A kind of hydrotreating catalyst and its preparation method and application

A hydrotreating and catalyst technology, applied in physical/chemical process catalysts, chemical instruments and methods, metal/metal oxide/metal hydroxide catalysts, etc., can solve the problem of excessive metal dispersion, unfavorable type II metal active phase, Strong interaction, etc.

Active Publication Date: 2018-06-26
PETROCHINA CO LTD +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, excessive dispersion of metals is not conducive to the formation of type II metal active phases during the vulcanization process, and the adsorption and hydrogenation removal activity of nitrides with complex molecular structures is not high.
[0007] In summary, the interaction between the conventional alumina support and the active metal is too strong, resulting in a high degree of dispersion of the active metal, which is not conducive to the reduction and sulfidation of the active metal, resulting in a high dispersion of the supported hydrodenitrogenation catalyst based on alumina. , The problem of poor vulcanization performance, the simple surface modification of alumina carrier or the addition of organic additives in the metal impregnation solution will have the problem of unsatisfactory active metal dispersion and vulcanization degree

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hydrotreating catalyst and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The present embodiment provides a kind of preparation method of hydrotreating catalyst, it comprises the following steps:

[0042] Step 1: Weigh 200g of alumina dry rubber powder and 8g of turmeric powder, add 90mL of ammonium bicarbonate solution (prepared by adding 12g of ammonium bicarbonate per 90mL of deionized water) and mix well; then add 90mL of nitric acid The solution (prepared by adding 10 g of nitric acid with a concentration of 65% by mass for every 90 mL of deionized water) was mixed and stirred evenly to obtain the material. Knead the material on the screw extruder for 15 minutes to make a clover strip-shaped wet material with a diameter of 1.5 mm, then dry the clover strip-shaped wet material naturally for 24 hours, then dry it at 120 ° C for 4 hours, and then transfer it to In a muffle furnace, calcinate at 700°C for 3 hours to obtain an alumina carrier, which is crushed into 20-40 mesh granules for future use.

[0043] Step 2: Weigh 50g of the above c...

Embodiment 2

[0046] The present embodiment provides a kind of preparation method of hydrotreating catalyst, it comprises the following steps:

[0047] Step 1: Weigh 200g of pseudo-boehmite powder and 8g of turmeric powder, add 90mL of ammonium bicarbonate solution (prepared by adding 12g of ammonium bicarbonate per 90mL of deionized water) and mix well; then add 90mL Nitric acid solution (prepared by adding 10 g of nitric acid with a mass percent concentration of 65% per 90 mL of deionized water) was mixed and stirred evenly to obtain materials. Knead the material on the screw extruder for 15 minutes to make a clover strip-shaped wet material with a diameter of 1.5 mm, then dry the clover strip-shaped wet material naturally for 24 hours, then dry it at 120 ° C for 4 hours, and then transfer it to In a muffle furnace, calcinate at 700°C for 3 hours to obtain an alumina carrier, which is crushed into 20-40 mesh granules for future use.

[0048] Step 2: Weigh 50g of the above crushed alumina...

Embodiment 3

[0051] The present embodiment provides a kind of preparation method of hydrotreating catalyst, it comprises the following steps:

[0052] Step 1: Weigh 200g of pseudo-boehmite powder and 8g of turmeric powder, add 90mL of ammonium bicarbonate solution (prepared by adding 12g of ammonium bicarbonate per 90mL of deionized water) and mix well; then add 90mL Nitric acid solution (prepared by adding 10 g of nitric acid with a mass percent concentration of 65% per 90 mL of deionized water) was mixed and stirred evenly to obtain materials. Knead the material on the screw extruder for 15 minutes to make a clover strip-shaped wet material with a diameter of 1.5 mm, then dry the clover strip-shaped wet material naturally for 24 hours, then dry it at 120 ° C for 4 hours, and then transfer it to In a muffle furnace, calcinate at 700°C for 3 hours to obtain an alumina carrier, which is crushed into 20-40 mesh granules for future use.

[0053] Step 2: Weigh 50g of the above crushed alumina...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a hydrotreating catalyst and its preparation method and application. The hydrotreating catalyst adopts a complexing agent roasting-drying combination method. First, an alumina carrier is prepared, and then the surface is impregnated with a complexing agent and roasted and modified in an inert gas to obtain a modified alumina carrier. Finally, the modified alumina carrier is obtained The hydrotreating catalyst is finally prepared by impregnating the loaded metal active component in volumetric steps and directly drying without roasting. The preparation method of the hydrotreating catalyst provided by the invention can effectively improve the problem of high L-acid ratio on the surface of the alumina carrier, and at the same time can effectively weaken the strong interaction between the active metal and the alumina carrier; the prepared hydrotreating catalyst is suitable for The hydrodesulfurization and denitrification process of coked wax oil with high sulfur and nitrogen content not only has good hydrodenitrification activity, but also has good hydrodesulfurization activity.

Description

technical field [0001] The invention belongs to the field of catalysts, and relates to a hydrogenation treatment catalyst, a preparation method thereof and an application of the hydrogenation treatment catalyst in hydrodenitrogenation and desulfurization of coking wax oil. Background technique [0002] With the intensification of the trend of heavy and inferior crude oil in the world, and the continuous improvement of gasoline and diesel quality requirements in environmental protection regulations, inferior heavy oil is delayed coking, coking wax oil is hydrotreated as raw material for catalytic cracking or hydrocracking. In order to maximize the yield of light oil products, the production of high-quality and low-quality coker wax oil has become the preferred process for delayed coking. Therefore, the hydrotreating of low-quality coker gas oil with high nitrogen content puts forward higher performance requirements for the catalyst. [0003] At present, industrial catalysts ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/883B01J23/888B01J23/882C10G45/08
CPCC10G45/08B01J23/002B01J23/882B01J23/883B01J23/888B01J2523/00C10G2300/70C10G2300/202B01J35/635B01J35/633B01J35/647B01J35/615B01J2523/31B01J2523/68B01J2523/847B01J2523/69B01J2523/845
Inventor 周亚松陈楠魏强张玲玲刘亭亭丁思佳周文武
Owner PETROCHINA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products