Modified slag compound admixture and preparation method thereof

A composite admixture and slag technology, which is applied in the field of modified slag composite admixture and its preparation, can solve the problems of resource utilization with high added value, increase added value, reduce heat of hydration, and reduce energy consumption Effect

Inactive Publication Date: 2015-02-18
TONGJI UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Slag and fly ash among the three major industrial wastes have been widely and maturely used in the cement concrete industry, but steel slag, one of the three major industrial wastes, has not yet been utilized as a resource with high added value
[0007] At present, fly ash and slag powder have been widely used in cement concrete as mineral admixtures to improve the rheological properties of fresh concrete and the mechanical properties and durability of hardened concrete. It has not been reported that it is used in concrete with blast furnace slag powder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified slag compound admixture and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The mass percentage of S95 grade slag powder is 60%, and the density is 2.90g / cm 3 , specific surface area 415m 2 / kg; 7-day activity index ≥ 75%, 28-day activity index ≥ 95%, sulfur trioxide content ≤ 4.0%, chloride ion content ≤ 0.06%.

[0027] The mass percentage of ground converter steel slag powder is 30%, and the density is 3.90g / cm 3 , specific surface area 405m 2 / kg, 28-day activity index ≥ 75%, sulfur trioxide content ≤ 4.0%, chloride ion content ≤ 0.05%, alkalinity ≥ 2.2.

[0028] The mass percentage of white slag is 10%, and the specific surface area is 420m 2 / kg.

[0029] Add 60% slag powder by mass, 30% steel slag powder and 10% white slag into the mixer and stir for 5 minutes to prepare the modified slag composite admixture . Refer to GB / T 18046-2008 "Granulated Blast Furnace Slag Powder Used in Cement and Concrete" to test the performance of the modified slag composite admixture sample in all aspects. The benchmark cement is Conch brand 42.5 Port...

Embodiment 2

[0031]The mass percentage of S95 grade slag powder is 68%, and the density is 2.90g / cm 3 , specific surface area 415m 2 / kg, 7-day activity index ≥ 75%, 28-day activity index ≥ 95%, sulfur trioxide content ≤ 4.0%, chloride ion content ≤ 0.06%.

[0032] The mass percentage of ground converter steel slag powder is 25%, and the density is 3.90g / cm 3 , specific surface area 405m 2 / kg, 28-day activity index ≥ 75%, sulfur trioxide content ≤ 4.0%, chloride ion content ≤ 0.05%, alkalinity ≥ 2.2.

[0033] The mass percentage of white slag is 7%, and the specific surface area is 420m 2 / kg.

[0034] The slag powder with a mass percentage of 68%, the steel slag powder with a mass percentage of 25%, and the white slag with a mass percentage of 7% were added to the mixer and stirred for 4 minutes to prepare a modified slag composite admixture . Refer to GB / T 18046-2008 "Granulated Blast Furnace Slag Powder Used in Cement and Concrete" to test the performance of the modified slag com...

Embodiment 3

[0036] The mass percentage of S95 grade slag powder is 80%, and the density is 2.90g / cm 3 , specific surface area 415m 2 / kg, 7-day activity index ≥ 75%, 28-day activity index ≥ 95%, sulfur trioxide content ≤ 4.0%, chloride ion content ≤ 0.06%.

[0037] The mass percentage of ground electric furnace steel slag powder is 15%, and the density is 3.90g / cm 3 , specific surface area 405m 2 / kg; 28-day activity index ≥ 75%, sulfur trioxide content ≤ 4.0%, chloride ion content ≤ 0.05%, alkalinity ≥ 2.2.

[0038] The mass percentage of white slag is 5%, and the specific surface area is 420m 2 / kg.

[0039] Put 80% slag powder by mass, 15% steel slag powder and 5% white slag into the mixer, and stir for 3 minutes to prepare the modified slag composite admixture . Refer to GB / T18046-2008 "Granulated Blast Furnace Slag Powder Used in Cement and Concrete" to test the performance of the modified slag composite admixture sample in all aspects. The benchmark cement is Conch brand 42.5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
specific surface areaaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical fields of resource utilization of solid wastes, environmental protection and energy conservation, and discloses a modified slag compound admixture and a preparation method thereof. The slag compound admixture disclosed by the invention is prepared from the following components in percentage by mass: 60-80% of slag powder, 15-30% of steelmaking slag powder, and 5-10% of white slag. The preparation method disclosed by the invention comprises the step of 60-80% of stirring slag powder, 15-30% of steelmaking slag powder and 5-10% of white slag for 3-5 min. The modified slag compound admixture disclosed by the invention has the most outstanding advantages that the disadvantage of being low in early strength of the compound admixture caused by doping a lot of steelmaking slag is overcome; furthermore, both the activity indexes for 7 days and 28 days are higher than the requirements of GB / T 18046-2008 on S95-level mineral powder; particularly, the activity index for 28 days is greatly increased; the long-period strength still can be increased continuously.

Description

technical field [0001] The invention belongs to the technical field of resource utilization of solid waste and environmental protection and energy saving, and relates to a modified slag composite admixture and a preparation method thereof. Background technique [0002] In recent years, with the vigorous development of commercial concrete in my country and the development and deepening of cement concrete research and application technology, mineral admixtures have become one of the indispensable and important components of modern concrete. Slag and fly ash among the three major industrial wastes have been widely and maturely used in the cement concrete industry, but steel slag, one of the three major industrial wastes, has not yet been utilized as a resource with high added value. It is China's established national policy to develop a circular economy and take the road of sustainable development, and the resource utilization of industrial waste residue is one of the key links...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03B18/14
Inventor 施惠生郭晓潞吴凯李东锋黄昆生林茂松
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com