Gravure glue

A glue and gravure printing technology, applied in the direction of adhesive type, hydrocarbon copolymer adhesive, etc., can solve the problems of paper backlighting, poor printing products, etc., and achieve the effect of improving the printing products and ink fastness

Inactive Publication Date: 2015-12-16
江苏琛亚印材科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the above problems, the present invention provides a kind of gravure printing glue, which solves the proble

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0010] Embodiment one

[0011] A kind of gravure printing glue, is to take mixed monomer, initiator, emulsifier, dispersant and water as raw material, wherein the consumption of initiator is 0.3% of the weight of mixed monomer, and the consumption of described emulsifier is the weight of mixed monomer 1.5% of the dispersant, the amount of the dispersant is 5% of the weight of the mixed monomer, and the amount of water is 100% of the weight of the mixed monomer; the weight percentage of the styrene is 50%, and the weight of the butadiene The percentage is 40%, and the weight percentage of the ethyl acrylate is 10%.

[0012] The initiator is ammonium persulfate, the emulsifier is sodium alkylbenzenesulfonate, and the dispersant is vinylbisstearamide.

Example Embodiment

[0013] Embodiment two

[0014] A kind of gravure printing glue, it is to take mixed monomer, initiator, emulsifier, dispersant and water as raw material, wherein the consumption of initiator is 0.2% of the weight of mixed monomer, and the consumption of emulsifier is 1% of the weight of mixed monomer %, the amount of dispersant is 3% of the weight of the mixed monomer, and the amount of water is 90% of the weight of the mixed monomer; the mixed monomer is composed of styrene, butadiene, ethyl acrylate, wherein the weight of styrene The percentage is 35%, the weight percentage of butadiene is 60%, and the weight percentage of ethyl acrylate is 5%.

[0015] The initiator is ammonium persulfate, the emulsifier is sodium alkylbenzenesulfonate, and the dispersant is vinylbisstearamide.

Example Embodiment

[0016] Embodiment three

[0017] A kind of gravure printing glue, it is to take mixed monomer, initiator, emulsifier, dispersant and water as raw material, wherein the consumption of initiator is 0.4% of the weight of mixed monomer, and the consumption of emulsifier is the % of mixed monomer weight , the amount of dispersant is 6% of the weight of the mixed monomer, and the amount of water is 110% of the weight of the mixed monomer; the mixed monomer is composed of styrene, butadiene, ethyl acrylate, wherein the weight percentage of styrene is 65%, butadiene is 25% by weight, and ethyl acrylate is 15% by weight.

[0018] The initiator is ammonium persulfate, the emulsifier is sodium alkylbenzenesulfonate, and the dispersant is vinylbisstearamide.

[0019] The gravure glue of the embodiment and the traditional gravure glue are used for paper gravure printing, and the paper produced by various latexes is compared. The paper of the gravure glue in the embodiment not only has an ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses gravure glue. According to the gravure glue, a mixed monomer, an initiator, an emulsifier, a dispersing agent and water are used as raw materials. The dosage of the initiator is 0.2%-0.4% of the weight of the mixed monomer, the dosage of the emulsifier is 1%-2% of the weight of the mixed monomer, the dosage of the dispersing agent is 3%-6% of the weight of the mixed monomer, and the dosage of the water is 90%-110% of the weight of the mixed monomer. The mixed monomer is prepared from, by weight, 35%-65% of styrene, 25%-60% of butadiene and 5%-15% of ethyl acrylate. The bonding firmness of SBR latex and the fast permeability of acrylic based emulsion are combined together; paper using the gravure glue is good in aluminum layer and printing ink firmness, and the surface scraping phenomenon of the paper is avoided; besides, certain folding resistance is achieved, and the quality of finished printed products is improved.

Description

technical field [0001] The invention belongs to the field of paper printing processing and relates to a gravure glue. Background technique [0002] As a kind of printing process, gravure printing has the advantages of thick ink layer, bright color, high saturation, high printing plate durability, stable quality of printed products, fast printing speed and other advantages in the field of printing, packaging and graphic publishing. occupies an extremely important position. [0003] However, due to the particularity of the gravure printing method, the paper produced by the general gravure glue (styrene-butadiene latex) is prone to the phenomenon of "reflecting light", which is also called rubbing. The metal effect of such paper after printing is very poor, and the surface is dull, which seriously affects the appearance of the printed product. Contents of the invention [0004] In order to solve the above problems, the present invention provides a kind of gravure glue, whic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J125/14C08F212/08C08F236/10C08F220/18
Inventor 范晓春
Owner 江苏琛亚印材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap