Electron beam welded joint, steel material for use in electron beam welded joint, and manufacturing method thereof

A technology for electron beam welding and steel materials, applied in the direction of electron beam welding equipment, welding/welding/cutting items, welding/cutting media/materials, etc.

Active Publication Date: 2014-08-20
NIPPON STEEL CORP
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

No welding wire is used in the usual electron beam welding method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electron beam welded joint, steel material for use in electron beam welded joint, and manufacturing method thereof
  • Electron beam welded joint, steel material for use in electron beam welded joint, and manufacturing method thereof
  • Electron beam welded joint, steel material for use in electron beam welded joint, and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment ）

[0181] Steel materials having the composition shown in Table 1 and Table 2 were used, and steel materials were produced under the conditions shown in Table 3 and Table 4. Collect test pieces from steel, conduct tensile test and CTOD test, and measure the tensile strength and fracture toughness of steel (base material). The strength of the steel material (base material) was measured based on JIS Z2241 by collecting a test piece from the 1 / 2 part of the plate thickness with the rolling direction as the longitudinal direction. In addition, steel materials with a yield stress of 355 to 420 MPa were evaluated as good.

[0182] Electron beam welding is performed on steel materials to produce I-groove butt weld joints. For electron beam welding, the RPEBW method is adopted, using pure Ni foil as the fillet, under the conditions of a voltage of 175V, a current of 120mA, and a welding speed of about 125mm / min under a vacuum of about 1mbar. The weld width is 3.0-5.5mm. Samples are co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
heightaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The present invention provides a steel material for electron beam welding, which contains at least C: 0.02% to 0.10%, Si: 0.03% to 0.30%, Mn: 1.5% to 2.5%, Ti: 0.005% to 0.015%, in mass %. N: 0.0020% ~ 0.0060%, O: 0.0010% ~ 0.0035%, Mg: 0.0003% ~ 0.0027%, Ca: 0.0003% ~ 0.0027%, limit Al to 0.015% or less, limit P to 0.015% or less, S It is limited to less than 0.010%, and the remaining part is composed of iron and unavoidable impurities; it satisfies 0.0006% ≤ Mg + Ca ≤ 0.0040%, and the index value CeEBB is 0.42% ~ 0.65%. In the plate along the thickness direction of the steel plate In the thick center part, the number of oxides with a circle equivalent diameter of 1.0 μm or more is 20 / mm2 or less, and in the plate thickness center part, the plate thickness center part contains 7% or more Mg and the circle equivalent diameter is 0.05 μm or more and less than 0.5 μm. The number of oxides is 1×103~1×105 / mm2.

Description

technical field [0001] The present invention relates to a steel material for electron beam welding which is welded by irradiating an electron beam to a welded part with a plate-like or foil-like fillet sandwiched between the groove surface and a manufacturing method thereof, and also relates to a steel material for welding by irradiating an electron beam on the groove surface of the steel material. An electron beam welded joint formed by irradiating electron beams to the welded part holding the fillet between the surfaces. [0002] This application claims priority based on Japanese Patent Application No. 2010-260582 for which it applied in Japan on November 22, 2010, and uses the content here. Background technique [0003] In recent years, in response to one of the causes of global warming, CO 2 With the reduction of gas and the depletion of fossil fuels such as oil in the future, we are actively trying to use renewable natural energy. Wind power generation is also expecte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/00B23K15/00B23K35/30C21D8/02C22C19/03C22C38/14C22C38/58F03D13/25F03D80/00
CPCC22C38/12B23K15/0053C22C38/14B23K35/3073C22C38/06C22C38/04B23K35/3033C22C38/001C22C38/002B23K2203/04C22C38/08C22C38/16C22C38/02B23K2103/04
Inventor 植森龙治本间竜一石川忠儿岛明彦星野学
Owner NIPPON STEEL CORP