Method for obtaining oil absorption material by adopting melamine resin foam as matrix

A technology of melamine resin and oil-absorbing materials, which is applied in the field of oil pollution treatment, can solve the problems of further improvement of oil absorption rate and magnification, and achieve the effects of significant production cost and environmental protection, low density and large specific surface area

Inactive Publication Date: 2016-12-14
郑州峰泰纳米材料有限公司
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the oil absorption rate and magnification of existing products need to be further improved, and the ability to reuse such oil-absorbing materials needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for obtaining oil absorption material by adopting melamine resin foam as matrix
  • Method for obtaining oil absorption material by adopting melamine resin foam as matrix
  • Method for obtaining oil absorption material by adopting melamine resin foam as matrix

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The present embodiment provides a method for obtaining an oil-absorbing material based on melamine resin foam, comprising the following steps:

[0030] (1) Take the melamine resin foam, put it into the hydrophobic agent solution, and vacuum impregnate it at 80°C for 40 minutes;

[0031] (2) Take out the melamine resin foam containing the hydrophobic agent and perform rapid drying to obtain an oil-absorbing material based on the melamine resin foam.

[0032] The water-repellent agent solution is an ethanol solution of octadecyltrimethyloxysilane, and the weight ratio of octadecyltrimethyloxysilane to ethanol is 2:55.

[0033] Determination of the absorption rate and oil retention rate of the oil-absorbing material obtained in this embodiment in diesel oil and water is as follows:

[0034]

[0035]

Embodiment 2

[0037] The present embodiment provides a method for obtaining an oil-absorbing material based on melamine resin foam, comprising the following steps:

[0038] (1) Take the melamine resin foam, put it into the hydrophobic agent solution, and vacuum impregnate it at 25°C for 60 minutes;

[0039] (2) Take out the melamine resin foam containing the hydrophobic agent and perform rapid drying to obtain an oil-absorbing material based on the melamine resin foam.

[0040] The water-repellent agent solution is an ethanol solution of octadecyltrimethyloxysilane, and the weight ratio of octadecyltrimethyloxysilane to ethanol is 1:50.

[0041] Determination of the absorption rate and oil retention rate of the oil-absorbing material obtained in this embodiment in diesel oil and water is as follows:

[0042] Oil type

Embodiment 3

[0044] The present embodiment provides a method for obtaining an oil-absorbing material based on melamine resin foam, comprising the following steps:

[0045] (1) Take the melamine resin foam, put it into the hydrophobic agent solution, and vacuum impregnate it at 100°C for 20 minutes;

[0046] (2) Take out the melamine resin foam containing the hydrophobic agent and perform rapid drying to obtain an oil-absorbing material based on the melamine resin foam.

[0047] The water-repellent agent solution is an ethanol solution of octadecyltrimethyloxysilane, and the weight ratio of octadecyltrimethyloxysilane to ethanol is 5:60.

[0048] Determination of the absorption rate and oil retention rate of the oil-absorbing material obtained in this embodiment in diesel oil and water is as follows:

[0049]

[0050]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for obtaining an oil absorption material by adopting melamine resin foam as a matrix, and belongs to the technical field of oil pollution treatment. The method comprises the following steps that the melamine resin foam is placed in a hydrophobing agent solution, and vacuum impregnation is carried out for 20-60 minutes at the temperature of 25 DEG C to 100 DEGC; the melamine resin foam containing a hydrophobing agent is taken out and dried fast, a hydrophobing agent infusion with the melamine resin foam as the matrix is obtained, and the oil absorption material is obtained. According to the oil absorption material prepared by adopting the melamine resin foam as the matrix, the modifying method that the hydrophobing agent is loaded in a dipping mode is adopted, the method is a simple physical modifying method, the process is simple, cost is low, and the advantages of being porous, large in specific surface area, low in density, high in oil absorption performance and good in oil retention effect are achieved.

Description

technical field [0001] The invention relates to the technical field of oil pollution treatment, in particular to a method for obtaining an oil-absorbing material using melamine resin foam as a matrix. Background technique [0002] In recent years, with the vigorous development of the world's industry, petroleum and its products have entered the ocean, rivers and lakes and other water bodies due to various accidents during the process of mining, refining, storage, transportation and use, which will cause serious water pollution and affect the ecological environment. The threat to people's lives cannot be ignored. These oil spills form an oil film covering the water surface, which not only wastes precious oil resources, but also blocks the process of water-air exchange, affects the biological chain cycle, destroys the ecological balance of the water body, and causes serious harm to aquatic organisms. If it is not dealt with in time, it will bring great harm to our ecological ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/26B01J20/30C02F1/28
CPCB01J20/26B01J2220/4812C02F1/285C02F2103/007
Inventor 李洋洋
Owner 郑州峰泰纳米材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap