Method for manufacturing graphite oxide and apparatus therefor

A graphite and fossil technology, applied in the field of preparation of graphite oxide, can solve the problems of insufficient and effective removal of graphite oxide ions and impurities, achieve excellent dispersion, suppress explosion, and reduce costs

Active Publication Date: 2016-03-30
IDT INT
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, even this method cannot sufficiently and effectively remove ions and impurities contained in graphite oxide

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing graphite oxide and apparatus therefor
  • Method for manufacturing graphite oxide and apparatus therefor
  • Method for manufacturing graphite oxide and apparatus therefor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0069] In Examples of the present invention, the concentration of remaining metal ions in the prepared graphite oxide was measured by using an inorganic elemental analysis (ICP) method, and then compared. The concentrations of the remaining metal ions in graphite oxide (from which impurities were removed by conventional filter press method or centrifugation) and in graphite oxide (from which impurities were removed by using the filter membrane device of the present disclosure) are shown in Table 1 below. The concentration of the remaining metal ions. In Examples of the present invention, inorganic element analysis was performed by using ICP-AES equipment (iCAP-6000SERIES, Thermoelectron). Pretreatment was performed by using 3 mL of hydrochloric acid, 1 mL of nitric acid, and 1 mL of hydrofluoric acid. Samples containing 0.1 g or more were collected by using Teflon containers. The primary dilution ratio is 25 mL, and the secondary dilution ratio is 50 mL.

[0070] [Table 1] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The present application relates to a method and an apparatus for producing graphite oxide, the method comprising: producing a graphite slurry comprising graphite and sulfuric acid; producing graphite oxide slurry by injecting an oxidizing agent into the graphite slurry to oxidize the graphite; mixing a hydrogen peroxide solution into the graphite oxide slurry; and obtaining graphite oxide from the graphite oxide slurry by means of a filtration membrane apparatus.

Description

technical field [0001] The present disclosure relates to a method for producing graphite oxide and an apparatus for producing graphite oxide. Background technique [0002] In 2004, Professor Andre Geim of the University of Manchester and others succeeded in first mechanically exfoliating graphene from graphite by using the "scotch tape method", and discovered the properties of graphene by using the exfoliated graphene to study the quantum Hall effect. Excellent electrical conductivity. In 2008, researchers such as James Hone of Columbia University confirmed the excellent strength of graphene. In the same year, researchers such as Alexander Balandin of the University of California, Riverside measured the thermal conductivity of graphene to be 5,300 pW / mpK, which is twice that of carbon nanotubes. [0003] To prepare graphene, exfoliation of graphite oxide by applying thermal shock, graphite exfoliation by Prof. Andre Geim et al., surface growth, hydrazine reduction on graph...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B31/04B01D37/00
CPCC01B32/23B01J8/002B01J8/006B01J19/1862B01J19/1893
Inventor 洪尚填严成勋李明信
Owner IDT INT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com