A kind of low chromatic aberration polyester wool-like type differential shrinkage composite yarn and preparation method thereof

A composite yarn and different shrinkage technology, which is applied in the direction of single-component polyester rayon, rayon manufacturing, melt spinning, etc., can solve the problem of increased air content in PET different shrinkage mixed fiber composite yarn fabrics, etc.

Active Publication Date: 2017-12-15
JIANGSU HENGLI CHEM FIBER
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Increased air content in PET different shrinkage blended composite silk fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of low chromatic aberration polyester wool-like type differential shrinkage composite yarn and preparation method thereof
  • A kind of low chromatic aberration polyester wool-like type differential shrinkage composite yarn and preparation method thereof
  • A kind of low chromatic aberration polyester wool-like type differential shrinkage composite yarn and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0084] A method for preparing low-color-difference polyester wool-like differential shrinkage composite yarn, the main process includes:

[0085] (1) Preparation of catalyst magnesium ethylene glycol:

[0086] Add ethylene glycol into the single-chamber electrolytic cell, the supporting electrolyte is magnesium chloride, the metal magnesium block is the anode, and the cathode is graphite; connect direct current, the initial voltage is 6V, the cathode current density is 150mA, and electrolyze for 10 hours at 50°C. Take out the electrode to obtain a white suspension; filter under reduced pressure, wash the white solid with absolute ethanol, and dry to obtain magnesium ethylene glycol;

[0087] (2) Preparation of polyester, including esterification reaction and polycondensation reaction:

[0088] Esterification reaction:

[0089] Use terephthalic acid and ethylene glycol as raw materials, the molar ratio of ethylene glycol to terephthalic acid is 1.2:1, add anti-ether agent sod...

Embodiment 2

[0123] A method for preparing low-color-difference polyester wool-like differential shrinkage composite yarn, the main process includes:

[0124] (1) Preparation of catalyst magnesium ethylene glycol:

[0125] Add ethylene glycol into the single-chamber electrolytic cell, the supporting electrolyte is magnesium chloride, the metal magnesium block is the anode, and the cathode is graphite; connect direct current, the initial voltage is 10V, the cathode current density is 200mA, electrolyze at 60°C for 12 hours, after the electrolysis ends Take out the electrode to obtain a white suspension; filter under reduced pressure, wash the white solid with absolute ethanol, and dry to obtain magnesium ethylene glycol;

[0126] (2) Preparation of polyester, including esterification reaction and polycondensation reaction:

[0127] Esterification reaction:

[0128] Using terephthalic acid and ethylene glycol as raw materials, the molar ratio of ethylene glycol to terephthalic acid is 2.0:...

Embodiment 3

[0162] A method for preparing low-color-difference polyester wool-like differential shrinkage composite yarn, the main process includes:

[0163] (1) Preparation of catalyst magnesium ethylene glycol:

[0164] Add ethylene glycol into the single-chamber electrolytic cell, the supporting electrolyte is magnesium chloride, the metal magnesium block is the anode, and the cathode is graphite; connect direct current, the initial voltage is 7V, the cathode current density is 160mA, and electrolyze for 11 hours at 55°C. Take out the electrode to obtain a white suspension; filter under reduced pressure, wash the white solid with absolute ethanol, and dry to obtain magnesium ethylene glycol;

[0165] (2) Preparation of polyester, including esterification reaction and polycondensation reaction:

[0166] Esterification reaction:

[0167] Using terephthalic acid and ethylene glycol as raw materials, the molar ratio of ethylene glycol to terephthalic acid is 1.5:1, adding anti-ether agen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
shrinkageaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention relates to low-color-difference polyester wool-like different-shrinkage complex yarn and a preparation method thereof. The low-color-difference polyester wool-like different-shrinkage complex yarn is prepared through carrying out fiber intermingling on low-color-difference polyester POY (Pre-Oriented Yarn) and low-color-difference polyester FDY (Fully Drawn Yarn), wherein the low-color-difference polyester POY forms small yarn loops which surround the low-color-difference polyester FDY; the low-color-difference polyester POY and the low-color-difference polyester FDY are made from polyester through carrying out dissolving and washing and then carrying out spinning. The low-color-difference polyester wool-like different-shrinkage complex yarn has the rupture strength not lower than 3.0cN / dtex, the breaking elongation of 40.0+ / -3.0%, the crimp contraction of 5.50+ / -3.0%, the interlacing degree of 95+ / -5 / m, the fiber number of 150dtex to 300dtex and the color difference [delta]E smaller than 0.200. According to the low-color-difference polyester wool-like different-shrinkage complex yarn and the preparation method thereof, ethylene glycol magnesium is relatively mild and has a very small thermal degradation coefficient, and the oligomers are reduced during polymerization and are further reduced during washing, so that during the dyeing and postprocessing thermosetting of polyester fibers, the amount of the oligomers migrating to the outside of the fibers from the inside is reduced, the occurrence of color spots and streaks is reduced, and the level dyeability and rubbing fastness of the fibers are guaranteed.

Description

technical field [0001] The invention belongs to the technical field of polyester preparation, and relates to a low-color-difference polyester wool-like differential shrinkage composite yarn and a preparation method thereof, in particular to a polycondensation catalyst using a mixture of ethylene glycol magnesium and ethylene glycol antimony and polyester chips Low-color-difference polyester wool-like differential shrinkage composite yarn boiled and washed with water and solvent at 120-130°C and 0.2-0.3 MPa and its preparation method. Background technique [0002] Polyethylene terephthalate (PET) is a polymer with excellent properties. PET is widely used for its high modulus, high strength, crispness, good shape retention, purity and hygiene, and good barrier properties. In the fields of fiber, bottle packaging, film and sheet, etc., the output is increasing year by year, and the industry status has been significantly improved. [0003] PET is a symmetrical linear macromolec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/92D01F1/10C08G63/86C08G63/83C08G63/183C08G63/90D02G3/02D01D7/00D01D5/088D01D5/08
CPCC08G63/183C08G63/83C08G63/866C08G63/90D01D5/08D01D5/088D01D7/00D01F1/10D01F6/92D02G3/02
Inventor 张学东马文平沈建根王力军
Owner JIANGSU HENGLI CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com