Low-temperature X80HD (High Density) large-deformation pipeline steel with great wall thickness and production method thereof
A technology for large deformation and pipeline steel, which is applied in the production of medium and thick plates and longitudinal submerged arc welded pipes. It can solve the problems of no design specifications and different performance requirements of steel pipes, and achieve uniform deformation, high uniform elongation, and production The effect of cost economy
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0036] Example 1
[0037] The thickness of the steel plate is 26.4mm, the width of the steel plate is 3740, the corresponding steel pipe specification is Φ1219*26.4mm, the thickness of the continuous casting billet is 400mm, the drawing speed is 0.80m / min, the dynamic soft reduction technology is adopted during smelting, and the segregation of the cast billet is C 0.5 , Its chemical composition is shown in Table 1. The heating temperature of the slab is 1160℃, and the heating time is 390min; the initial rolling temperature of the rough rolling stage is 1035℃, the final rolling temperature is 990℃, the total rolling reduction rate after rough rolling and widening is 63.5%, and the last three passes are single pass The secondary reduction rate is 18%-22%; the start-rolling temperature of the finishing rolling stage is 835℃, and the final rolling temperature is 786℃. The total steel reduction rate of this stage is 73.2%; the relaxation phase transformation control stage, the steel p...
Example Embodiment
[0039] Example 2
[0040] The thickness of the steel plate is 27.5mm, the width of the steel plate is 3740, the corresponding steel pipe specification is Φ1219*27.5mm, the thickness of the continuous casting billet is 400mm, the drawing speed is 0.80m / min, the dynamic soft reduction technology is adopted during smelting, and the segregation of the cast billet is C 0.5 , Its chemical composition is shown in Table 1. The heating temperature of the slab is 1150℃, the heating time is 430min; the opening temperature of the rough rolling stage is 1020℃, the final rolling temperature is 1000℃, the total rolling reduction rate after rough rolling and widening is 61.4%, and the last three passes are single pass The secondary reduction rate is 18%-22%; the start-rolling temperature of the finishing rolling stage is 830℃, and the final rolling temperature is 798℃. The total steel reduction rate at this stage is 67%; the relaxation phase transformation control stage, the steel plate is 1 At...
Example Embodiment
[0042] Example 3
[0043] The thickness of the steel plate is 23.7mm, the width of the steel plate is 3745, the corresponding steel pipe specification is Φ1219*23.7mm, the thickness of the continuous casting billet is 350mm, the drawing speed is 0.85m / min, the dynamic soft reduction technology is used during smelting, and the segregation of the cast billet is C 0.5 , Its chemical composition is shown in Table 1. The heating temperature of the slab is 1170℃, and the heating time is 340min; the initial rolling temperature of the rough rolling stage is 1030℃, the final rolling temperature is 1017℃, the total rolling reduction rate after rough rolling and widening is 64.2%, and the last three passes are single pass The secondary reduction rate is 18%-24%; the start-rolling temperature of the finishing rolling stage is 840℃, the final rolling temperature is 803℃, and the total steel reduction rate of this stage is 70%; the relaxation phase transformation control stage, the steel plate...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap