A production process and refined cotton technology, applied in pulping with inorganic alkali, pretreatment of finely split raw materials, textiles and papermaking, etc., can solve the problems of affecting product viscosity, simple cooking process, unfavorable cooking treatment, etc., and achieve improvement The effect of product viscosity, reducing the cost of use, and meeting the whiteness requirements

Active Publication Date: 2016-11-23
HUBEI JINHANJIANG REFINED COTTON
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current process for producing high-viscosity refined cotton cannot produce products with a viscosity range of more than 2200. The main reasons are that, firstly, before the cooking process in the production process, the alkali soaking and pretreatment process of raw materials are not enough. Reasonable, so that the lye does not fully penetrate into the cotton linters, which is not conducive to the subsequent cooking treatment; second, the cooking process is simple, and a suitable cooking process is not well established according to the characteristics of the cotton linters; the third is bleaching In the process, the use of hydrogen peroxide as a bleaching agent will greatly affect the increase in product viscosity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0007] Embodiment 1: ultra-high-viscosity refined cotton production process, its specific production process is as follows: a, material selection, cotton opening: select 4 tons of high-quality cotton linters without three silk impurities as raw material, and the fiber length of cotton linters is between 13 ~ 15mm, absolute dryness is 92%, maturity is over 80%, and has been treated with loosening, impurity removal and cotton opening; The final cotton linters are sprayed with a dissolving ratio of 1:2.7. After extrusion treatment at 0.18MPa, the sodium hydroxide solution is fully and evenly penetrated into the cotton linters to form alkali fibers, and the humidity of the alkali fibers is controlled at 78%; c , Pretreatment: The alkali fibers after soaking in alkali fully and uniformly are subjected to 2MPa rolling treatment, and the lye solution rolled out is recycled and reused. After rolling, the humidity of the alkali fibers is controlled at 45%, and then the mass concentratio...

Embodiment 2

[0008] Embodiment 2: ultra-high-viscosity refined cotton production process, its specific production process is as follows: a, material selection, cotton opening: select 4 tons of high-quality cotton linters without three silk impurities as raw material, and the fiber length of cotton linters is between 13 ~ 15mm, absolute dryness is 92%, maturity is over 80%, and has been treated with loosening, impurity removal and cotton opening; The final cotton linters are sprayed with a solvent ratio of 1:3.0, and after extrusion treatment at 0.20 MPa, the sodium hydroxide solution is fully and evenly penetrated into the cotton linters to form alkali fibers, and the humidity of the alkali fibers is controlled at 75%; c , pretreatment: the alkali fiber after soaking in alkali fully and evenly is processed through 3MPa rolling, and the lye liquid that is rolled out is recycled and reused. 4 kg of AES auxiliary agent is used to perform three times of repeated spraying and rolling treatment ...

Embodiment 3

[0009]Embodiment 3: ultra-high-viscosity refined cotton production process, its specific production process is as follows: a, material selection, cotton opening: select 4 tons of high-quality cotton linters without three silk impurities as raw material, and the fiber length of cotton linters is between 13 ~ 15mm, absolute dryness is 92%, maturity is over 80%, and has been treated with loosening, impurity removal and cotton opening; The final cotton linters are sprayed with a solvent ratio of 1:2.8, and after extrusion treatment at 0.19MPa, the sodium hydroxide solution is fully and evenly penetrated into the cotton linters to form alkali fibers, and the humidity of the alkali fibers is controlled at 76%; c , Pretreatment: The alkali fibers after soaking in alkali fully and evenly are subjected to 2.8MPa rolling treatment, and the lye solution rolled out is recycled and reused. After rolling, the humidity of the alkali fibers is controlled between 43%, and then the mass concentr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an ultrahigh-viscosity refined cotton production process. The specific production process comprises the step a of material selection and cotton opening, the step b of soaking, the step c of pretreatment, the step d of digesting, the step e of bleaching and the step f of grinding and drying. In the step d, pretreated alkali fibers are placed into an airtight spherical digester, and the temperature in the spherical digester is raised; next, the spherical digester is rotated in an idle mode, the temperature is raised again while the spherical digester is rotated, and the pressure is controlled to range from 0.20 MPa to 0.22 MPa; next, rotation of the spherical digester is stopped, a small amount of steam is released for 10 minutes, and a part of oxygen in the spherical digester is discharged to prevent oxidation and viscosity reduction; next, the temperature is raised again while the spherical digester is rotated, and the pressure is controlled to range from 0.25 MPa to 0.28 MPa; lastly, a large amount of steam is released after the temperature is kept for 30 minutes, alkali liquor is recovered, and cotton slurry is poured out when the temperature drops to 100 DEG C. The ultrahigh-viscosity refined cotton production process has the advantages that the use amount of the alkali liquor is reduced, the use cost of the alkali liquor is effectively lowered, and the requirement for improving the ultrahigh viscosity of products is met.

Description

technical field [0001] The invention relates to the technical field of refined cotton production technology, more specifically relates to the technical field of ultra-high viscosity refined cotton production technology. Background technique [0002] Refined cotton, also known as cotton pulp, is a white cotton fiber refined from cotton linters through processes such as cotton opening, cooking, rinsing, and drying. It is non-toxic, tasteless and easy to absorb water. It is the main material for the manufacture of ether cellulose, nitrocellulose and cellulose acetate. It is widely used in food, medicine, daily chemicals, plastics, electronics, papermaking, metallurgy, aerospace and many other fields. , Known as "special industrial monosodium glutamate". Under the premise of reaching a certain whiteness, the higher the viscosity of refined cotton, the better, which is more conducive to the production of high-viscosity products by cellulose manufacturers. However, the current p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D21B1/02D21C1/06D21C1/00D21C3/02D21C9/12D21C9/18
CPCD21B1/02D21C1/00D21C1/06D21C3/02D21C9/142D21C9/185
Inventor 周家贵
Owner HUBEI JINHANJIANG REFINED COTTON
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products