A kind of gold nanocup or gold nanobottle and preparation method thereof

A gold nano- and nano-structure technology, applied in nanotechnology, nanotechnology, nanotechnology for materials and surface science, etc., can solve the problem of uncontrollable blockage and release of drug molecules, uncontrollable pore size and density and other problems, to achieve a very high utilization rate of gold, a simple synthesis method, and a high degree of convenience

Active Publication Date: 2018-08-03
NANOSEEDZ
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the size and density of holes on the walls of gold nanocages cannot be controlled, so there is no controllability for drug molecule loading, pore blocking and release.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of gold nanocup or gold nanobottle and preparation method thereof
  • A kind of gold nanocup or gold nanobottle and preparation method thereof
  • A kind of gold nanocup or gold nanobottle and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] First prepare the following solutions:

[0033] 1. 0.5M thioacetamide aqueous solution: Weigh 3.7565g thioacetamide (analytical purity) and dissolve it in 100mL deionized water to fully dissolve it to form a colorless transparent solution;

[0034] 2. The concentration of 0.1M cetyltrimethylammonium bromide aqueous solution: Weigh 14.6g cetyltrimethylammonium bromide (analytical purity) and dissolve it in 400mL deionized water, heat and stir to fully dissolve it to form Colorless transparent solution;

[0035] 3. A 0.5M lead acetate aqueous solution: Weigh 8.1323g of lead acetate (analytical purity) and dissolve it in 50mL of deionized water to fully dissolve it to form a colorless and transparent solution;

[0036] 4. The concentration of 1M lead acetate aqueous solution: Weigh 6.005g of lead acetate (analytical purity) and dissolve it in 100mL of deionized water to fully dissolve it to form a colorless and transparent solution;

[0037] 5. Aqueous solution of tetrachloroauric ...

Embodiment 2-4

[0047] Example 2-4: The effect of the amount of the lead sulfide nanoparticle solution added in step 2 on the growth of the gold nanocup.

Embodiment 2

[0049] In this embodiment, except that the volume of the lead sulfide nanoparticle solution added in step 2 is 0.2 mL, the other steps are the same as in embodiment 1, and the size of the obtained gold nano bottle is 202 ± 15 nm ( Figure 5 ), the surface plasmon resonance spectrum is 768 nm ( Figure 4 , Line 4).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a gold nano-particle cup and a gold nano-particle bottle. The preparation method comprises the steps that (1) a lead sulfide nano-particle solution is prepared; (2) a lead sulfide gold hybrid nano-structure is prepared; (3) a lead sulfide template is removed selectively; and (4) the gold nano-particle cup or the gold nano-particle bottle is obtained. Through the preparation method, the lead sulfide gold hybrid nano-structure, the gold nano-particle cup and the gold nano-particle bottle can be obtained.

Description

Technical field [0001] The invention relates to the technical field of preparation of gold nanoparticles, in particular to a method for preparing a gold nano cup or a gold nano bottle based on a template method. Background technique [0002] Gold nanoparticles have good chemical stability and excellent physical and chemical properties. Due to the high free electron density and high conductivity of gold, gold nanoparticles exhibit excellent surface plasmon resonance properties. When resonance occurs, gold nanoparticles have a very high electric field strength enhancement effect, a great optical absorption and scattering cross-section. These properties have shown great applications in the fields of optical control, biotechnology, optoelectronic technology, solar technology, and microelectronics technology. prospect. [0003] So far, gold nanoparticles with a variety of morphologies have been prepared, such as gold nanospheres, gold nanorods, gold nanobicones, gold nanosheets, and g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F9/24B82Y30/00B82Y40/00
CPCB22F9/24B82Y30/00B82Y40/00
Inventor 江瑞斌阮琦锋王建方
Owner NANOSEEDZ
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com