Piercing plug laser strengthening process dispensing with preheating before laser cladding

A perforated plug and laser cladding technology, which is applied in the coating process and coating of metal materials, can solve the problems of cumbersome procedures, reduced hardness of the cladding layer, and slow production efficiency, so as to reduce pollution, hardness and wear resistance Improvement and long service life

Active Publication Date: 2014-02-12
JIANGSU ZHONGOU FERTILIZER
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The laser cladding process of the perforated plug in the prior art must preheat the plug and anneal after the surfacing to eliminate stress. Not on

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0015] The specific steps of the laser strengthening process of the perforated plug in this embodiment are as follows:

[0016] A. Pre-treat the surface of the pierced plug.

[0017] Remove dust, oil, rust, etc. on the perforated plug; detect the size of each part; and clean.

[0018] B. Laser cladding the surface of the perforated plug.

[0019] Using the segmented laser cladding method, starting from the tip of the nose of the perforated plug, from front to back (the tip of the nose of the plug is the front end, and the part with the largest outer diameter of the plug is the rear end) to carry out laser cladding on the surface of the perforated plug segment by segment. First, a layer of transition alloy is clad on the surface of the perforated plug substrate, and then a layer of high-strength alloy is clad on the transition alloy layer. During the laser cladding process, the perforated plug is continuously tapped with a copper rod, so that the perforated plug vibrates to r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a laser strengthening process of a piercing plug. The laser strengthening process is characterized by firstly carrying out laser cladding on a transition alloy layer on the surface of a piercing plug matrix and then carrying out laser cladding on the high-strength alloy layer on the transition alloy layer, wherein the alloy powder adopted by the transition alloy layer is the nickel base alloy; the alloy powder adopted by the high-strength alloy layer is the cobalt base alloy. The laser strengthening process has the advantages that the transition alloy layer in the process has lower hardness than the high-strength alloy layer, plays a role in transition for the high-strength alloy layer with high hardness and high wear resistance and can well relieve the surfacing stress, so that even if the plug is not preheated or annealed, the residual surfacing stress can not have great impacts on the tissues of a laser cladding layer, thus effectively avoiding impacting the properties of the cladding layer by annealing, substantially improving the surface hardness and wear resistance of the piercing plug, simultaneously omitting the processes of preheating and annealing and also improving the production efficiency.

Description

[0001] This application is a divisional application, the application number of the original application: 201210248964.9, the name of the invention: laser strengthening process for perforated plugs, and the application date: 2012-07-18. technical field [0002] The invention relates to a laser cladding method, in particular to a laser cladding method for the surface of a perforated plug. Background technique [0003] With the increase of my country's export of seamless steel pipes, the consumption of spare parts used in the production of seamless steel pipes is also increasing year by year. The perforated plug is a key tool for producing seamless steel pipes. The quality and service life of the perforated plug have a direct impact on the output, quality and production cost of seamless steel pipes. The temperature of the perforated plug is very high when it is working, and it bears a lot of combined stress. During use, it will fail such as deformation, collapse, sticking to st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C24/10C22C19/05C22C19/07
Inventor 邓琦林
Owner JIANGSU ZHONGOU FERTILIZER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap