Body paper containing titanium dioxide and preparation method thereof

A technology of titanium dioxide and composite titanium dioxide, which is applied in the field of papermaking, can solve problems such as water resistance, weak gloss, and difficulty in meeting market demand, and achieve the effects of enhancing strength, improving grip, and improving physical and mechanical properties

Inactive Publication Date: 2015-09-16
ZHEJIANG HUACHUAN IND GRP
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the development of modern science and technology, the use of paper is not only positioned for recording and writing, but also for indoor wall decoration. However, the existing wallpaper has weak heat insulation, is not water-resistant, is difficult to clean, has weak gloss, and is resistant to water. Poor abrasiveness, it is difficult to meet the demand of the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A base paper containing titanium dioxide, comprising the following raw materials in parts by weight: 5 parts of composite titanium dioxide, 20 parts of bamboo fiber, 25 parts of wood pulp fiber, 15 parts of polyester fiber, 1 part of sodium carboxymethyl cellulose, nano 2 parts of bamboo carbon fiber, 4 parts of chopped aramid fiber and 4 parts of aramid pulp, the internal components of the composite titanium dioxide are made according to the following proportions by weight: 20 parts of inorganic powder, 20 parts of titanium dioxide, stearin 0.1 part of acid ester, 0.1 part of hydrogen-containing silicone oil, 1 part of potassium sulfate, 1 part of ferrous iron, 80 parts of titanium dioxide.

[0021] A preparation method of base paper containing titanium dioxide, comprising the following steps:

[0022] 1) Send 20 parts of inorganic powder and 80 parts of titanium dioxide into the activation machine, control the rotation speed of the activation machine to 1500r / min, and...

Embodiment 2

[0030] A base paper containing titanium dioxide, comprising the following raw materials in parts by weight: 10 parts of composite titanium dioxide, 30 parts of bamboo fiber, 35 parts of wood pulp fiber, 25 parts of polyester fiber, 3 parts of sodium carboxymethyl cellulose, nano 4 parts of bamboo carbon fiber, 6 parts of chopped aramid fiber and 6 parts of aramid pulp, the internal components of the composite titanium dioxide are made according to the following proportions by weight: 40 parts of inorganic powder, 40 parts of titanium dioxide, stearin 0.3 parts of acid ester, 0.3 parts of hydrogen-containing silicone oil, 10 parts of potassium sulfate, 10 parts of ferrous iron, and 100 parts of titanium dioxide.

[0031] A preparation method of base paper containing titanium dioxide, comprising the following steps:

[0032] 1) Send 40 parts of inorganic powder and 100 parts of titanium dioxide into the activation machine, control the rotation speed of the activation machine to ...

Embodiment 3

[0040] A base paper containing titanium dioxide, comprising the following raw materials in parts by weight: 7 parts of composite titanium dioxide, 25 parts of bamboo fiber, 30 parts of wood pulp fiber, 20 parts of polyester fiber, 2 parts of sodium carboxymethyl cellulose, nano 3 parts of bamboo carbon fiber, 5 parts of chopped aramid fiber and 5 parts of aramid pulp, the internal components of the composite titanium dioxide are made according to the following proportions by weight: 30 parts of inorganic powder, 30 parts of titanium dioxide, stearin 0.2 parts of acid ester, 0.2 parts of hydrogen-containing silicone oil, 5 parts of potassium sulfate, 5 parts of ferrous iron, and 90 parts of titanium dioxide.

[0041] A preparation method of base paper containing titanium dioxide, comprising the following steps:

[0042] 1) Send 30 parts of inorganic powder and 90 parts of titanium dioxide into the activation machine, control the rotation speed of the activation machine to 1500r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a piece of body paper containing titanium dioxide and a preparation method of the body paper. The body paper is prepared from the following materials in parts by weight: 5-10 parts of composite titanium dioxide, 20-30 parts of bamboo fiber, 25-35 parts of wood pulp fiber, 15-25 parts of polyester fiber, 1-3 parts of sodium carboxymethyl cellulose, 2-4 parts of nano bamboo carbon fiber, 4-6 parts of chopped aramid fiber and 4-6 parts of aramid fiber pulp; the composite titanium dioxide is prepared from the following components in parts by weight: 20-40 parts of inorganic powder, 20-40 parts of titanium dioxide, 0.1-0.3 part of stearate, 0.1-0.3 part of silicone oil containing hydrogen, 1-10 parts of potassium sulfate, 1-10 parts of ferrous compound and 80-100 parts of titanium dioxide. The body paper containing titanium dioxide and the preparation method of the body paper are relatively strong in heat insulation property, and are waterproof, easy to clean, strong in glossiness, good in abrasion resistance, and capable of meeting the requirements of the market.

Description

technical field [0001] The invention belongs to the field of papermaking, and in particular relates to base paper containing titanium dioxide and a preparation method thereof. Background technique [0002] Paper is an important invention of the working people of the Han nationality in ancient times. In ancient times, ancestors mainly relied on knotting to record events, and then gradually invented characters, and began to use oracle bones as writing materials, and later discovered and used bamboo chips, wood chips, and silk as writing materials. However, because silk was too expensive and bamboo chips were too bulky, paper was produced. One of the four great inventions in ancient China, papermaking, together with the compass, gunpowder, and printing, provided a material and technological foundation for the prosperity of ancient Chinese culture. The invention of paper ended the complicated history of bamboo slips and slips in ancient times, and greatly promoted the spread ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D21H17/63D21H17/33D21H17/05
Inventor 冯向华冯子坚王家斌
Owner ZHEJIANG HUACHUAN IND GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com