A kind of driving gear and its preparation method

A driving gear and tooth shape technology, applied in the field of driving gear and its preparation, can solve the problems of short service life, low gear hardness and impact toughness, etc., achieve the improvement of metallographic structure and mechanical properties, shorten the holding time of nitriding, and improve the processing efficiency. Effects on efficiency and processing quality

Active Publication Date: 2016-08-17
南京航迅机电有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the gear material is mostly QT500 ductile iron, and the average service life of a gear is only about 15 days. The hardness and impact toughness of the gear are low, and the service life is short, which cannot meet the needs of industrial applications.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A driving gear provided in this embodiment, the chemical composition of the driving gear is: C: 0.20%, Si: 0.35%, Mn: 0.50%, Cr: 1.6%, Ni: 3.4%, Nb: 0.04%, V: 0.03%, Cu: 0.4%, P: 0.03%, S: 0.025%, lanthanide rare earth: 0.03%, the balance is Fe;

[0036] The chemical composition of the lanthanide rare earth components by weight percentage is: La: 20%, Sc: 12%, Y: 16%, Sm: 21%; Gd: 20%, and other lanthanide elements: 11%.

[0037] The preparation method of above-mentioned drive gear, specifically carries out according to the following steps:

[0038] (1) The driving gear mold is made of molding sand and core sand as molding materials. Before making the mold, the molding sand in the molding material is first placed in an oven for drying;

[0039](2) Heat and melt the chemical composition of the driving gear at 1650°C, inject it into the mold formed in step (1), and release it after air cooling to obtain the driving gear blank;

[0040] (3) For the drive gear blank in st...

Embodiment 2

[0048] A drive gear provided in this embodiment, the chemical composition of the drive gear is: C: 0.23%, Si: 0.33%, Mn: 0.55%, Cr: 1.5%, Ni: 3.2%, Nb: 0.03%, V: 0.01%, Cu: 0.2%, P: 0.025%, S: 0.018%, lanthanide rare earth: 0.01%, the balance is Fe;

[0049] The chemical composition of the lanthanide rare earth components by weight percentage is: La: 23%, Sc: 11%, Y: 15%, Sm: 20%; Gd: 19%, and other lanthanide elements: 12%.

[0050] The preparation method of above-mentioned drive gear, specifically carries out according to the following steps:

[0051] (1) The driving gear mold is made of molding sand and core sand as molding materials. Before making the mold, the molding sand in the molding material is first placed in an oven for drying;

[0052] (2) Heat and melt the chemical composition of the driving gear at 1660°C, inject it into the mold formed in step (1), and release it after air cooling to obtain the driving gear blank;

[0053] (3) For the drive gear blank in step...

Embodiment 3

[0061] A drive gear provided in this embodiment, the chemical composition of the drive gear is: C: 0.22%, Si: 0.30%, Mn: 0.60%, Cr: 1.4%, Ni: 3.3%, Nb: 0.02%, V: 0.02%, Cu: 0.3%, P: 0.01%, S: 0.029%, lanthanide rare earth: 0.02%, the balance is Fe;

[0062] The chemical composition of the lanthanide rare earth is: La: 22%, Sc: 11%, Y: 17%, Sm: 21%; Gd: 19%, and other lanthanide elements: 10%.

[0063] The preparation method of above-mentioned drive gear, specifically carries out according to the following steps:

[0064] (1) The driving gear mold is made of molding sand and core sand as molding materials. Before making the mold, the molding sand in the molding material is first placed in an oven for drying;

[0065] (2) Heat and melt the chemical composition of the driving gear at 1670°C, inject it into the mold formed in step (1), and release it after air cooling to obtain the driving gear blank;

[0066] (3) For the driving gear blank in step (2), heat it at 305°C, then co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a driving gear and a preparation method thereof. The chemical composition of the driving gear includes: C, Si, Mn, Cr, Ni, Nb, V, Cu, P, S, lanthanide rare earth and the rest Fe, the blank is first prepared by casting, and then the blank is subjected to heat treatment, the cutting process of rough turning gear ring gear, rough milling tooth profile process, carburizing and nitriding treatment, tempering, quenching and tempering heat treatment, and finally finishing The turning process and the fine milling tooth profile process are inspected and packed into the warehouse; the driving gear has high strength, hardness and wear resistance, the gear has good corrosion resistance and oxidation resistance, and the yield strength and tensile strength are high. The processing method of the gear Simple, low cost and good formability.

Description

technical field [0001] The invention relates to a gear and a preparation method of the gear, in particular to a driving gear and a preparation method thereof. Background technique [0002] As one of the most basic transmission parts in the machinery industry, gears are used to adjust the speed and transmit power in mechanical devices. They play a key role in equipment including automobiles, machine tools, and cranes, and are widely used. When the gear is in operation, contact will be formed on the tooth surface to transmit power, the tooth will be subjected to huge alternating bending stress and contact stress, and a large friction force will also be generated between the tooth surfaces that mesh with each other. The damage form of the gear is mainly due to the fracture of the tooth part and the wear of the tooth surface. The choice of material has a great influence on the damage of the gear. [0003] With the continuous improvement of the technical parameters of modern mec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/48C21D9/32
Inventor 陆树根杨忠喜冯强龙
Owner 南京航迅机电有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap