Low floating fiber antiflaming reinforced PBT (polybutylece terephthalate) composite material

Abstract

The invention relates to the technical field of plastic modification, and particularly relates to a low floating fiber antiflaming reinforced PBT (polybutylece terephthalate) composite material. The material comprises PBT, flexibilizer, silicon coupling agent, chopped glass fiber, environment-friendly fire retardant, antioxidant, lubricant and floating fiber remover, wherein the PBT accounts for 55-70 weight percent of the total amount of the raw material, and the weight ratio of the PBT to flexibilizer is (1-20):1. A preparation method of the material comprises steps of mixing, extruding and injection moulding. The product prepared by the method has low floating fiber, is inflaming retarding and is reinforced.

Description

technical field [0001] The invention relates to the technical field of plastic modification, in particular to a flame-retardant reinforced PBT composite material with low floating fibers. Background technique [0002] Polybutylene terephthalate (PBT for short), which belongs to the polyester series, is composed of 1,4-butanediol (1,4-Butylene glycol) and terephthalic acid (PTA) or terephthalic acid Ester (DMT) polycondensation, and a milky white translucent to opaque, crystalline thermoplastic polyester resin produced through a mixing process. Together with PET, it is collectively referred to as thermoplastic polyester, or saturated polyester. [0003] Because PBT has good heat resistance, weather resistance, chemical resistance, good electrical properties, low water absorption, and good gloss, it is widely used in electronic appliances, auto parts, machinery, household products and other fields, and PBT products are also Together with PPS, PC, POM, PA, etc., they are cal...

AI Technical Summary

Problems solved by technology

However, traditional PBT products have the following problems: 1. When in use, accidents such as burning due to factors such as open flames or static electricity often occur; 2. The phenomenon of floating fibers is prone to decrease in surface smoothness during injection molding, and the appearance is poor. ,Affect

This patent avoids the floating fiber phenomenon and is flame retardant, but it is a non-reinforced product

[0006] In summary, there is no PBT composite material with low floating fiber, flame retardancy and reinforcement in the prior art