Sealing glass powder for electric connectors, preparation method for sealing glass powder and sealing process of sealing glass powder
A technology for sealing glass and electrical connectors, which is applied in connection, line/collector parts, circuits, etc., can solve problems such as failure to meet performance requirements, poor product stability, and product resistance drop, and achieve improved chemical stability and Electrical insulation, lower melting temperature, and improve high-temperature insulation performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0070] A preparation method of sealing glass powder for electrical connectors specifically includes the following steps:
[0071] 1). Select raw materials according to the following weight percentages:
[0072] K 2 O: 3%-7%
[0073] MgO: 1%-5%
[0074] CaO: 3%-7%
[0075] SrO: 0.5%-2%
[0076] BaO: 20%-30%
[0077] ZnO: 0.05%-1%
[0078] Fe 2 O 3 :0.05%-1%
[0079] Al 2 O 3 : 5%-15%
[0080] SiO 2 : 40%-60%
[0081] ZrO 2 : 0.5% -1.5%
[0082] TiO 2 :0.05%-1%
[0083] V 2 O 5 : 1%-7%
[0084] Na 3 AlF 6 : 1%-3%;
[0085] 2) Put the above ingredients in a ball mill for ball milling to make the ingredients evenly mixed, the grinding speed is 300r / min, and the time is 20-40min;
[0086] 3). Then place the ball milled and mixed materials in a corundum crucible or platinum crucible, and place the crucible in a silicon-molybdenum furnace. In the air, the temperature rises from room temperature to 700-900°C at a heating rate of 10°C / min. After being kept at 700-900℃ for 20-40min, the temperature will be...
Example Embodiment
[0099] Example 1
[0100] A sealing glass powder for electrical connectors, calculated by weight percentage, prepared from the following raw materials: K 2 O is 3%, MgO is 2%, CaO is 4%, SrO is 0.5%, BaO is 26%, ZnO is 0.9%, Fe 2 O 3 0.05%, Al 2 O 3 15%, SiO 2 45%, ZrO 2 0.5%, TiO 2 Is 0.05%, V 2 O 5 2%, Na 3 AlF 6 Is 1%.
[0101] A preparation method of sealing glass powder for electrical connectors specifically includes the following steps:
[0102] 1). Select raw materials according to the following weight percentages:
[0103] K 2 O is 3%, MgO is 2%, CaO is 4%, SrO is 0.5%, BaO is 26%, ZnO is 0.9%, Fe 2 O 3 0.05%, Al 2 O 3 15%, SiO 2 45%, ZrO 2 0.5%, TiO 2 Is 0.05%, V 2 O 5 2%, Na 3 AlF 6 Is 1%.
[0104] 2) Put the above-prepared raw materials in a ball mill for ball milling to make the ingredients evenly mixed, the grinding speed is 300r / min, and the time is 20min;
[0105] 3) Put the ball-milled and mixed materials in step (2) in a corundum crucible or platinum crucible, place the ...
Example Embodiment
[0123] Example 2
[0124] A sealing glass powder for electrical connectors, calculated by weight percentage, prepared from the following raw materials: K 2 O is 4.5%, MgO is 3.5%, CaO is 5.5%, SrO is 0.75%, BaO is 21.5%, ZnO is 0.75%, Fe 2 O 3 0.5%, Al 2 O 3 10%, SiO 2 Is 44.5%, ZrO 2 1%, TiO 2 0.5%, V 2 O 5 4%, Na 3 AlF 6 Is 3%.
[0125] A preparation method of sealing glass for electrical connectors specifically includes the following steps:
[0126] 1). Select raw materials according to the following weight percentages: K 2 O is 4.5%, MgO is 3.5%, CaO is 5.5%, SrO is 0.75%, BaO is 21.5%, ZnO is 0.75%, Fe 2 O 3 0.5%, Al 2 O 3 10%, SiO 2 Is 44.5%, ZrO 2 1%, TiO 2 0.5%, V 2 O 5 4%, Na 3 AlF 6 Is 3%,
[0127] 2) Put the above-prepared raw materials in a ball mill for ball milling to make the ingredients evenly mixed, the grinding speed is 300r / min, and the time is 15min;
[0128] 3) Put the ball-milled and mixed materials in step (2) in a corundum crucible or platinum crucible, place the...
PUM
Property | Measurement | Unit |
---|---|---|
Transition temperature | aaaaa | aaaaa |
Density | aaaaa | aaaaa |
Thermal expansion coefficient | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap