LED-UV (light-emitting diode-ultraviolet) anti-doodling pollution-resisting coating and preparation method as well as use method thereof
An anti-graffiti and coating technology, applied in anti-fouling/underwater coatings, fire-resistant coatings, polyester coatings, etc., can solve the problems of oil-based anti-graffiti coatings with long drying time, poor VOC emission and environmental protection, and can not be used for outdoor construction. Achieve the effects of fast UV curing rate, excellent weather resistance and thermal stability, and low film-forming surface tension
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0039] Example 1
[0040] The LED-UV anti-graffiti and anti-fouling paint of this embodiment is composed of the following components by weight:
[0041] 4.5-functional fluorosilicone acrylate resin 25kg; low-energy curing special functional acrylic resin 25kg; 8-functional hyperbranched polyester acrylic resin 19.7kg; monomer 25kg; photoinitiator 4kg; wetting and dispersing agent 0.3kg; Foaming agent 0.4kg, anti-graffiti aid 0.6kg;
[0042] Get each component according to the weight shown in Example 1 in Table 1, and the preparation method is as follows:
[0043] Step 1, under the condition of avoiding sunlight or ultraviolet light, add 4.5-functional fluorosilicone acrylate resin, low-energy curing special functional acrylic resin, 8-functional hyperbranched polyester acrylic resin and monomer according to the above weight. Put it in the paint container and disperse it evenly, then add the photoinitiator and the wetting and dispersing agent in turn and stir at a stirring spee...
Example Embodiment
[0047] Example 2
[0048] 4.5-functional fluorosilicone acrylate resin 28kg; special functional acrylic resin 28kg; 8-functional hyperbranched polyester acrylic resin 15kg; monomer 22.3kg; photoinitiator 5kg; wetting and dispersing agent 0.5kg; defoamer 0.5kg ;Anti-graffiti aid 0.7kg;
[0049] Take each component according to the weight shown in Example 2 in Table 1, repeat the preparation method described in Example 1, wherein the stirring speed in step 1 is 600 rpm, and in step 2, the stirring speed is 900 rpm, The LED-UV anti-graffiti and anti-fouling paint of the present invention is obtained, and the performance of the paint liquid is tested.
[0050] Apply the LED-UV anti-graffiti and anti-fouling paint by brushing or spraying at a rate of 60g / m 2 Apply the same amount of coating on the surface of the coated object (decorative exterior wall, bus stop sign, communication and power facilities, etc.) that has been polished and dusted in advance. After the coating is compl...
Example Embodiment
[0051] Example 3
[0052] Take each component according to the weight shown in Example 3 in Table 1, repeat the preparation method described in Example 1, wherein the stirring speed in step 1 is 700 rpm, and the stirring speed in step 2 is 1000 rpm The LED-UV anti-graffiti and anti-fouling paint of the present invention is obtained, and the performance of the paint liquid is tested.
[0053] Apply the LED-UV anti-graffiti and anti-fouling paint by brushing or spraying at a rate of 70g / m 2 Apply the same amount of coating on the surface of the coated object (decorative exterior wall, bus stop sign, communication and power facilities, etc.) that has been polished and dusted in advance. After the coating is completed, use the LED-UV lamp to irradiate light for 7 seconds. The LED-UV anti-graffiti and anti-fouling paint coating film in Example 3 can be obtained. The performance test results are shown in the corresponding data of Example 3 in Table 2.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap