Activated carbon fiber composite material and preparation method thereof as well as activated carbon fiber composite filter element

A technology of activated carbon fibers and composite materials, applied in chemical instruments and methods, water/sewage multi-stage treatment, water/sludge/sewage treatment, etc. It is not resistant to high temperature and other problems, and achieves the effect of overcoming poor strength, large adsorption capacity and uniform microporous structure.

Inactive Publication Date: 2015-11-25
GUANGDONG ZHENGYE TECH
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the prepared filter element has poor adsorption and filtration effect, and most of the filter element structures listed above are not resistant to high temperature, and have poor acid and alkali resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Activated carbon fiber composite material and preparation method thereof as well as activated carbon fiber composite filter element
  • Activated carbon fiber composite material and preparation method thereof as well as activated carbon fiber composite filter element
  • Activated carbon fiber composite material and preparation method thereof as well as activated carbon fiber composite filter element

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0048] The present invention also provides a kind of preparation method of activated carbon fiber composite material, comprises the following steps:

[0049] After weighing activated carbon fiber chopped strands and / or activated carbon fiber powder, powdered activated carbon, short fibers, modified cellulose and auxiliary agents to obtain a mixed raw material, the mixed raw material is mixed with water evenly, and is prepared on a paper machine at one time. The net is shaped to form an activated carbon fiber composite material.

[0050] The present invention first weighs the activated carbon fiber chopped strands and / or activated carbon fiber powder, powdered activated carbon, short fiber, modified cellulose and auxiliary agents to obtain the mixed raw material, and then mixes the mixed raw material with water to obtain the mixed slurry material. Wherein, the mass ratio of the mixed raw material to water is preferably 1: (10-20), and in some specific embodiments of the presen...

Embodiment 1

[0073] 1. Raw material formula of activated carbon fiber composite material:

[0074] 20wt% activated carbon fiber, purchased from Ningxia Baoda Carbon Fiber Co., Ltd., iodine value 1500mg / g;

[0075]30wt% coconut shell activated carbon with an iodine value of 800mg / g;

[0076] 35wt% wood pulp;

[0077] 10wt% carboxymethyl cellulose;

[0078] 5 wt% polyamide epichlorohydrin.

[0079] 2. Weigh the above materials according to the weight ratio, mix them with water at a ratio of 1:20, and form a net on a paper machine to obtain an activated carbon fiber composite material.

[0080] 3. Cut the activated carbon fiber composite material into a width of 254mm with a circular knife slitting machine, and then cut it into a length of 1200mm, and wind it on a 254mm long hollow cylindrical plastic skeleton covered with polypropylene microfiber cloth. The ethylene protective net and the upper and lower end caps are fixed to make a 10-inch activated carbon fiber composite filter element...

Embodiment 2

[0082] 1. Raw material formula of activated carbon fiber composite material:

[0083] 30wt% activated carbon fiber, purchased from Ningxia Baoda Carbon Fiber Co., Ltd., with an iodine value of 1500mg / g;

[0084] 20wt% coconut shell activated carbon with an iodine value of 800mg / g;

[0085] 35wt% wood pulp;

[0086] 10wt% carboxymethyl cellulose;

[0087] 5 wt% polyamide epichlorohydrin.

[0088] 2. Weigh the above materials according to the weight ratio, mix them with water at a ratio of 1:20, and form a net on a paper machine to obtain an activated carbon fiber composite material.

[0089] 3. Cut the activated carbon fiber composite material into a width of 254mm with a circular knife slitting machine, and then cut it into a length of 1200mm, and wind it on a 254mm long hollow cylindrical plastic skeleton covered with polypropylene microfiber cloth. The ethylene protective net and the upper and lower end caps are fixed to make a 10-inch activated carbon fiber composite fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention provides an activated carbon fiber composite material which is prepared from activated carbon fiber, staple fiber, powdered activated carbon, modified cellulose, processing aids and the like. As an adsorbing material of an efficient activated carbon filter element, the activated carbon fiber composite material overcomes the problems of poor intensity and easy slipping of lint of an activated carbon fiber felt, reserves the rich and uniform micro-pore structure of the activated carbon fiber and has all meso-pores of high-quality powdered and granular activated carbon, so that the activated carbon fiber composite material has large adsorption capacity and has a wide range of application for adsorbing organic matters. Moreover, the filter element prepared from the material is resistant to high temperature as well as acid and alkali and can be widely applied to electroplating production lines of the PCB (Printed Circuit Board) industry.

Description

technical field [0001] The invention belongs to the technical field of activated carbon filter elements, and in particular relates to an activated carbon fiber composite material, a preparation method thereof and an activated carbon fiber composite filter element. Background technique [0002] In the electroplating industry, in order to make the coating bright and dense, additives are generally added. Among them, the most important brightener, as an organic substance, inevitably has phenomena such as decomposition. After its decomposition, in addition to the decrease in the brightness of the coating, it may also cause disadvantages such as loose coating. In the past, regular carbon treatment was usually carried out on the plating solution, but carbon treatment will bring certain problems, such as loss of plating solution, difficulty in sedimentation of carbon powder, and subsequent filtration, etc., which increases the difficulty of operation and labor costs. [0003] The u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C02F9/02
Inventor 徐地华徐地明苏华弟曹四峰吴国芳梅领亮
Owner GUANGDONG ZHENGYE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap