A high-chromium martensitic heat-resistant steel resistant to liquid metal corrosion
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A liquid metal and heat-resistant steel technology, applied in the field of heat-resistant metal materials, can solve the problems of low strength, toughness and toughness, low high temperature creep durability, and no mention of it.
Active Publication Date: 2017-08-25
INST OF METAL RESEARCH - CHINESE ACAD OF SCI +1
View PDF1 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Although this martensitic structure material has good oxidation resistance, due to the presence of delta ferrite with a content of ≤5% in its structure, its strength and toughness, especially toughness, are low, and its high-temperature creep durability is also low.
In addition, this patent document does not mention the characteristics of the present invention, namely, obtaining a full martensitic structure, improving toughness and high temperature creep strength
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0034] The chemical composition of the martensitic heat-resistant steel in this example is: C: 0.18wt.%, Si: 1.10wt.%, Cr: 10.05wt.%, Mn: 0.95wt.%, W: 1.10wt.%, Ta: 0.10wt.%, V: 0.20wt.%, Nb: 0.01wt.%, S: 20 (ppm), P: 40 (ppm), Cu<0.01wt.%, Ti: 40 (ppm), Al : 60 (ppm), Co: 30 (ppm), and the balance is iron.
Embodiment 2
[0036] The chemical composition of the martensitic heat-resistant steel in this example is: C: 0.23wt.%, Si: 1.30wt.%, Cr: 10.30wt.%, Mn: 0.67wt.%, W: 1.22wt.%, Ta: 0.23wt.%, V: 0.20wt.%, Nb: 0.01wt.%, S: 30 (ppm), P: 30 (ppm), Cu<0.01wt.%, Ti: 40 (ppm), Al <50 (ppm), Co: 20 (ppm), the balance is iron.
Embodiment 3
[0038] The chemical composition of the martensitic heat-resistant steel in this example is: C: 0.25wt.%, Si: 1.48wt.%, Cr: 10.10wt.%, Mn: 0.59wt.%, W: 1.30wt.%, Ta: 0.28wt.%, V: 0.10wt.%, Nb: 0.01wt.%, S<30 (ppm), P: 20 (ppm), Cu<0.01wt.%, Ti: 40 (ppm), Al <50 (ppm), Co: 40 (ppm), the balance is iron.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a liquid metal corrosion-resistant high-chromium martensitic heat-resistant steel, which belongs to the field of heat-resistant metal materials. It is characterized in that the weight percentage (wt.%) of the alloy composition is: 0.18%≤C≤0.26%, 1.0%<Si≤1.5%, 10%<Cr≤11.5%, 1.0%<W≤1.5%, 0%< Mn<1.0%, Ta+Nb: ≤0.3%, 0%<V≤0.2%, the balance is iron. The beneficial effect of the present invention is that the liquid metal corrosion resistance is improved by adopting a more reasonable high silicon and high chromium content, and the generation of δ ferrite is suppressed by adjusting the content of carbon, manganese and other elements to obtain a full The martensitic structure improves the strength and toughness, and the microalloying elements such as tantalum, niobium and vanadium are used for composite strengthening to improve the high-temperature creep performance, so that the heat-resistant steel has excellent strength and toughness, high-temperature creep performance and liquid metal corrosion resistance. .
Description
technical field [0001] The invention belongs to the field of heat-resistant metal materials, in particular to a martensitic heat-resistant steel with excellent strength and toughness, excellent high-temperature creep performance and liquid metal corrosion resistance, in particular to a liquid metal corrosion-resistant high-chromium martensitic steel Body heat-resistant steel. Background technique [0002] Liquid metals such as liquid lead and lead-bismuth have excellent properties such as high thermal conductivity, low melting point and high boiling point, and low vapor pressure, and are designed by countries all over the world for advanced nuclear reaction systems such as fast neutron reactors, fusion reactors, and accelerator-driven subcritical systems. The loop or cladding coolant is also designed to be used as a high-energy neutron target for accelerator-driven subcritical systems due to its excellent neutronic properties and radiation damage resistance. In these advanc...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/26
Inventor 单以银严伟王志光王威杨柯周强国
Owner INST OF METAL RESEARCH - CHINESE ACAD OF SCI
Login to view more 
Login to view more