Carbon steel wire processing technology

A processing technology, carbon steel technology, applied in the field of carbon steel wire processing technology, can solve the problems of a large amount of waste acid and increase costs, and achieve the effect of reducing waste acid recovery costs and production costs

Active Publication Date: 2018-07-03
重庆方略精控金属制品有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention intends to provide a carbon steel wire processing process, which is used to solve the problem that the existing process will produce a large amount of waste acid, which requires special equipment and methods for recycling, thereby increasing the cost of the enterprise due to waste disposal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon steel wire processing technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The present invention will be further described in detail below through specific implementations:

[0029] The reference signs in the drawings of the specification include: gas explosion chamber 1, rust removal chamber 2, air inlet 3, igniter 4, gas detector 5, sliding zone 6, positioning block 7, elastic layer 8, abrasive 9, inlet Material channel 10, shelf 11.

[0030] This embodiment is a carbon steel wire processing technology, and the specific processing steps are:

[0031] (1) Select carbon steel with a hardness of less than 85HRB, a weight of 200kg, and a diameter of 9mm as the raw material for carbon steel wire processing;

[0032] (2) Derusting carbon steel with hydrogen explosion derusting device;

[0033] (3) Quickly put the carbon steel that has been derusted into a phosphate solution with a concentration of 12-20g / L and a temperature of 75-85°C for 8-10 minutes to form a network of phosphating on the surface of the carbon steel. The film has the effect of preventin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of carbon steel wire machining, in particular to a carbon steel wire machining process. Compared with the prior art, in the scheme, a hydrogen explosion rust removal device is adopted for removing rust of carbon steel alloy materials, hydrogen is inflated into the device, shake generated by hydrogen explosion is used for achieving mutual friction of abrasive materials and carbon steel in the device, rust removal of the carbon steel is achieved, matter generated after hydrogen explosion only contains water, and therefore direct discharging can be achieved without retreatment. In this way, the problem that a large amount of waste acid will be generated in the existing process, special equipment and method are needed for recycling, and enterprise cost generated by treating waste is increased can be solved.

Description

Technical field [0001] The invention relates to the technical field of carbon steel wire processing, in particular to a carbon steel wire processing technology. Background technique [0002] Carbon steel wire is a steel wire processed from carbon steel. It has the characteristics of high strength, low relaxation, light weight and tensile strength. It is widely used in construction and industrial fields. At present, the general process for producing carbon steel wire is: material selection-rust removal-phosphating and saponification-wire drawing. Among them, the rust removal process uses dilute sulfuric acid with a temperature of 55-65° and a concentration of 10-25%. The carbon steel is placed in dilute sulfuric acid to remove the oxide layer on the surface; the phosphating process can make the surface of the carbon steel form a protective layer. Reticulated phosphating film; the saponification process can lubricate the surface of carbon steel. [0003] However, the above processi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21D1/32C21D8/06B24C1/08C23C22/05
CPCB24C1/086C21D1/32C21D8/065C23C22/05Y02P10/20
Inventor 张尧
Owner 重庆方略精控金属制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com