Ecological permeable concrete and preparing method thereof

A permeable concrete and ecological technology, applied in the field of new ecological permeable concrete and its preparation, can solve the problem of high production energy consumption, achieve the effects of reducing production costs, being suitable for wide-scale use, and easy to obtain materials

Active Publication Date: 2016-12-07
上海每天生态科技发展有限公司
View PDF5 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] In view of the above-mentioned defects of the prior art, the technical problem to be solved by the present invention is to provide a new type of ecological permeable concrete, which uses industrial by-products such as gypsum, steel slag, construction waste, and tailings as the main raw materials. , can overcome the shortcomings of high energy consumption of traditional permeable concrete production and has high strength, easy to obtain materials, low cost, simple preparation process, does not require high temperature calcination, and is conducive to environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ecological permeable concrete and preparing method thereof
  • Ecological permeable concrete and preparing method thereof
  • Ecological permeable concrete and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] Three components of permeable concrete: modified gypsum cementitious material 20%, aggregate 75%, water 5%.

[0065] The main ingredients of the modified gypsum cementitious material are: 40% gypsum, 30% slag powder, 20% steel slag powder, and 10% cement, wherein the gypsum is a single-component desulfurized gypsum;

[0066] Construction admixtures and their percentages to the mass of main materials are: retarder 2‰, water reducing agent 2‰, cellulose 0.5‰;

[0067] The aggregate is steel slag, the particle size of coarse aggregate is 3-5mm, and the dosage is 100%;

[0068] The performance is as follows:

[0069]

Embodiment 2

[0071] Three components of permeable concrete: modified gypsum cementitious material 10%, aggregate 88%, water 2%.

[0072] The main ingredients of the modified gypsum cementitious material are: 40% gypsum, 30% slag powder, 20% steel slag powder, and 10% cement, wherein the gypsum is mixed with desulfurized gypsum and phosphogypsum at a mass ratio of 1:1;

[0073] The building admixture and its percentage per thousand to the mass of the main material are: retarder 2‰, water reducing agent 3‰, cellulose 0.5‰, PP fiber 1‰;

[0074] The aggregate is steel slag, the particle size of fine aggregate is 1-3mm, the dosage is 25%, the particle size of coarse aggregate is 3-5mm, and the dosage is 75%;

[0075] The performance is as follows:

[0076]

Embodiment 3

[0078] Three components of permeable concrete: modified gypsum cementitious material 20%, aggregate 75%, water 5%.

[0079] The main ingredients of the modified gypsum cementitious material are: 30% gypsum, 35% slag powder, 25% steel slag powder, and 10% cement. The gypsum is desulfurized gypsum, phosphogypsum and fluorogypsum in a mass ratio of 1:1:1 mix;

[0080] Construction admixtures and their percentages per thousand to the mass of main materials are: retarder 2‰, water reducing agent 2‰, cellulose 1‰, PP fiber 2‰;

[0081] The aggregate is steel slag, the particle size of fine aggregate is 1-3mm, the dosage is 10%, the particle size of coarse aggregate is 3-5mm, and the dosage is 90%;

[0082] The performance is as follows:

[0083]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses novel ecological permeable concrete. According to the permeable concrete, industrial by-products such as industrial by-product gypsum, steel slag, building waste and gravel made from tailing serve as main raw materials, the defect that traditional permeable concrete is high in production energy consumption can be overcome, the novel ecological permeable concrete is high in strength, low in cost and simple in preparing process, and does not need to be subjected to high-temperature calcination, the materials are easy to get, and environmental protection is facilitated.

Description

technical field [0001] The invention relates to a novel ecological permeable concrete and a preparation method thereof, belonging to the field of building materials and solid waste utilization. Background technique [0002] Ordinary concrete road pavement is simple and low in cost, which brings great convenience to people's travel. However, compared with natural soil, ordinary concrete pavement lacks the ability of breathing and rainwater penetration, which also brings problems such as the drop of groundwater level to the ecological environment of the city. , land subsidence, heat island effect, urban waterlogging and a series of environmental problems. In response to the above problems, permeable concrete came into being. [0003] Permeable concrete, also known as porous concrete, is essentially a building material mixed with aggregate, cementitious material, water and additives. Its strength mainly depends on the hardened cementitious material wrapped on the surface of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B38/00C04B11/26C04B11/036C04B111/20
CPCC04B11/036C04B11/26C04B11/262C04B11/264C04B28/147C04B2111/00284C04B2111/29C04B2201/50C04B18/141C04B18/142C04B7/02C04B2103/22C04B2103/302C04B24/383C04B38/00C04B16/0633
Inventor 李涛方爱华程雲周琳
Owner 上海每天生态科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com