Waterproof and antiflaming PVC (polyvinyl chloride) cable material and preparation technology thereof

A technology of cable material and degree of polymerization, applied in the direction of insulated cables, cables, circuits, etc., can solve the problems of rising cost, difficult to meet the requirements of product index performance, unqualified thermal deformation, etc. make a difference

Active Publication Date: 2013-04-17
SUZHOU HENGLI COMM MATERIAL
View PDF4 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is difficult to find the existing technology from the literature, but generally using high-quality plasticizers, reducing or not using fillers, the product index performance is still difficult to meet the requirements, and it is easy to cause thermal deformation and other indicators to fail, and the cost rises and other problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof and antiflaming PVC (polyvinyl chloride) cable material and preparation technology thereof
  • Waterproof and antiflaming PVC (polyvinyl chloride) cable material and preparation technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1~3

[0040] Embodiments 1-3: A water-resistant and flame-retardant PVC cable material, the water-resistant and flame-retardant PVC cable material is composed of the following components by weight, as shown in Table 1:

[0041] Table 1

[0042]

[0043] All the above are parts by weight.

[0044] The above-mentioned silane coupling agent is vinyl tris(β-methoxyethoxy) silane, vinyl trimethoxy silane or γ-glycidyl etheroxypropyl trimethoxy silane.

[0045] The above-mentioned silane coupling agent is vinyl tris (β-methoxyethoxy) silane, vinyl trimethoxy silane and γ-glycidyl etheroxypropyl trimethoxy silane mixed in a ratio of 10:5:3 by weight .

[0046] Above-mentioned lubricant embodiment 1 is polyethylene wax, lubricant embodiment 2 is stearic acid, lubricant embodiment 3 is the compound of polyethylene wax and stearic acid.

[0047] The above antioxidant embodiment 1 is tetrakis [3-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid] pentaerythrit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a waterproof and antiflaming PVC (polyvinyl chloride) cable material and a preparation technology thereof. The waterproof and antiflaming PVC cable material comprises the following components in parts by weight: 55-65 parts of PVC of degree of polymerization of 590-720, 35-45 parts of PVC of degree of polymerization of 1110-1340, 20-30 parts of trioctyl trimellitate, 15-25 parts of didecyl phthalate,5-10 parts of environmental protection calcium and zinc compound stabilizer, 5-10 parts of compound rare earth stabilizer, 4-8 parts of antimonous oxide, 0.3-1 parts of lubricant, 0.1-0.5 parts of antioxygen, 3.5-7 parts of nano barium sulfate, 2.6-5.2 parts of calcined kaolin, 3.5-7 parts of nano silica, and 0.18-0.36 parts of silane coupling agent, wherein the silane coupling agent is vinyl (beta-methoxy-ethoxy) silane, vinyl trimethoxy silane or gamma-glycidyl ether oxygen propyl three methoxy-silane. The hydroscopicity of a cable jacket is greatly lowered, when the cable material is used in wet or soaking environment, the stable property of electric is further improved and does not change generally, and the compact of the product is improved and the micropores of the material are removed.

Description

technical field [0001] The invention relates to a PVC cable material and a preparation process thereof, in particular to a water-resistant and flame-retardant PVC cable material and a preparation process thereof. Background technique [0002] PVC cable insulation material is one of the general-purpose synthetic plastics, and it is the second largest plastic species in the world after polyethylene. Due to its good mechanical and physical properties, electrical properties, simple processing technology, excellent processing performance and low price, PVC cable material has always been in the forefront of the cable material industry and is widely used. PVC cable materials are generally used in medium and low voltage, data communication cables and other products, general-purpose wire and cable products, PVC cable materials can basically meet the requirements of insulation and sheathing. However, with the expansion of wire and cable applications, the requirements for PVC cable ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08K13/06C08K5/12C08K3/22C08K3/30C08K3/34C08K3/36H01B7/17
CPCC08K2201/011C08L27/06C08L2201/02C08L2203/202C08L2205/025C08L2205/03H01B3/443H01B7/17H01B7/18C08K13/06C08K9/06C08K9/00C08K5/12C08K3/2279C08K2003/3045C08K3/346C08K3/36C08L23/06C08K5/09
Inventor 程晓松于德宝王小菲孙玉萍李凤彪
Owner SUZHOU HENGLI COMM MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com