Ultraviolet curing vacuum coating metal primer capable of achieving electrostatic spraying

A technology of vacuum coating and electrostatic spraying, applied in coatings, powder coatings, polyester coatings, etc., can solve problems such as hindering the development of UV-curing vacuum coating coatings, poor spraying quality at the edges of products, and low production efficiency of enterprises. The effect of focusing on excellent, improving light curing speed and improving utilization rate

Active Publication Date: 2016-06-15
GUANGDONG SHEN ZHAN IND CO LTD
View PDF6 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, ultraviolet curing vacuum coating coatings cannot be sprayed electrostatically. The reason is that it is difficult for coatings to meet the requirements of vacuum coating and electrostatic spraying at the same time. Nowadays, air spraying and other methods are mainly used for construction. The phenomenon of coating overspray is serious, the consumption of paint is large, and the utilization rate of coatings is high. Low, harsh working environment, serious pollution, and poor quality of spraying on the edge of the product, resulting in low production efficiency, low yield rate, increased cost, and reduced profit, hindering the development of the UV-curable vacuum coating coating industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultraviolet curing vacuum coating metal primer capable of achieving electrostatic spraying
  • Ultraviolet curing vacuum coating metal primer capable of achieving electrostatic spraying
  • Ultraviolet curing vacuum coating metal primer capable of achieving electrostatic spraying

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] S1. According to the ratio shown in Table 1, add the UV-curable vacuum coating resin, reactive diluent, and photoinitiator into the stirring tank and stir for 3 hours to disperse evenly;

[0036] S2. Add a leveling agent, an adhesion promoter, a conductive agent, and an electrostatic diluent, and stir for 1 hour to obtain a UV-curable vacuum coating metal primer that can be electrostatically sprayed.

Embodiment 2

[0038] S1. According to the ratio shown in Table 1, add the UV-curable vacuum coating resin, reactive diluent, and photoinitiator into the stirring tank and stir for 2 hours to disperse evenly;

[0039] S2. Add a leveling agent, an adhesion promoter, a conductive agent, and an electrostatic diluent, and stir for 2 hours to obtain a UV-curable vacuum coating metal primer that can be electrostatically sprayed.

Embodiment 3

[0041] S1. According to the ratio shown in Table 1, add the UV-curable vacuum coating resin, reactive diluent, and photoinitiator into the stirring tank and stir for 4 hours to disperse evenly;

[0042] S2. Add a leveling agent, an adhesion promoter, a conductive agent, and an electrostatic diluent, and stir for 1 hour to obtain a UV-curable vacuum coating metal primer that can be electrostatically sprayed.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses ultraviolet curing vacuum coating metal primer capable of achieving electrostatic spraying and a preparation method thereof.The ultraviolet curing vacuum coating metal primer capable of achieving electrostatic spraying is prepared from, by weight, 5-20 parts of urethane acrylate, 10-20 parts of epoxy acrylate, 0-5 parts of pure acrylate, 5-10 parts of polyesteracrylate, 30-40 parts of trimethylolpropane triacrylate, 10-20 parts of low-functionality active diluted monomers, 2-5 parts of photoinitiator, 0.05-0.1 part of a flatting agent, 0.05-0.5 part of adhesion promoter, 0.01-0.5 part of a conductive agent and 3-5 parts of electrostatic thinner.The ultraviolet curing vacuum coating metal primer prepared through the method can be used for electrostatic spraying, has the advantages of being good in coating performance, good in adhesion, high in salt fog resistance, high in production efficiency, high in paint utilization rate and the like, and has wide market prospects.

Description

technical field [0001] The invention belongs to the technical field of ultraviolet light curing coatings, in particular, the invention relates to an ultraviolet light curing vacuum coating metal primer which can be electrostatically sprayed. Background technique [0002] Vacuum coating technology is a new technology developed in the past ten years. It can coat a thin metal layer on the surface of the plated parts to give the base material a metallic luster. In the process of vacuum coating, the vacuum coating primer must be coated on the surface of the substrate first, otherwise the coated metal film is easy to fall off. Therefore, the quality of the coating depends largely on the quality of the primer. [0003] At present, ultraviolet curing vacuum coating coatings cannot be sprayed electrostatically. The reason is that it is difficult for coatings to meet the requirements of vacuum coating and electrostatic spraying at the same time. Nowadays, air spraying and other method...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/10C09D175/14C09D167/06C09D133/04C09D5/46
CPCC08L2205/025C08L2205/03C08L2205/035C09D5/03C09D163/10C09D175/14C08L75/14C08L67/06C08L33/04C08L63/10
Inventor 张永涛黄剑彬陈锦珍黄鸿宏黄洪填
Owner GUANGDONG SHEN ZHAN IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap