A kind of washable touch screen temporary protection ink and its preparation method and application

A temporary protection, touch screen technology, applied in the field of ink, can solve the problems of touch screen cover glass or ITO glass corrosion, operator health damage, low process efficiency, etc., to achieve easy expansion of production, convenient cleaning process, simple craftsmanship

Inactive Publication Date: 2017-12-19
SOUTH CHINA UNIV OF TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are many protections for touch screen cover glass or ITO glass. The traditional ones, such as peelable protective glue / protective film, can play a protective role in the process of processing, but they need to be peeled off manually, which consumes a lot of manpower and reduces the process efficiency. Low
Printing ink is currently the most important way to protect the best touch screen cover glass or ITO glass, but most of them have disadvantages such as not easy to remove the film and difficult to clean
Although there have been some inventions that can be washed off with hot acid and alkali solutions or removed by high-temperature hot water, the film removal speed is relatively slow, generally 2 to 5 minutes, which increases the cost of film removal on the one hand, such as purchasing treatment liquid, heating water On the other hand, acid, lye, etc. may also be corrosive to the touch screen cover glass or ITO glass itself, and may also cause health damage to the operator

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of washable touch screen temporary protection ink and its preparation method and application
  • A kind of washable touch screen temporary protection ink and its preparation method and application
  • A kind of washable touch screen temporary protection ink and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0060] A washable touch screen temporary protection ink, first equipped with a water-based acrylic modified epoxy resin aqueous solution with a solid content of 40%, and a starch aqueous solution with a solid content of 5%, and then weighed according to the mass ratio:

[0061]

[0062] Add the above-mentioned polyacrylic acid resin aqueous solution, XH-103Z leveling agent, and nano silicon dioxide into the disperser and stir at 400r / min for 10min until uniform, then add other remaining raw materials and stir at 300r / min for 50min to obtain ink.

[0063] The obtained ink was printed with a 200-mesh screen brush on a 10 μm coating film on the above-mentioned touch screen cover glass and ITO glass, first dried at 80°C for 30 minutes, and then placed in an oven at 200°C for 2 hours before testing. The hardness tested by the GB / T 6739 method is B, and the film is smooth and yellowish. The film-removing effect in 50°C water is about 90s and it falls off in pieces.

Embodiment 3

[0065] A washable touch screen temporary protection ink, first equipped with a water-based amino resin aqueous solution with a solid content of 40%, and an aqueous solution of sodium alginate with a solid content of 5%; then weighed according to the mass ratio

[0066]

[0067] Add the above-mentioned polyacrylate emulsion and XH-103Z leveling agent into the disperser and stir at 400r / min for 15min until uniform, then add other remaining raw materials and stir at 300r / min for 60min to obtain the ink.

[0068] The obtained ink was printed with a 200-mesh screen brush on a 10 μm coating film on the above-mentioned touch screen cover glass and ITO glass, first dried at 80°C for 30 minutes, and then placed in an oven at 200°C for 2 hours before testing. The hardness tested by the GB / T 6739 method is B, the film is smooth and light yellow, and the effect of film removal in 50°C water is about 50s, and it will fall off in large blocks.

[0069] Implementation 4

[0070] A washab...

Embodiment 6

[0080] A kind of washable touch screen temporary protective ink, first equipped with a water-based polyacrylate aqueous solution with a solid content of 40%, and an aqueous solution of polyvinylpyrrolidone (K30) with a solid content of 40%

[0081] Then weigh it according to the mass ratio

[0082]

[0083]

[0084] Add the above polyacrylic acid resin aqueous solution, XH-103Z leveling agent and nano silicon dioxide into the disperser and stir at 400r / min for 10min until uniform, then add other remaining raw materials and stir at 300r / min for 40min to obtain ink.

[0085] The obtained ink was printed with a 200-mesh screen brush on a 10 μm coating film on the above-mentioned touch screen cover glass and ITO glass, first dried at 80°C for 30 minutes, and then placed in an oven at 200°C for 2 hours before testing. The hardness tested by the GB / T 6739 method is 2B, the film is smooth and yellowish, and the film-removing effect in 50°C water is about 45s, and the film falls...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a washable touch screen temporary protection ink and its preparation method and application. The raw materials are composed of 0-50% of polyacrylic acid resin solution and 5%-90% of water-based paint resin in terms of mass percentage. %, water-soluble polymer solution 5% to 50%, polyacrylate emulsion 0‑70%, filler 1% to 10%, pigment 0.1% to 2%, functional additives 2% to 5%, of which polyacrylic resin The solution and the polyacrylate emulsion are not 0 at the same time. When preparing, add polyacrylic acid solution, polyacrylate emulsion, water-based leveling agent and filler into the disperser, mix well and then add other components and mix well to obtain a washable touch screen temporary protection ink. The ink of the present invention can protect the touch screen cover glass or ITO glass surface film from damage during the construction process at a high temperature of 200°C, and after being immersed in 50°C water at 200°C, it can fall off in blocks within 30s to 2 minutes .

Description

technical field [0001] The present invention relates to the field of ink, specifically a kind of ink that can temporarily protect the surface of the touch screen cover glass or ITO glass during the processing of the touch screen, especially at a high temperature of 200°C. An ink that can be washed off in warm water at a very fast speed after the construction of the control screen cover glass or ITO glass and its preparation method. technical background [0002] With the continuous development of touch screen technology, its related industries have developed rapidly, such as smart phones, tablet computers, navigators, ATMs, etc., and have penetrated into every field of life, which has greatly changed people's way of life. However, the touch screen cover glass or ITO glass in the unprotected state is easy to be damaged to a certain extent during the subsequent cutting, edging or other processing processes, especially under high temperature conditions. The damage is more obviou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/107C09D11/102C09D11/103C09D11/03C09D11/033C09D11/037B41M1/34B41M1/12
Inventor 文秀芳贾丹枫皮丕辉蔡智奇徐守萍程江
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com