Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Compound additive for textile sizing, and preparation method thereof

A composite auxiliary agent and textile technology, which is applied in the field of textile sizing composite auxiliary agent and its preparation, can solve problems such as poor use effect, low technological content, and lack of environmental protection performance, and achieve strong practicability, increase sizing rate, and raw material cheap effect

Inactive Publication Date: 2017-05-31
WUJIANG BEISHE SHENGYUAN TEXTILE PROD AUXILIARIES PLANT
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the current domestic textile auxiliaries' poor use effect, low technological content, and lack of environmental protection performance, it is particularly necessary to develop a batch of new textile auxiliaries with excellent use functions and good environment to improve the market competitiveness of products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] (1) Accurately weigh 40 parts of ethylene glycol salicylate, 38 parts of fatty alcohol polyoxyethylene ether, 32 parts of polyvinylpyrrolidone, 20 parts of dioctyl sodium sulfosuccinate, and sorrel 15 parts of alcohol ester, 12 parts of sodium sulfite, 8 parts of dimethyl azobisisobutyrate, 6 parts of quinol dimethacrylate, 8 parts of cocamidopropyl betaine, 6 parts of sulfonated lignin, carrageenan 4 parts, 2 parts of zinc phenolsulfonate, 2 parts of aluminum hydroxide, 3 parts of palmitic acid, 3 parts of methylenebisacrylamide, 100 parts of deionized water;

[0023] (2) Add dimethyl azobisisobutyrate, quinol dimethacrylate, sulfonated lignin, carrageenan, zinc phenolsulfonate, and aluminum hydroxide into the ball mill, mill for 1 hour, and then pour The mixture was added deionized water, and stirred for 2 hours at a stirring rate of 1000 rpm to obtain a preliminary mixed solution;

[0024] (3) Send the preliminary mixture into the reaction kettle, add ethylene glyco...

Embodiment 2

[0028] (1) Accurately weigh 43 parts of ethylene glycol salicylate, 40 parts of fatty alcohol polyoxyethylene ether, 34 parts of polyvinylpyrrolidone, 23 parts of dioctyl sodium sulfosuccinate, and sorrel 18 parts of alcohol ester, 14 parts of sodium sulfite, 10 parts of dimethyl azobisisobutyrate, 8 parts of quinol dimethacrylate, 9 parts of cocamidopropyl betaine, 7 parts of sulfonated lignin, carrageenan 5 parts, 3 parts of zinc phenolsulfonate, 3 parts of aluminum hydroxide, 4 parts of citric acid, 4 parts of polyethylene glycol dimethacrylate, 100 parts of deionized water;

[0029] (2) Add dimethyl azobisisobutyrate, quinol dimethacrylate, sulfonated lignin, carrageenan, zinc phenolsulfonate, and aluminum hydroxide into the ball mill, mill for 1.5 hours, and then pour The mixture was added deionized water, stirred at a stirring rate of 1500 rpm for 2.5 hours to obtain a preliminary mixed solution;

[0030] (3) Send the preliminary mixture into the reaction kettle, add et...

Embodiment 3

[0034] (1) Accurately weigh 46 parts of ethylene glycol salicylate, 42 parts of fatty alcohol polyoxyethylene ether, 35 parts of polyvinylpyrrolidone, 26 parts of dioctyl sodium sulfosuccinate, and sorrel 21 parts of alcohol ester, 16 parts of sodium sulfite, 12 parts of dimethyl azobisisobutyrate, 10 parts of quinol dimethacrylate, 10 parts of cocamidopropyl betaine, 8 parts of sulfonated lignin, carrageenan 6 parts, 4 parts of zinc phenolsulfonate, 4 parts of aluminum hydroxide, 5 parts of linoleic acid, 5 parts of ethylene glycol diglycidyl ether, 100 parts of deionized water;

[0035] (2) Add dimethyl azobisisobutyrate, quinol dimethacrylate, sulfonated lignin, carrageenan, zinc phenolsulfonate, and aluminum hydroxide into the ball mill, mill for 2 hours, and then pour The mixture was added deionized water, and stirred for 3 hours at a stirring rate of 2000 rpm to obtain a preliminary mixed solution;

[0036] (3) Send the preliminary mixture into the reaction kettle, add ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a compound additive for textile sizing, and a preparation method thereof. The preparation method comprises the following steps: by taking glycol salicylate, fatty alcohol-polyoxyethylene ether, polyvinyl pyrrolidone and sodium dioctylsulfosuccinate as main components, adding sodium sulfite, dimethyl azobisisobutyrate, coconut oil amide propyl betaine, aluminum hydroxide, organic acid, a cross-linking agent and deionized water, and performing ball milling, stirring, emulsification, pH value adjustment, heating, holding, ultrasonic vibration, high-speed shearing and the like, so as to obtain the compound additive. After the prepared compound additive is used, textiles have the effect of remarkably increasing the sizing rate, the tensile strength of the textiles can be enhanced, the adhesion of dust can be decreased to meet the industrial demands, and thus the compound additive has better application prospects.

Description

technical field [0001] The invention relates to the technical field of textile auxiliaries, in particular to a composite auxiliaries for textile sizing and a preparation method thereof. Background technique [0002] Textile auxiliaries are necessary chemicals in the process of textile production and processing. Textile auxiliaries play an indispensable role in improving the product quality and added value of textiles. It can not only endow textiles with various special functions and styles, such as softness, wrinkle resistance, shrink resistance, waterproof, antibacterial, antistatic, flame retardant Etc., can also improve the dyeing and finishing process, play a role in saving energy and reducing processing costs. Textile auxiliaries are crucial to improving the overall level of the textile industry and their role in the textile industry chain. There are nearly 100 categories of textile auxiliaries in the world, producing nearly 16,000 varieties, with an annual output of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/45D06M11/56D06M13/188D06M13/203D06M13/224D06M13/256D06M13/322D06M13/46D06M15/01D06M15/03D06M15/356D06M15/53
CPCD06M13/224D06M11/45D06M11/56D06M13/188D06M13/203D06M13/2246D06M13/256D06M13/322D06M13/46D06M15/01D06M15/03D06M15/3562D06M15/53D06M2200/40
Inventor 钱华
Owner WUJIANG BEISHE SHENGYUAN TEXTILE PROD AUXILIARIES PLANT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com