Crystal glaze ceramic tile and production method thereof

A production method and technology of crystalline glaze, applied in the field of crystalline glazed ceramic tiles and their production, can solve the problems of not being applicable to the field of architectural ceramic decoration, having pinholes, complex composition of crystallization agents, etc., and achieving increased artistic aesthetic value, uniform crystal flowers, strong artistic effect

Active Publication Date: 2015-01-28
HANGZHOU NABEL CERAMIC
View PDF18 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Chinese patent CN 102627476 A introduces a blue crystalline glaze and its application method. The formula of this technical solution is relatively simple, the decorative effect is better, and the crystalline effect can be obtained. Blue ceramic products, but the firing cycle is 15~16h, not suitable for the field of architectural

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] 1) Preparation of crystalline frit: According to the conventional glass frit preparation process, potassium feldspar, albite, quartz, dolomite, calcite and chemical raw materials are selected, and the ingredients are mixed, melted at 1350°C, water quenched, dried, Crushing, sieving, and grading processes, the obtained composition is SiO 2 45%, Al 2 o 3 10%, CaO 11%, MgO 4%, K 2 O 3.5%, Na 2 O 2%, B 2 o 3 5%, ZnO 22%, moisture ≤ 0.5% crystalline frit with a particle size of 4~60 mesh;

[0027] 2) Preparation of seed crystals: mix and melt the crystalline frit and zinc oxide at a ratio of 10:3 to form a high-zinc frit as the seed crystal;

[0028] 3) Preparation of brick adobe: prepare porcelain brick adobe powder according to conventional methods, and press to prepare adobe;

[0029] 4) Apply frit and seed crystals: apply crystalline frit on the surface of the brick, and the application amount is 2.5kg / m 2 , a small amount of seeds can be applied in the lower ...

Embodiment 2

[0032] 1) Preparation of crystalline frit: According to the conventional glass frit preparation process, potassium feldspar, albite, quartz, dolomite, calcite and chemical raw materials are selected, and are prepared by batching, melting at 1240°C, water quenching, drying, Crushing, sieving, and grading processes, the obtained composition is SiO 2 55%, Al 2 o 3 5%, CaO 8%, MgO 3%, K 2 O 2%, Na 2 O 3.5%, B 2 o 3 3.5%, ZnO 16%, iron oxide 2%, manganese oxide 2%, moisture ≤ 0.5%, particle size 4~60 mesh crystalline frit;

[0033] 2) Preparation of seed crystals: using zinc oxide as the seed crystals;

[0034] 3) Preparation of high-viscosity frit: select potassium feldspar, albite, quartz, dolomite, calcite and chemical raw materials, through batching, melting at 1350 ° C, water quenching, drying, crushing, sieving, and grading processes, Get composition range for SiO 2 60%, Al 2 o 3 6%, K 2 O 7%, Na 2 O 6%, B 2 o 3 14%, BaO 5%, Li 2 O 1%, moisture ≤ 0.5%, tr...

Embodiment 3

[0040] 1) Preparation of crystalline frit: select potassium feldspar, albite, quartz, dolomite, calcite and chemical raw materials, and obtain The composition is SiO 2 50%, Al 2 o 3 8%, CaO 10%, MgO 2%, K 2 O 1%, Na 2 O 3.5%, B 2 o 3 4.5%, ZnO 20%, Nickel Oxide 1%, Cobalt Oxide 0.5%, Moisture ≤ 0.5%, the particle size is 4~60 mesh crystalline frit;

[0041] 2) Preparation of seed crystals: mix and melt the crystalline frit and zinc oxide at a ratio of 2:1 to form a high-zinc frit as the seed crystal;

[0042] 3) Preparation of brick adobe: prepare porcelain brick adobe powder according to conventional methods, and press to prepare adobe;

[0043] 4) Apply frit and seed crystals: apply crystalline frit on the surface of the adobe, and the amount of application is 4kg / m 2 , you can first apply part of the frit to cover the surface of the adobe, then apply a small amount of seed crystals, and finally apply the remaining frit on the seeds;

[0044] 5) Firing: raise the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a crystal glaze ceramic tile and a production method thereof. The method comprises the following steps: distributing a crystal clinker and seed crystal on a conventional ceramic tile blank, heating to 1130-1200 DEG C, and insulating for 10-30 minutes; then, cooling to 1000-1080 DEG C, and insulating at the temperature for 1-2 hours to prepare the crystal glaze ceramic tile with a remarkable crystal flower effect. An artistic decoration effect with large and round crystal flower and diversified patterns and colors can be achieved by utilizing the crystal glaze ceramic tile; a crystal glaze ceramic of which flowing stripes are arranged on the surface, and an artistic aesthetic value can be remarkably increased. When the crystal clinker is prepared, the smelting temperature is low, and the smelting time is short; when the crystal glaze ceramic tile is fired, the firing temperature is low, and the required crystallization time is short, so that the production energy consumption is remarkably reduced, the firing cycle is shortened, the production cost is reduced, the waste emission amount in the production process is reduced, and excellent economic and social benefits can be brought.

Description

technical field [0001] The invention relates to the technical field of production methods of artistic ceramic tiles, in particular to a crystal glazed ceramic tile and a production method thereof. Background technique [0002] Crystalline glaze is a kind of artificial crystal flower glaze used to decorate and display ceramics, daily-use ceramics and other products. It is developed on the basis of Chinese ancient glaze. In the Song Dynasty, on the basis of color glazes, redox atmosphere was used to manufacture kiln-changing flower glazes. Some of the color glazes naturally presented gorgeous and colorful microcrystals, such as Tianmu, Xingzhan, tea powder, iron embroidery, grape spots, sesame spots, etc. Microcrystalline crystalline glaze is considered to be the earliest crystalline glaze product in the world. [0003] However, the large-scale application of crystal glaze to architectural ceramic decoration is still a technical bottleneck that is difficult to break through. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/86
Inventor 余爱民夏昌奎余剑峰彭西洋谢明锋
Owner HANGZHOU NABEL CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap