Preparation method of novel modified furan resin for casting

A furan resin and modification technology, which is applied in casting molding equipment, casting molds, cores, etc., can solve the problems of unsuitable wood adhesives, etc., and achieve the effects of good stability and transparency, high tensile strength, and low price

Active Publication Date: 2013-05-22
SUZHOU XINGYE MATERIALS TECH
View PDF3 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with the comprehensive performance requirements of the casting process mentioned above, the wood adhesive is not suitable for direct use as casting resin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of novel modified furan resin for casting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Add 30g of water, 100g of sucrose and 0.1g of urea into the reaction vessel, stir at 10°C until dissolved, then add 5g of concentrated sulfuric acid, stir and heat up to 60°C, react for 20h, cool down to 30°C; use 30% hydrogen to oxidize Adjust the pH value to 7.5 with sodium, add 0.1 g of formaldehyde, raise the temperature at 60°C for 6 hours, and then dehydrate 5 g to obtain a brown-red viscous liquid.

[0036] According to the corresponding steps of the comparative example, under the conditions of steps (1) to (3) unchanged, in step (4), take 5 g of the above-mentioned brown-red viscous liquid to replace 5 g of furfuryl alcohol in step (4) of the comparative example (the total amount of raw materials 5% by weight), the raw materials actually participating in the reaction are 35g furfuryl alcohol, 5g brownish-red viscous liquid and 0.85g silane coupling agent, and other conditions remain unchanged to obtain a modified furan resin for casting, and its properties are sh...

Embodiment 2

[0038] Add 60g of water, 100g of glucose and 5g of urea into the reaction vessel, stir at 30°C until dissolved, then add 10g of concentrated nitric acid, stir and raise the temperature to 80°C, react for 4 hours, and cool down to 40°C; use 30% sodium hydroxide Adjust the pH value to 8.5, add 6g of formaldehyde, heat up to 70°C for 4 hours, and then dehydrate 80g to obtain a brown-red viscous liquid.

[0039] According to the corresponding steps of the comparative example, under the conditions of steps (1) to (3) unchanged, in step (4), take 5 g of the above-mentioned brown-red viscous liquid to replace 10 g of furfuryl alcohol in the step (4) of the comparative example (the total amount of raw materials 10% by weight), the actual raw materials that participated in the reaction were 30g furfuryl alcohol, 10g brownish-red viscous liquid and 0.85g silane coupling agent, and other conditions were unchanged to obtain a modified furan resin for casting, and its properties are shown i...

Embodiment 3

[0041] Add 76g of water, 100g of sucrose and 7.5g of urea into the reaction vessel, stir at 40°C until dissolved, then add 25g of concentrated hydrochloric acid, stir and raise the temperature to 84°C, react for 2 hours, then cool down to 50°C; adjust with 20% ammonia water When the pH value reached 8.5, 8g of formaldehyde was added, the temperature was raised to 95°C for 1 hour, and then 98g was dehydrated to obtain a brown-red viscous liquid.

[0042] According to the corresponding steps of the comparative example, under the condition that steps (1) to (3) remain unchanged, in step (4), take 20 g of the above-mentioned brown-red viscous liquid to replace 20 g of furfuryl alcohol in step (4) of the comparative example (the total amount of raw materials 20% by weight), the raw materials actually participating in the reaction are 20g furfuryl alcohol, 20g brownish-red viscous liquid and 0.85g silane coupling agent, and other conditions remain unchanged to obtain a modified furan...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of novel modified furan resin for casting. The method is characterized by comprising the following steps of: (1) dissolving 100 parts by weight of saccharides and 0.1-40 parts by weight of urea into 30-200 parts by weight of water; adding 5-60 parts by weight of acid into a mixture to react for 0.5-10 hours at the temperature of 60-105 DEG C; cooling to 30-90 DEG C; regulating a pH value to 7.5-10 and adding 0.1-40 parts by weight of formaldehyde; raising the temperature to 60-100 DEG C to react for 0.5-6 hours; and removing 3-300 parts by weight of water to obtain viscous liquid; and (2) using the viscous liquid obtained in the step (1) as a partial furfuryl alcohol substitute and preparing the novel modified furan resin for casting according to the conventional process of furan resin for casting, wherein the using amount of the viscous liquid is equivalent to the weight of furfuryl alcohol to be substituted and accounts for 1-20 percent of the total weight of a furan resin synthetic raw material for casting. The method is simple, feasible and environmentally-friendly, and a reticulate structure of the resin is formed during curing, so that the intensity of furan resin sand for casting can be improved.

Description

technical field [0001] The invention belongs to the technical field of furan resin synthesis technology for casting, and in particular relates to a preparation method of a novel modified furan resin for casting. Background technique [0002] The foundry binder system is composed of resin, curing agent and catalyst. A good foundry binder system must have good chemical stability and low viscosity; the resin and raw sand have a longer working life. After curing, it has good demoulding performance; sufficient strength at room temperature and high temperature; and has good collapsibility and easy regeneration of molding sand. Therefore, the choice of casting resin is very important. [0003] Furan resin refers to a resin synthesized with furfuryl alcohol having a furan ring as the main raw material. In the 1960s, furan resin began to be used in the foundry industry. It has developed rapidly due to its excellent properties such as fast hardening at room temperature, good diffusi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G16/04B22C1/22
Inventor 王进兴黄萍珍顾嫒娟陆玉峰朱文英
Owner SUZHOU XINGYE MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap