Ethylene-propylene-diene monomer material used for electric wire and preparation method of ethylene-propylene-diene monomer material

A EPDM rubber, wire and cable technology, applied in the direction of rubber insulators, organic insulators, etc., can solve the problems of inability to meet actual use requirements, poor processing performance, etc., and achieve the effects of low production cost, improved strength performance, and convenient processing.

Active Publication Date: 2015-03-25
JIANGSU LONG E CABLE
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the traditional EPDM rubber cannot meet the requirements of high cable strength. Its processing performance is poor, and its anti-aging and flame-retardant properties cannot meet the actual use requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The EPDM material for electric wire and cable of the present invention has its distribution ratio of each component in parts by weight:

[0032] (1) 100 parts of EPDM rubber,

[0033] (2) 7 parts of acrylic acid,

[0034] (3) 5 parts of sodium stearate,

[0035] (4) 3 parts of initiator,

[0036] (5) 3 parts of anti-aging agent,

[0037] (6) 0.8 part of inorganic filler,

[0038] (7) 1.5 parts of flame retardant.

[0039] The initiator is dicumyl peroxide.

[0040] The anti-aging agent is anti-aging agent MB.

[0041] The inorganic filler is white carbon black, and the flame retardant is polyammonium phosphate.

[0042] The preparation method of EPDM rubber material for said electric wire and cable, it may further comprise the steps:

[0043] (1) Pre-mix EPDM rubber, acrylic acid, and sodium stearate by heating at a temperature of 55°C.

[0044] (2) Then heat the initiator, anti-aging agent, inorganic filler and flame retardant with the mixture in step (1) and ...

Embodiment 2

[0048] The EPDM material for electric wire and cable of the present invention, its distribution ratio of each component in parts by weight:

[0049] (1) 105 parts of EPDM rubber,

[0050] (2) 8 parts of acrylic acid,

[0051] (3) 5 parts of sodium stearate,

[0052] (4) 4 parts of initiator,

[0053] (5) 4 parts of anti-aging agent,

[0054] (6) 0.9 part of inorganic filler,

[0055] (7) 1.2 parts of flame retardant.

[0056] The initiator is dicumyl peroxide.

[0057] The anti-aging agent is anti-aging agent MB.

[0058] The inorganic filler is pottery clay, and the flame retardant is polyammonium phosphate.

[0059] The preparation method of EPDM rubber material for said electric wire and cable, it may further comprise the steps:

[0060] (1) Pre-mix EPDM rubber, acrylic acid, and sodium stearate by heating at a temperature of 53°C.

[0061] (2) Then heat the initiator, anti-aging agent, inorganic filler and flame retardant with the mixture in step (1) and mix thoro...

Embodiment 3

[0065] The EPDM material for electric wire and cable of the present invention, its distribution ratio of each component in parts by weight:

[0066] (1) 119 parts of EPDM rubber,

[0067] (2) 6 parts of acrylic acid,

[0068] (3) 3 parts of sodium stearate,

[0069] (4) 5 parts of initiator,

[0070] (5) 7 parts of anti-aging agent,

[0071] (6) 1.2 parts of inorganic filler,

[0072] (7) 1.0 parts of flame retardant.

[0073] The initiator is dicumyl peroxide.

[0074] The anti-aging agent is anti-aging agent MB.

[0075] The inorganic filler is pottery clay, and the flame retardant is polyammonium phosphate.

[0076] The preparation method of EPDM rubber material for said electric wire and cable, it may further comprise the steps:

[0077] (1) Pre-mix EPDM rubber, acrylic acid and sodium stearate by heating at 52°C.

[0078] (2) Then heat the initiator, anti-aging agent, inorganic filler and flame retardant with the mixture in step (1) and mix thoroughly, the heatin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an ethylene-propylene-diene monomer material used for an electric wire and a preparation method of the ethylene-propylene-diene monomer material. The ethylene-propylene-diene monomer material comprises the following components in parts by weight: 85-115 parts of an ethylene-propylene-diene monomer, 2.5-10 parts of acrylic acid, 1.5-7 parts of sodium stearate, 1.5-6 parts of an initiator, 2.5-8 parts of an antiager, 0.5-1.5 parts of an inorganic filler and 1-2 parts of a fire retardant. According to the preparation method, a mixture is added to a double-screw extruder to carry out extrusion pelleting. The ethylene-propylene-diene monomer material used for the electric wire is high in strength, good in anti-aging, good in flame retardant property, stable in power supply property and convenient to process.

Description

technical field [0001] The invention relates to a material for cable manufacturing and a preparation method thereof, in particular to a rubber material for electric wires and cables and a preparation method thereof. Background technique [0002] EPDM rubber has excellent electrical properties, excellent heat resistance, good low temperature flexibility, etc., so it is widely used in cables, especially mine cables and marine cables. However, the traditional EPDM rubber cannot meet the requirements for high cable strength, and its processing performance is poor, and its anti-aging and flame-retardant properties cannot meet the actual use requirements. Contents of the invention [0003] Purpose of the invention: the purpose of the invention is to overcome the deficiencies in the prior art, to provide a rubber material for wire and cable with high strength, good aging resistance, good flame retardancy and stable power supply performance, and to provide a rubber material capabl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/04C08K13/02C08K5/098C08K3/36C08K3/34C08K3/32C08K5/37C08F255/06C08F220/06H01B3/28B29C47/92B29C48/92
Inventor 芮逸
Owner JIANGSU LONG E CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com