Thermal-resistant light-smoke halogen-free flame-retardant PC/ABS alloy material and preparation method thereof

An alloy material and heat-resistant technology, applied in the field of alloy materials, can solve the problems of reducing thermal deformation temperature and impact strength, large smoke generation, fast smoke diffusion, etc., to improve temperature resistance and flame retardancy, and reduce smoke density , the effect of simple operation

Active Publication Date: 2014-12-17
中广核俊尔(上海)新材料有限公司 +1
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] 1. General flame retardant materials generate a large amount of smoke during combustion, and release toxic, corrosive, and carcinogenic gases. The smoke spreads quickly and the visibility is low. Once it catches fire, it will cause great problems.
[0007] 2. Brominated flame retardants are being used less due to toxicity, while halogen-free and environmentally friendly phosphorus-based flame retardants will significantly reduce heat distortion temperature and impact strength
The alloy adopts a heat-resistant modifier, which has strong heat resistance, but the amount of smoke is not ideal, and it cannot meet the international environmental standards such as the German VDE 0472 (815) with a smoke density of less than 400.
[0010] Combining the existing PC / ABS alloys, it is difficult to achieve a comprehensive balance in terms of heat resistance, low smoke, and high-efficiency flame retardancy. Therefore, it is necessary to develop a PC / ABS alloy with high heat resistance, low smoke, and high-efficiency halogen-free flame retardancy. ABS alloy material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermal-resistant light-smoke halogen-free flame-retardant PC/ABS alloy material and preparation method thereof
  • Thermal-resistant light-smoke halogen-free flame-retardant PC/ABS alloy material and preparation method thereof
  • Thermal-resistant light-smoke halogen-free flame-retardant PC/ABS alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-2 and comparative example 1-3

[0075] Add the raw materials into the high-speed mixer (10000 rpm) and stir for 2 minutes, mix evenly, and then add them to the twin-screw extruder to extrude and granulate. The temperature from the feed section to the head of the twin-screw extruder is respectively : 240°C±5°C, 260°C±5°C, 260°C±5°C, 260°C±5°C, 255°C±5°C, 250°C±5°C, 250°C±5°C, 250°C±5°C, 250°C ℃±5℃, die head: 260℃±5℃;

[0076] After water cooling and pelletizing, the pellets were dried in a blast drying oven at 110° C. for 4 hours to obtain a heat-resistant, halogen-free, flame-retardant PC / ABS alloy material.

[0077] The prepared heat-resistant halogen-free flame-retardant PC / ABS alloy material was prepared by an injection molding machine for testing samples.

[0078] Table 1 Raw material composition distribution ratio

[0079] components

[0080] Toughener MBS

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
heat deflection temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a thermal-resistant light-smoke halogen-free flame-retardant PC (polycarbonate) / ABS (acrylonitrile-butadiene-styrene terpolymer) alloy material and a preparation method thereof. The alloy material comprises the following raw material in percentage by weight: 60%-80% of PC resin, 5%-20% of ABS resin, 6%-15% of halogen-free flame retardant, 5%-15% of thermal-resistant modifier, 0.1%-2% of inorganic complex antismoke agent, 0%-10% of flexibilizer and 1%-5% of other processing agents. According to the invention, the thermal-resistant light-smoke halogen-free flame-retardant PC / ABS alloy material can be obtained by a manner of adopting the PC and ABS resins as the substrates and using the synergistic interaction of the thermal-resistant modifier, the halogen-free flame retardant and the inorganic complex antismoke agent; and the alloy material can be widely applied to the industries, such as communications industries, automobile industries, building materials, decoration materials, cables and electrical appliance industries. The preparation method of the alloy material adopts the existing equipment, and the operation is simple, so that the method is suitable for industrial production.

Description

technical field [0001] The invention relates to the field of alloy materials, in particular to a heat-resistant low-smoke halogen-free flame-retardant PC / ABS alloy material and a preparation method thereof. Background technique [0002] Blending polycarbonate (PC) and acrylonitrile-butadiene-styrene copolymer (ABS) in a certain proportion to make PC / ABS alloy is the earliest industrial production, currently the most mature, the most widely used and the largest output A PC modified product, this type of alloy can combine the excellent properties of the two: on the one hand, it can improve the heat resistance, impact resistance and tensile properties of ABS, and replace ABS in high-performance fields; on the other hand, it can reduce the PC It is a polymer alloy with comprehensive performance by reducing the cost and melt viscosity, improving its processing performance, and reducing the sensitivity of product internal stress and impact strength to product thickness. [0003] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L69/00C08L55/02C08L83/04C08L81/02C08L25/12C08L25/04C08K13/02C08K5/523C08K5/544C08K3/22C08K5/3415B29C47/92B29C48/92
CPCB29C47/92B29C48/04B29C48/40B29C48/875B29C48/92B29C2948/92704B29C2948/92895B29C2948/92904
Inventor 杨燕黄志杰顾伟左绍文沈岳新杨仓先
Owner 中广核俊尔(上海)新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com