Building panel doped with complex mineral

A composite mineral, construction technology, applied in the field of building material manufacturing, can solve problems such as failure to reach the designed service life, damage, cracking and water seepage of building materials

Inactive Publication Date: 2015-05-20
WAN YANG GRP
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] During the project, the basements, roofs, roads and bridges of many buildings did not reach the designed service life, and some projects were seriously damaged after only a few years of use and had to be repaired. The main reason is that the current waterproof materials and cement plus The agent generally contains Cl-,,,,, and K+ ions are too heavy, and when added to the cement, it reacts with the active silica in the concrete to form an alkali silicate gel and cause the concrete to expand and crack. This is a common problem in engineering. Alkali-aggregate reaction, while accelerating the corrosion of steel bars, resulting in cracking and water seepage of building materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A method for preparing a building board mixed with composite minerals, characterized in that:

[0026] Weigh raw materials: cement 282g, cement composite mineral additive 18g, sand 750g, polypropylene fiber 4g, naphthalene-based water reducer 3g; put the above raw materials into a conical double-helix mixer and stir evenly for 50 minutes. After stirring Casting into the mold; static curing, the time is 8 hours; after static curing, enter the autoclave for the first autoclaving curing, the temperature of the first autoclaving curing is 220 ° C, and the time is 10 hours; after that Cool naturally, place at room temperature for 4 hours, and perform the second autoclaving curing, the temperature of the second autoclaving curing is 160° C., and the time is 20 hours; a building board mixed with composite minerals is obtained.

[0027] The preparation method steps of the cement composite mineral additive are:

[0028] Step (1): According to 20 parts of alumina clinker, 15 par...

Embodiment 2

[0033] A method for preparing a building board mixed with composite minerals, characterized in that:

[0034] Weigh raw materials: cement 282g, cement composite mineral additive 18g, sand 750g, polypropylene fiber 4g, naphthalene-based water reducer 3g; put the above raw materials into a conical double-helix mixer and stir evenly for 50 minutes. After stirring Casting into the mold; static curing, the time is 8 hours; after static curing, enter the autoclave for the first autoclaving curing, the temperature of the first autoclaving curing is 220 ° C, and the time is 10 hours; after that Cool naturally, place at room temperature for 4 hours, and perform the second autoclaving curing, the temperature of the second autoclaving curing is 160° C., and the time is 20 hours; a building board mixed with composite minerals is obtained.

[0035] The preparation method steps of the cement composite mineral additive are:

[0036]Step (1): According to 25 parts of alumina clinker, 20 part...

Embodiment 3

[0041] A method for preparing a building board mixed with composite minerals, characterized in that:

[0042] Weigh raw materials: cement 282g, cement composite mineral additive 18g, sand 750g, polypropylene fiber 4g, naphthalene-based water reducer 3g; put the above raw materials into a conical double-helix mixer and stir evenly for 50 minutes. After stirring Casting into the mold; static curing, the time is 8 hours; after static curing, enter the autoclave for the first autoclaving curing, the temperature of the first autoclaving curing is 220 ° C, and the time is 10 hours; after that Cool naturally, place at room temperature for 4 hours, and perform the second autoclaving curing, the temperature of the second autoclaving curing is 160° C., and the time is 20 hours; a building board mixed with composite minerals is obtained.

[0043] The preparation method steps of the cement composite mineral additive are:

[0044] Step (1): According to 23 parts of alumina clinker, 17 par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a building panel doped with a complex mineral. The panel is characterized by comprising the following processes: weighing 282g of material cement, 18g of prepared cement complex mineral additive, 750g of sand, 4g of polypropylene fiber and 3g of naphthalene water reducer according to the ratio; feeding the raw materials to a conical twin-screw mixer to evenly agitate according to the ratio, wherein the agitating time is 50 minutes. The building panel doped with the complex mineral disclosed by the invention has the functions of efficiently preventing water, preventing moisture, expanding, anti-cracking, anti-seepage and the like, and is free of corrosive action on a reinforcing steel bar.

Description

technical field [0001] The invention relates to a building board mixed with composite minerals, which belongs to the field of building material manufacturing. Background technique [0002] During the project, the basements, roofs, roads and bridges of many buildings did not reach the designed service life, and some projects were seriously damaged after only a few years of use and had to be repaired. The main reason is that the current waterproof materials and cement plus The agent generally contains Cl-,,,,, and K+ ions are too heavy, and when added to the cement, it reacts with the active silica in the concrete to form an alkali silicate gel and cause the concrete to expand and crack. This is a common problem in engineering. Alkali-aggregate reaction also accelerates the corrosion of steel bars, resulting in cracking and water seepage of building materials. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies of the prio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00C04B16/06
Inventor 梅伟苏孝锋谢进曾焕录谢学高苏孝忠
Owner WAN YANG GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com