High-load wear resistant stacking machine arm and preparation method

A palletizing robot arm, wear-resistant technology, applied in the direction of chemical instruments and methods, cleaning methods and utensils, cleaning methods using liquids, etc., can solve the problem of low density, short service life and load capacity of palletizing robot arms No high-level problems, to achieve significant oxygen removal effect, good quality, simple and effective preparation method

Active Publication Date: 2016-07-27
HEXIAN LONGSHENG PRECISION MACHINERY CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, defects such as slag inclusions, pores, shrinkage cavities, and shrinkage porosity often occur in the preparation process of palletizing robot arms at present, so that the internal structure of the prepared palletizing robot arm is not high in density, hardness is not enough, and the load capacity is not high. Easy to be worn out, short service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A high-load wear-resistant palletizing machine arm, composed of the following weight percentages: C: 3.5, Cr: 18%, Si: 0.7%, Mo: 0.8%, Mn: 0.8%, Ni: 0.2%, V: 0.03 %, S: 0.018%, P: 0.03%, Zn: 0.02%.

[0022] The preparation method comprises the following steps:

[0023] (1) First, take raw material scrap steel and pig iron by weight percentage, then put them into an induction furnace for melting and carry out pre-deoxidation operation, then add ferrochrome, ferromanganese and ferrosilicon, and wait until all the raw materials are dissolved to obtain molten iron;

[0024] (2) get molten iron sample and carry out content analysis, adjust described molten iron to the requirement of qualified molten iron according to analysis result, then add limestone;

[0025] (3) Then the temperature of the qualified molten iron is raised to 1550° C., adding silicon that accounts for 0.1% of the quality of the qualified molten iron, and putting it in once every 15 minutes, and putting it...

Embodiment 2

[0029] A high-load wear-resistant palletizing machine arm, composed of the following weight percentages: C: 3.6%, Cr: 16%, Si: 0.7%, Mo: 0.8%, Mn: 0.8%, Ni: 0.12%, V: 0.02%, S: 0.02%, P: 0.03%, Zn: 0.02%.

[0030] The preparation method comprises the following steps:

[0031] (1) First, take raw material scrap steel and pig iron by weight percentage, then put them into an induction furnace for melting and carry out pre-deoxidation operation, then add ferrochrome, ferromanganese and ferrosilicon, and wait until all the raw materials are dissolved to obtain molten iron;

[0032] (2) get molten iron sample and carry out content analysis, adjust described molten iron to the requirement of qualified molten iron according to analysis result, then add limestone;

[0033] (3) Then the temperature of the qualified molten iron is raised to 1600° C., adding silicon that accounts for 0.2% of the quality of the qualified molten iron, and puts it in once every 16 minutes, and puts it in th...

Embodiment 3

[0037] A high-load wear-resistant palletizing machine arm, composed of the following weight percentages: C: 3.5%, Cr: 18%, Si: 0.7%, Mo: 0.8%, Mn: 0.9%, Ni: 0.3%, V: 0.03%, S: 0.018%, P: 0.04%, Zn: 0.04%.

[0038] The preparation method comprises the following steps:

[0039] (1) First, take raw material scrap steel and pig iron by weight percentage, then put them into an induction furnace for melting and carry out pre-deoxidation operation, then add ferrochrome, ferromanganese and ferrosilicon, and wait until all the raw materials are dissolved to obtain molten iron;

[0040] (2) get molten iron sample and carry out content analysis, adjust described molten iron to the requirement of qualified molten iron according to analysis result, then add limestone;

[0041] (3) Then the temperature of the qualified molten iron is raised to 1550° C., adding silicon that accounts for 0.3% of the quality of the qualified molten iron, and dropping it once every 20 minutes, and putting it i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-load wear resistant stacking machine arm and a preparation method. The high-load wear resistant stacking machine arm consists of the following components in percentage by weight: 3.0-4.5% of C, 12-25% of Cr, 0.6-0.9% of Si, 0.4-1.3% of Mo, 0.4-1.4% of Mn, 0.2-0.8% of Ni, 0.01-0.06% of V, 0.02-0.08% of S, 0.01-0.06% of P, and 0.01-0.06% of Zn. The preparation method comprises the following steps: firstly, waste steel and pig iron are molten and pre-deoxidized; then, ferrochromium, ferromanganese and ferrosilicon are added to obtain molten iron; silicon is added to perform final deoxidation and slagging; and after the molten iron is molded through pouring, the heat treatment and the surface treatment are performed. The stacking machine arm is excellent in high-load capacity and hardness, is simple and effective in preparation method, and is suitable for large-scale industrial popularization.

Description

technical field [0001] The invention relates to the field of alloy materials, in particular to a high-load wear-resistant palletizing machine arm product and a preparation method. Background technique [0002] Palletizer, it is a device that automatically stacks bags, cartons or other packaging materials conveyed by the conveyor into stacks according to the working method required by the customer's process, and transports the stacked materials. At present, there are more automatic palletizers on the market. It is a high-tech product integrating machinery and electricity. The medium and low-level palletizers can meet the production needs of medium and low output. According to the required grouping method and number of layers, the palletizing of various products such as bags, rubber blocks, boxes, etc. can be completed. The optimized design makes the stacking shape compact and neat. Automatic palletizers are divided into two types according to the level of intelligence: robot...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C37/10C22C33/08C21C7/06C21D5/00B08B3/02
CPCB08B3/02C21C7/0037C21C7/06C21D5/00C22C33/08C22C37/10
Inventor 韩年珍程东华何凯
Owner HEXIAN LONGSHENG PRECISION MACHINERY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap