White light sensitivity resin composition and purpose thereof

A resin composition and optical rotation technology, applied in optics, optomechanical equipment, instruments, etc., can solve the problems of white photoresist yellowing, poor consumer perception, etc., and achieve high adhesion, excellent resolution, good The effect of resolution

Inactive Publication Date: 2014-09-24
EVERLIGHT CHEMICAL INDUSTRIAL CORPORATION
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the temperature of the ITO wiring process may be as high as 250°C or above, at this high temperature, the commonly used white photoresist is prone to yellowing, resulting in poor consumer perception

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • White light sensitivity resin composition and purpose thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029]Uniformly mix 4.86 parts by weight of EL-200 (alkali-soluble resin, manufactured by Yongguang Co.); 3.42 parts by weight of R551 (polymerizable compound having ethylenically unsaturated bonds, manufactured by Nippon Kayaku Co., Ltd.); photoinitiator In the agent, 1-hydroxyl-cyclohexyl-phenyl-ketone (I-184) accounts for 0.72 parts by weight, 2,4,6-trimethylbenzoyl diphenylphosphine oxide (TPO) accounts for 2.88 parts by weight; 1.94 Parts by weight of DPMP (manufactured by Sakai chemical Industry Co., Ltd); 32.56 parts by weight of propylene glycol methyl ether acetate (PGMEA, solvent); 32.50 parts by weight of ethyl lactate (solvent); 21 parts by weight of titanium dioxide (white pigment ); 0.08 parts by weight of I1010 (manufactured by Ciba-BASF); 0.03 parts by weight of S-386 (manufactured by Asahi Whistle Co., Ltd.); and 0.01 parts by weight of HQ (manufactured by Merck, Taiwan). Prepare 100 parts by weight of a white photosensitive resin composition, and then filter ...

Embodiment 2

[0031] The preparation method of the white photosensitive resin composition of Example 2 is substantially the same as that of Example 1, the only difference is that the content of I-184 and TPO constituting the photoinitiator is different. In Example 2, I-184 accounts for 0.97 parts by weight, and TPO accounts for 2.63 parts by weight.

Embodiment 3

[0033] The preparation method of the white photosensitive resin composition of Example 3 is substantially the same as that of Example 1, the only difference is that the content of I-184 and TPO constituting the photoinitiator are different. In Example 3, I-184 accounts for 1.46 parts by weight, and TPO accounts for 2.14 parts by weight.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

Provided is a white light sensitivity resin composition comprising alkali soluble resin, polymeric composition, photoinitiator, white pigment, and solvents, wherein the photoinitiator is formed by 2,4,6-trimethylbenzoyldiphenylphosphine oxide and 1-hydroxyl-cyclohexyl-phenyl-ketone. The white light sensitivity resin composition has characteristics of not turning yellow in high-temperature baking (about 250 DEG C) and being graphical. The invention also provides the purpose of the above white light sensitivity resin composition, the composition is used in touch panels and for forming a shielding layer at the periphery of a transmittance substrate.

Description

technical field [0001] The present invention relates to a white photosensitive resin composition and its application, especially to a white photosensitive resin composition used in a touch panel and its application. Background technique [0002] Liquid crystal displays are widely used in consumer electronics products, such as smart phones, tablet computers, satellite navigation devices, and digital cameras. In recent years, in order to improve the user interface and efficiency of use, the rise of touch panels allows users to directly Input operation information on the liquid crystal display panel. Due to the advantages of portability and easy operation of electronic products equipped with touch panels, it has gradually become an indispensable basic equipment for many consumer electronics products, and has also become a major development of many consumer electronics products. direction. [0003] Thinning has become the development trend of touch panels. In order to greatly r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G03F7/027G06F3/041
Inventor 张桂嘉林凡森胡登贵张志毅
Owner EVERLIGHT CHEMICAL INDUSTRIAL CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap