Double-sided adhesive asphalt-base and PET (polyethylene terephthalate)-carrier wet-laid waterproof roll and production process thereof

A waterproofing membrane, bitumen-based technology, applied in the direction of asphalt layered products, synthetic resin layered products, layered products, etc., can solve the problem of poor tensile properties of wet-laid waterproofing membranes and tearing strength of wet-laid waterproofing membranes Low peeling strength, low peeling strength of wet-laid waterproofing membrane, etc., to achieve the effect of high peeling strength, high tearing strength, and improved radiation resistance

Active Publication Date: 2016-06-01
WEIFANG HONGYUAN WATERPROOF MATERIAL
View PDF4 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The existing technology has the following defects: (1) the tensile properties of the wet-laid waterproof membrane are poor; (2) the peel strength of the wet-laid waterproof membrane is low; (3) the tear strength of the wet-laid waterproof membrane is low; (4) ) Poor heat aging resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Double-sided adhesive asphalt-base and PET (polyethylene terephthalate)-carrier wet-laid waterproof roll and production process thereof
  • Double-sided adhesive asphalt-base and PET (polyethylene terephthalate)-carrier wet-laid waterproof roll and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] Embodiment 1 A double-sided adhesive asphalt-based PET carrier wet-laid waterproof membrane

[0068] The waterproof membrane includes the following three parts:

[0069] The first part is a PET film as a carrier; the thickness of the PET film is 0.15mm;

[0070] The second part is two layers of modified asphalt layer, that is, wet-laid self-adhesive modified asphalt coating compound, and the thickness of wet-laid self-adhesive modified asphalt coating compound is 1 mm;

[0071] The third part is two layers of PE film coated with silicone oil, and the thickness of the silicon-coated PE film is 0.04mm.

[0072] The raw material components of the wet paving modified asphalt layer sizing material, in parts by mass, include:

[0073] Raw material components by mass

[0074] 250 parts of petroleum asphalt

[0075] Minus 28 parts of second-line oil

[0076] SBS10 copies

[0077] SIS18 copies

[0078] SBR20 copies

[0079] 10 parts petroleum resin

[0080] 3 parts coum...

Embodiment 2

[0095] Embodiment 2 A double-sided adhesive asphalt-based PET carrier wet-laid waterproof membrane

[0096] The waterproof membrane includes the following three parts:

[0097] The first part is a PET film as a carrier; the thickness of the PET film is 0.1mm;

[0098] The second part is two layers of wet-laid self-adhesive modified asphalt coating compound, and the thickness of the wet-laid self-adhesive modified asphalt coating compound is 0.8mm;

[0099] The third part is two layers of PE film coated with silicone oil, and the thickness of the silicon-coated PE film is 0.03mm.

[0100] The raw material components of the wet paving modified asphalt layer sizing material, in parts by mass, include:

[0101] Raw material components by mass

[0102] 245 parts of petroleum asphalt

[0103] Minus 25 parts of second-line oil

[0104] SBS8 copies

[0105] SIS16 copies

[0106] SBR15 copies

[0107] 11 parts petroleum resin

[0108] 2 parts coumarone resin

[0109] Anti-str...

Embodiment 3

[0123] Embodiment 3 A double-sided adhesive asphalt-based PET carrier wet-laid waterproof membrane

[0124] The waterproof membrane includes the following three parts:

[0125] The first part is a PET film as a carrier; the thickness of the PET film is 0.2mm;

[0126] The second part is two layers of wet-laid self-adhesive modified asphalt coating compound, and the thickness of wet-laid self-adhesive modified asphalt coating compound is 1.5mm;

[0127] The third part is two layers of PE film coated with silicone oil, and the thickness of the silicon-coated PE film is 0.05mm.

[0128] The raw material components of the wet paving modified asphalt layer sizing material, in parts by mass, include:

[0129] Raw material components by mass

[0130] 260 parts of petroleum asphalt

[0131] Minus 32 parts of second-line oil

[0132] SBS9 copies

[0133] SIS20 copies

[0134] SBR18 copies

[0135] 12 parts petroleum resin

[0136] 4 parts coumarone resin

[0137] Anti-strippi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flash pointaaaaaaaaaa
ignition pointaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a double-sided adhesive asphalt-base and PET (polyethylene terephthalate)-carrier wet-laid waterproof roll. The waterproof roll comprises a PET film, a modified asphalt layer and PE (polyethylene) film, wherein the PET film is 0.1-0.2 mm thick, the modified asphalt layer is 0.7-1.5 mm thick, and the PE film is 0.03-0.05 mm thick; raw material components of the modified asphalt layer comprise, in parts by mass, 245-260 parts of petroleum asphalt, 25-32 parts of second vacuum side-stream oil, 8-10 parts of SBS, 16-20 parts of SIS, 15-20 parts of SBR, 10-12 parts of petroleum resin, 2-4 parts of coumarone resin, 1-3 parts of an anti-stripping agent, 0.8-1.2 parts of an antioxidant, 50-60 parts of cement and 40-50 parts of talcum powder. The waterproof roll has good tensile property, high tearing strength and peeling strength, heat resistance and aging resistance.

Description

technical field [0001] The invention relates to a wet-laid waterproof coiled material, in particular to a double-sided adhesive asphalt-based PET carrier wet-laid waterproof coiled material and a production process thereof, belonging to the field of building waterproof materials. Background technique [0002] Wet-laid self-adhesive waterproofing membrane is a high-performance waterproofing membrane. It is based on synthetic rubber, high-quality heavy-duty asphalt, etc., high-quality polyethylene film, fine sand aluminum foil as the upper surface material or no film (double-sided self-adhesive), using peelable silicon-coated film or silicon-coated crepe paper as the surface material. A self-adhesive waterproof membrane made of anti-adhesive isolation material. [0003] The wet-laid self-adhesive waterproof membrane has low requirements on the base surface, and can be constructed on a wet base surface; it shortens the construction period and saves costs; it can achieve full a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B11/04B32B27/06B32B27/36B32B27/32B32B37/02C08L95/00C08L53/02C08L9/06C08L27/02C08L45/02C08K13/02C08K3/34
CPCB32B11/046B32B27/32B32B27/36B32B37/02B32B2250/03B32B2305/30B32B2307/306B32B2307/552B32B2323/04B32B2395/00B32B2419/00C08L95/00C08L2201/08C08L2205/035C08L53/02C08L9/06C08L27/02C08L45/02C08K13/02C08K3/34
Inventor 刘兴邦郑风启郑庆涛王永效徐燕
Owner WEIFANG HONGYUAN WATERPROOF MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More