Environment-friendly formaldehyde removal decorative material and preparation method thereof

A decorative material and formaldehyde technology, applied in the field of decorative materials, can solve the problem that formaldehyde cannot be removed from the source, and achieve the effects of low raw material prices, excellent impact resistance, and simple preparation methods

Inactive Publication Date: 2015-09-09
SUZHOU HONGHENG CHEM
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to limited technology and materials, the use of raw materials containing formaldehyde components cannot be completely prohibited in the process of manufacturing indoor furniture and decoration, and the hazards of formaldehyde cannot be removed from the source. Therefore, eliminating and reducing the hazards of formaldehyde is a top priority

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] An environmentally friendly formaldehyde-removing decorative material, in parts by weight, comprises the following components:

[0037] 20 parts of silicone resin, 15 parts of polyamide resin,

[0038] 3 parts of glass fiber, 8 parts of waste tea leaves,

[0039] 10 parts of Chlorophytum, 5 parts of oyster shell powder,

[0040] 3 parts of nano-titanium oxide, 1 part of carbon nanotube,

[0041] 2 parts of ethylene-vinyl acetate, 5 parts of polyacrylate,

[0042] 2 parts of methyl hydroxyethyl cellulose, 1 part of crosslinking agent, 2 parts of plasticizer.

[0043] Its preparation method comprises the following steps:

[0044] (1) drying waste tea leaves and Chlorophytum chinensis, pulverizing, mixing uniformly, adding oyster shell powder, nano-titanium oxide, carbon nanotubes, mixing uniformly to obtain mixed powder;

[0045] (2) Add silicone resin, polyamide resin, glass fiber, and the mixed powder obtained in step (1) into a high-speed kneader, knead for 2-min ...

Embodiment 2

[0048] An environmentally friendly formaldehyde-removing decorative material, in parts by weight, comprises the following components:

[0049] 40 parts of silicone resin, 30 parts of polyamide resin,

[0050] 10 parts of glass fiber, 15 parts of waste tea leaves,

[0051] 15 parts of Chlorophytum, 10 parts of oyster shell powder,

[0052] 8 parts of nano-titanium oxide, 3 parts of carbon nanotubes,

[0053] 5 parts of ethylene-vinyl acetate, 9 parts of polyacrylate,

[0054] 5 parts of methyl hydroxyethyl cellulose, 3 parts of crosslinking agent, 5 parts of plasticizer.

[0055] Its preparation method comprises the following steps:

[0056] (1) drying waste tea leaves and Chlorophytum chinensis, pulverizing, mixing uniformly, adding oyster shell powder, nano-titanium oxide, carbon nanotubes, mixing uniformly to obtain mixed powder;

[0057] (2) Add silicone resin, polyamide resin, glass fiber, and the mixed powder obtained in step (1) into a high-speed kneader, knead for ...

Embodiment 3

[0060] An environmentally friendly formaldehyde-removing decorative material, in parts by weight, comprises the following components:

[0061] 25 parts of silicone resin, 18 parts of polyamide resin,

[0062] 4 parts of glass fiber, 9 parts of waste tea leaves,

[0063] 11 parts of Chlorophytum, 6 parts of oyster shell powder,

[0064] 4 parts of nano-titanium oxide, 1.5 parts of carbon nanotubes,

[0065] 2.5 parts of ethylene-vinyl acetate, 6 parts of polyacrylate,

[0066] 2.5 parts of methyl hydroxyethyl cellulose, 1.5 parts of crosslinking agent, and 2.5 parts of plasticizer.

[0067] Its preparation method comprises the following steps:

[0068] (1) drying waste tea leaves and Chlorophytum chinensis, pulverizing, mixing uniformly, adding oyster shell powder, nano-titanium oxide, carbon nanotubes, mixing uniformly to obtain mixed powder;

[0069] (2) Add silicone resin, polyamide resin, glass fiber, and the mixed powder obtained in step (1) into a high-speed kneader, k...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
particle sizeaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly formaldehyde removal decorative material comprising the following components in parts by weight: 20-40 parts of silicon resin, 15-30 parts of polyamide resin, 3-10 parts of glass fibers, 8-15 parts of waste tea residues, 10-15 parts of chlorophytum comosum, 5-10 parts of oyster shell powder, 3-8 parts of nano titanium oxide, 1-3 parts of carbon nanotubes, 2-5 parts of ethylene-vinyl acetate, 5-9 parts of polyacrylate, 2-5 parts of methyl hydroxyl ethyl cellulose, 1-3 parts of a crosslinking agent and 2-5 parts of a plasticizer. The invention also provides a preparation method of the environment-friendly formaldehyde removal decorative material. The decorative material provided by the invention can effectively remove formaldehyde, is good in thermal stability and sound insulation effect and excellent in impact resistance, is wear-resistant and nontoxic, is beneficial for environmental protection, and can be widely applied to the fields of decorative materials including door windows, floors, ceilings and the like.

Description

Technical field: [0001] The invention relates to the field of decorative materials, in particular to an environmentally friendly decorative material for removing formaldehyde. Background technique: [0002] Modern interior decoration materials can not only improve the indoor artistic environment and enable people to enjoy beauty, but also have multiple functions such as heat insulation, moisture resistance, and fire prevention, which can protect the main structure of the building, prolong its service life and meet certain special requirements. It is an indispensable material for modern architecture. As interior decoration materials become more and more complex, formaldehyde in these decoration materials, floors, and furniture will slowly volatilize into the air, which will have a serious impact on human health. Due to limited technology and materials, the use of raw materials containing formaldehyde components cannot be completely prohibited in the process of manufacturing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/04C08L67/00C08L77/00C08L33/08C08L23/08C08L1/28C08L97/02C08K13/04C08K7/14C08K3/22C08K3/04
Inventor 矫磊
Owner SUZHOU HONGHENG CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com