A kind of naphtha reforming catalyst and preparation method thereof

A reforming catalyst and catalyst technology, which can be used in naphtha catalytic reforming, chemical instruments and methods, physical/chemical process catalysts, etc. The effect of structural selectivity

Active Publication Date: 2018-04-13
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] For the carrier γ-Al commonly used in industry at present 2 o 3 , in order to adjust its acidic function, CN96103410.6, CN200610144205.2 disclose the reforming catalyst containing molecular sieve, introduce β molecular sieve, SAPO molecular sieve to improve catalyst performance in active alumina carrier, but this kind of microporous molecular sieve often causes catalyst to have Strong cracking activity, and the product is easily restricted by molecular sieve channels, easy to deactivate by carbon deposition

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of naphtha reforming catalyst and preparation method thereof
  • A kind of naphtha reforming catalyst and preparation method thereof
  • A kind of naphtha reforming catalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] The preparation method of the mesoporous γ-alumina of the present invention is as follows: first mix the template agent, fatty alcohol, inorganic acid and aluminum source compound, react under the condition of pH 1-7, dry the reactant, and Roast at 300-600°C, preferably 350-450°C, preferably for 2-6 hours, remove the template agent, generate amorphous mesoporous alumina, then impregnate and introduce an appropriate amount of platinum, after drying, heat at 300-700°C, preferably 350- Mesoporous γ-alumina is obtained by calcining at 450°C, and the calcining time is preferably 2 to 12 hours.

[0029] Among the raw materials used in the method of the present invention, the molar ratio of the template agent to the aluminum source compound is preferably 1:20 to 80, and the molar ratio of the fatty alcohol to the aluminum source compound is preferably 20 to 60:1. Add the template agent to the fatty alcohol to dissolve it, Then add inorganic acid to adjust the pH value of the r...

example 1

[0061] Prepare mesoporous alumina by the method of the present invention

[0062] Get the MA-400 mesoporous amorphous alumina that 20g comparative example 1 makes, impregnate 24 hours at 25 ℃ with the impregnating solution that chloroplatinic acid is made into, contain the Pt of 0.05% in the impregnating solution (relative to the quality of alumina on a dry basis ), the liquid / solid volume ratio was 2:1, filtered, the obtained solid was dried at 120°C for 8 hours, and calcined in air at 400°C for 4 hours to obtain the carrier MA-400-005, and its specific surface area is shown in Table 1.

[0063] For the small angle XRD spectrum (0.5~5°) of MA-400-005 see figure 1 In the curve c, the characteristic diffraction peak of the (100) plane appears in this curve, indicating the existence of mesoporous structure.

[0064] MA-400-005 wide angle XRD spectrum (10~70°) such as image 3 As shown in the middle b curve, there are more obvious crystal diffraction peaks, indicating that the ...

example 2

[0066] Mesoporous alumina was prepared according to the method of Example 1, except that the prepared impregnation solution contained 0.10% Pt (relative to the mass of alumina on a dry basis), and the carrier MA-400-010 was obtained. The specific surface area is shown in Table 1.

[0067] The wide-angle XRD spectrum (10-70°) of MA-400-010 is as follows image 3 As shown in the middle c curve, there are more obvious crystal diffraction peaks, indicating that the amorphous alumina has transformed into γ-Al 2 o 3 crystal phase structure.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

A naphtha reforming catalyst, comprising a composite carrier and active components with the following content calculated on the basis of the carrier: 0.04-3.0% by mass of platinum, 0.04-5.0% by mass of Group VIIB metals, and 0.5-5.0% by mass of halogens. The composite support includes 0-80% by mass of γ-alumina and 20-100% by mass of mesoporous γ-alumina, and the preparation method of said mesoporous γ-alumina comprises template agent, fatty alcohol, inorganic acid Mix with aluminum source compound, fully react at pH 1-7, 1-100°C, dry the reaction product, and roast at 300-600°C for 2-12 hours to obtain amorphous mesoporous alumina, then use platinum-containing compound Solution impregnation, take the solid matter and dry it and bake it at 300-700°C. The template agent is polyethylene oxide-polypropylene oxide-polyethylene oxide tri-block copolymer, and the mole ratio of the template agent and the aluminum source compound The ratio is 1:1-200, and the molar ratio of the fatty alcohol to the aluminum source compound is 20-100:1. The catalyst has high isomerization and aromatization selectivity.

Description

technical field [0001] The invention relates to a hydrocarbon conversion catalyst and a preparation method thereof, in particular to a naphtha reforming catalyst and a preparation method thereof. Background technique [0002] Catalytic reforming is based on C 6 ~C 11 The naphtha fraction is used as the raw material, and under certain temperature, pressure, presence of hydrogen and catalyst, the raw material hydrocarbon molecules undergo reforming reactions such as cycloalkane dehydrogenation, linear paraffin dehydrogenation isomerization, and paraffin dehydrocyclization , the process of producing high-octane gasoline blending components or aromatics with cheap hydrogen as a by-product. Currently, supported dual-functional reforming catalysts widely used in catalytic reforming processes include hydrogenation / dehydrogenation functions provided by metal components and acidic isomerization functions provided by supports. The reforming catalyst is usually a dual (multi)metal c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J27/13C10G35/09
Inventor 张大庆王涛臧高山张玉红王嘉欣
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com