a method for preparing thick cardboard with high bonding strength between cardboard layers...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H17/28D21H17/55
Inventor 姜兆宏
Owner JIANGXI JIEMEI ELECTRONICS INFORMATION MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com