Humidity-heat resistant cyanacrylate adhesive

A technology of cyanoacrylate and polymerization inhibitor, used in adhesives, polymer adhesive additives, non-polymer organic compound adhesives, etc., can solve the problems of limitation, poor heat and water resistance, etc.

Inactive Publication Date: 2015-03-18
TONSAN ADHESIVES INC
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Cyanoacrylate adhesives are a unique type of monomer-type fast-curing adhesives. Since they were introduced by Eastman in 1958, they have been widely used because of their many advantages, such as one-component, rapid curing at room temperature, bonding Wide range of materials, low viscosity, thin adhesive layer, and the adhesive film has transparency, oil resistance and electrical insulation. However, the adhesive formed after curing is linear and easily hydrolyzed, resulting in poor heat and water resistance, which limits its use. wider application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Humidity-heat resistant cyanacrylate adhesive
  • Humidity-heat resistant cyanacrylate adhesive
  • Humidity-heat resistant cyanacrylate adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Add 0.1% free radical stabilizer hydroquinone, 0.05% anion stabilizer p-toluenesulfonic acid, and 0.5% accelerator dimethylsila-11-crown-4 to ethyl cyanoacrylate , 10% polymethyl methacrylate (PMMA), polyvinyl acetate (PVAC), vinyl acrylate rubber (AEM), nitrile rubber (NBR), acrylonitrile-butadiene-styrene copolymer ( ABS), acrylonitrile-styrene-acrylic rubber copolymer (ASA), stirred at 55-65°C for 1-2h to obtain glue. Test the positioning time of the glue on the nitrile rubber, and test the shear strength of the glue bonded carbon steel sheet according to the GB / T7124-2008 method. ℃, 90%RH in these two environments, test the shear strength of aging for 168h, so as to evaluate the moisture and heat resistance of the glue. The results are shown in the following table, where the percentage in the damp heat aging data is the relative 24h shear strength retention rate, and sample No. 1 is the blank sample:

[0030]

[0031] Compared with linear polymers PMMA and PVAC...

Embodiment 2

[0032] Add 0.1% free radical stabilizer hydroquinone, 0.05% anion stabilizer p-toluenesulfonic acid, and 0.5% accelerator dimethylsila-11-crown-4 to ethyl cyanoacrylate , different contents of ABS and ASA, and investigate the storage period of the prepared glue solution at 55°C (the maximum number of days for the glue solution not to thicken or solidify significantly) and the appearance change. Sample No. 8 is a blank sample.

[0033]

[0034] Compared with ABS, the addition of ASA can effectively improve the stability of ethyl α-cyanoacrylate, and the ideal addition amount is 10%.

[0035] Embodiment two:

[0036] Add 10% ASA or PMMA, 0.1% free radical stabilizer hydroquinone, 0.05% anion stabilizer p-toluenesulfonic acid, 0.5% anion stabilizer to methyl cyanoacrylate and ethyl cyanoacrylate respectively. % accelerator dimethylsila-11-crown-4. According to the method of GB / T 2791-1995, the peel strength of the aluminum sheet bonded by the glue is tested. Sample Nos. 15...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention is a cyanoacrylate composition, including: (1) 50-98% cyanoacrylate monomer, (2) 0.001%-10% anionic polymerization inhibitor, (3) radical polymerization inhibitor Agent 0.01-5%, (4) Thickener 1-30%, (5) Accelerator 0.1-10%; This patent uses acrylonitrile-styrene-acrylate rubber copolymer (ASA) as the cyano Thickener and toughener of acrylate adhesives, this substance can effectively improve the heat and humidity resistance of the adhesive, and because it does not contain groups that hinder the curing of the glue, it does not affect the curing speed of the adhesive. In addition, because ASA itself Excellent anti-aging performance, it also improves the anti-aging performance of the adhesive.

Description

technical field [0001] The present invention relates to a cyanoacrylate-containing composition, in particular to a cyanoacrylate adhesive used under hot and humid conditions. Background technique [0002] Cyanoacrylate adhesives are a unique type of monomer-type fast-curing adhesives. Since they were introduced by Eastman in 1958, they have been widely used because of their many advantages, such as one-component, rapid curing at room temperature, bonding Wide range of materials, low viscosity, thin adhesive layer, and the adhesive film has transparency, oil resistance and electrical insulation. However, the adhesive formed after curing is linear and easily hydrolyzed, resulting in poor heat and water resistance, which limits its use. wider application. [0003] Many studies at home and abroad use the method of adding carboxylic acid or anhydride to improve the heat and humidity resistance of cyanoacrylate adhesives. On the one hand, carboxylic acids and anhydrides can produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J4/04C09J11/08
Inventor 聂聪王兵林新松李印柏翟海潮
Owner TONSAN ADHESIVES INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com