Stainless steel passivating agent

A passivation agent, stainless steel technology, applied in the direction of metal material coating process, etc., can solve the problems such as the need to improve the protective film and the surface finish is not ideal, and achieve excellent rust prevention and good surface finish.

Inactive Publication Date: 2016-12-07
常熟市虞东磷化材料有限公司
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing stainless steel passivators are used for passivation treatment of metals to form a passivation protective film on the metal surface, but the antirust, abrasion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Passivating agent for stainless steel consists of the following components in parts by weight:

[0054] 1~2 parts of anhydrous borax,

[0055] 0.9 parts potassium chlorate,

[0056] 0.7 part calcium silicate powder,

[0057] 4.9 parts of tannins,

[0058] 1.8 parts hydroxypropyl methylcellulose,

[0059] 2.3 parts fatty amine polyoxyethylene ether,

[0060] 1.1 parts ammonium fluotitanate,

[0061] 1.3 parts sodium alkyl sulfate,

[0062] 0.7 part titanyl sulfate,

[0063] 44 parts deionized water.

Embodiment 2

[0065] Passivating agent for stainless steel consists of the following components in parts by weight:

[0066] 1 part anhydrous borax,

[0067] 0.9 parts potassium chlorate,

[0068] 0.7 part calcium silicate powder,

[0069] 4.9 parts of tannins,

[0070] 1.8 parts hydroxypropyl methylcellulose,

[0071] 2.3 parts fatty amine polyoxyethylene ether,

[0072] 1.1 parts ammonium fluotitanate,

[0073] 1.3 parts sodium alkyl sulfate,

[0074] 0.7 part titanyl sulfate,

[0075] 44 parts deionized water.

Embodiment 3

[0077] Passivating agent for stainless steel consists of the following components in parts by weight:

[0078] 2 parts anhydrous borax,

[0079] 0.9 parts potassium chlorate,

[0080] 0.7 part calcium silicate powder,

[0081] 4.9 parts of tannins,

[0082] 1.8 parts hydroxypropyl methylcellulose,

[0083] 2.3 parts fatty amine polyoxyethylene ether,

[0084] 1.1 parts ammonium fluotitanate,

[0085] 1.3 parts sodium alkyl sulfate,

[0086] 0.7 part titanyl sulfate,

[0087] 44 parts deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a stainless steel passivating agent which consists of the following components in parts by weight: 1-2 parts of borax anhydrous, 0.9 part of potassium chlorate, 0.7 part of silicon-calcium powder, 4.9 parts of tannic acid, 1.8 parts of hydroxyl propyl methylcellulose, 2.3 parts of fatty amine polyoxyethylene ether, 1.1 parts of ammonium hexafluorotitanate, 1.3 parts of alkyl sodium sulfovinate, 0.7 part of titanyl sulfate and 44 parts of deionized water. The stainless steel passivating agent disclosed by the invention can be used for passivating treatment of metal, so that a uniform passivating protective film is formed on the surface of the metal; and the protective film has excellent rust protection, abrasion resistance, corrosion resistance, heat resistance, cold resistance, weather resistance, and is good in surface smoothness.

Description

technical field [0001] The invention relates to a passivator for stainless steel. Background technique [0002] Existing stainless steel passivators are used for passivation treatment of metals to form a passivation protective film on the metal surface, but the antirust, abrasion resistance, corrosion resistance, heat resistance, cold resistance and weather resistance of the protective film need to be improved, and The surface finish is also less than ideal. Contents of the invention [0003] The purpose of the present invention is to provide a kind of stainless steel passivation agent, can be used for the passivation treatment of metal, forms uniform passivation protection film on the metal surface, and protection film has excellent antirust, abrasion resistance, corrosion resistance, heat resistance, Cold resistance, weather resistance, and good surface finish. [0004] For achieving the above object, technical scheme of the present invention is to design a kind of sta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C22/34
CPCC23C22/34
Inventor 钱文华
Owner 常熟市虞东磷化材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap