Novel PVC tile and preparing method thereof

A polyvinyl chloride and resin technology, applied in the field of polyvinyl chloride (PVC) tiles and its preparation, can solve the problems of easily damaged bricks and tiles, easy corrosion of brick and tile materials, affecting roof shelter from wind and rain, etc., to reduce costs , enhance the anti-ultraviolet effect

Inactive Publication Date: 2016-12-07
无锡市天聚科技有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional roofs are paved with bricks and tiles, which are brittle and easily damaged, and bricks and tiles are easily corroded after long-term use, affecting the roof's wind and rain protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel PVC tile and preparing method thereof
  • Novel PVC tile and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Weigh 10Kg of polyvinyl chloride, 5Kg of wood flour, 0.3Kg of AC foaming agent, 2kg of magnesium powder, and 1kg of MBS resin and blend them in a high-speed mixer. The mixed sample was extruded through a sheet extruder into a corrugated sheet and co-extruded with a 0.8mm top layer of ASA. That is, a PVC solid tile with a length of 5m and a width of 1m;

Embodiment 2

[0019] Weigh 10Kg of polyvinyl chloride, 2Kg of wood flour, 0.8Kg of DPT foaming agent, 3kg of aluminum hydroxide, and 0.5kg of MBS resin and blend them in a high-speed mixer. The mixed sample was extruded into a corrugated sheet through a sheet extruder and co-extruded with a 2mm surface layer of PMMA. That is to get a PVC hollow tile with a length of 6m and a width of 3m;

Embodiment 3

[0021] Weigh 20Kg of polyvinyl chloride, 3Kg of straw powder, 0.4Kg of AC foaming agent, 1kg of magnesium powder, and 1kg of MBS resin and blend them in a high-speed mixer. The mixed sample was extruded through a sheet extruder into a corrugated sheet and co-extruded with a 0.5mm top layer of ASA. That is, a PVC solid tile with a length of 4m and a width of 2m;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel PVC tile and a preparing method thereof. The middle of the PVC tile is a downward concave arc, in other words, the PVC tile is wavy so as to facilitate drainage of a roof. The preparing method comprises the steps of preparing a PVC composite plate firstly, and then forming anti-UV resin surface layer on the upper surface of the plate through co-extrusion. The formula of the novel PVC tile comprises PVC, a foaming agent, a biobased material or inorganic filler, an MBS resin, an inorganic flame retardant and anti-UV resin. According to the PVC tile, on the premise that sun shading and rain sheltering are guaranteed, flame retardant property, light weight, sound insulation, attractiveness, aging resistance and heat insulation are all improved, cost can be reduced, and the environment-friendly requirement for sustainable development is met; the preparing method is simple, and industrialization can be achieved easily. Furthermore, installation is convenient, construction period is short, and the novel PVC tile can be widely applied to top surface installation of various buildings.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a novel polyvinyl chloride (PVC) tile and a preparation method thereof. Background technique [0002] Traditional roofs are paved with bricks and tiles, which are brittle and easily damaged, and bricks and tiles are easily corroded after long-term use, affecting the roof's wind and rain protection. Therefore, tiles made of asbestos tiles, resin tiles, and color steel tiles have emerged. [0003] The invention relates to a new type of polyvinyl chloride (PVC) tile and its preparation method, in order to enrich people's choice of roof tile materials, and the PVC roof tile has flame retardant, heat preservation, sound insulation, environmental protection, aesthetics, anti-ultraviolet and other aspects. All have a certain improvement, and the installation is convenient, the construction period is short, and it can be widely used in the top surface installation of various buildi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L51/04C08L97/02C08K3/08C08K3/26C08K3/22C08J9/10B32B27/30B32B27/18B32B27/20B32B1/00B32B27/08B32B33/00
CPCC08L27/06B32B1/00B32B27/08B32B27/18B32B27/20B32B27/304B32B27/308B32B33/00B32B2307/102B32B2307/304B32B2307/3065B32B2307/71C08J9/103C08J9/104C08J9/107C08J2327/06C08J2451/04C08J2497/02C08L2205/03C08L97/02C08L51/04C08K3/08C08K2003/2227C08K2003/265
Inventor 杨先刚
Owner 无锡市天聚科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com