Preparation method of high-strength waterproof composite coal briquette adhesive
A compound type and adhesive technology, which is applied in the petroleum industry, solid fuel, fuel, etc., can solve the problems that it is difficult to meet the transportation strength and waterproof requirements of coal briquettes, reduce lime activity, etc., and achieve good impact resistance and hydrophilicity Strong, high thermal strength effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0027] Example 1
[0028] Take 5.52kg of magnesium oxide, 1.49kg of high-energy activator, 0.168kg of surfactant, and 12.32kg of bituminous coal. After crushing and sieving, weigh the ingredients according to the weight percentage of the ingredients, and weigh the biomass fibers according to the ratio. Take water Put 27.3kg in a container, add the biomass fiber to the water, stir it with a stirrer after it fully absorbs water, so that the biomass fiber is well dispersed in the water; then the weighed components are powdered Add, and stir while adding the ingredients until they are evenly mixed.
[0029] The anthracite pulverized coal is crushed to below 3.0mm, the prepared binder is mixed with the anthracite pulverized coal at a weight ratio of 21:79, and the anthracite pulverized coal is mixed with 79kg. After fully stirring, grinding, and standing for 8 hours, it will be shaped The briquette with a diameter of 40mm and a weight of 40g is pressed on the machine with a pressure of...
Example Embodiment
[0030] Example 2
[0031] Take 5.04 kg of magnesium oxide 24%, 1.05 kg of activator, 2.52 kg of biomass fiber, 0.105 kg of surfactant, 12.285 kg of bituminous coal, and 23.1 kg of water. The production steps are as in Example 1.
[0032] The anthracite pulverized coal is crushed to below 3.0mm, the prepared binder is mixed with the anthracite pulverized coal at a weight ratio of 21:79, and the anthracite pulverized coal is mixed with 79kg. The briquette with a diameter of 40mm and a weight of 40g is pressed on the machine with a pressure of 20MPa, and then dried at a temperature of about 100°C for 3 hours. After testing, the cold compressive strength of the briquette is higher than 4.2MPa, and the hot compressive strength is more than 1.2MPa. The briquette falls freely from a height of 2m to a thick steel plate three times without breaking. The stability index exceeds 81%, and the wear resistance index reaches more than 96%; the air-dry base fixed carbon content of briquette is 72...
Example Embodiment
[0033] Example 3
[0034] Take 7.14 kg of magnesium oxide, 1.68 kg of activator, 1.26 kg of biomass fiber, 0.21 kg of surfactant, 10.71 kg of bituminous coal, and 25.2 kg of water. The production steps are the same as in Example 1.
[0035] The anthracite pulverized coal is crushed to below 3.0mm, the prepared binder is mixed with the anthracite pulverized coal at a weight ratio of 21:79, and the anthracite pulverized coal is mixed with 79kg. The briquette with a diameter of 40mm and a weight of 40g is pressed on the machine with a pressure of 20MPa, and then dried at a temperature of about 100°C for 3 hours. After testing, the cold compressive strength of the briquette is higher than 4.13MPa, and the hot compressive strength is more than 1.14MPa. The briquette falls freely from a height of 2m to a thick steel plate three times without breaking. The stability index exceeds 88%, and the wear resistance index reaches more than 92%; the air-dry base fixed carbon content of briquettes...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap