A kind of anti-riot helmet and preparation method thereof

A helmet and inner helmet technology, applied in helmets, helmet caps, caps and other directions, can solve the problems of reduced ballistic resistance, low structural strength, poor toughness of phenolic resin, etc., and achieve the effect of strong penetration resistance

Inactive Publication Date: 2018-05-08
FUJIAN QUANZHOU HAIBIN PROTECTIVE ARMANMENTS CO LTD
View PDF11 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, phenolic resin also has the defects of poor toughness and brittleness, and cannot give full play to the high strength and high modulus characteristics of aramid fiber. reduced performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A riot helmet, comprising an inner helmet body and an outer helmet body sheathed on the inner helmet body, the shape of the inner helmet body and the outer helmet body are the same, and the size of the outer helmet body is slightly larger than that of the inner helmet body, and the inner helmet body It is bonded together with the outer helmet body by an adhesive, the outer helmet body is made of PC / ABS alloy pellets melted and then injection molded, and the inner helmet body is made of multi-layer aramid fiber fabric layers impregnated with modified phenolic resin Made by molding; the PC / ABS alloy pellets are made of 80 parts of PC, 55 parts of ABS, 2 parts of polyethylene grafted maleic anhydride, 3 parts of modified sepiolite fiber, 0.5 part of inorganic filler, 0.5 part of antistatic agent, 0.2 part of dispersant and 0.2 part of antioxidant are mixed uniformly and placed in a twin-screw extruder through melt extrusion and granulation; the modified sepiolite fiber is 5...

Embodiment 2

[0034] A riot helmet, comprising an inner helmet body and an outer helmet body sheathed on the inner helmet body, the shape of the inner helmet body and the outer helmet body are the same, and the size of the outer helmet body is slightly larger than that of the inner helmet body, and the inner helmet body It is bonded together with the outer helmet body by an adhesive, the outer helmet body is made of PC / ABS alloy pellets melted and then injection molded, and the inner helmet body is made of multi-layer aramid fiber fabric layers impregnated with modified phenolic resin Molded and shaped; the PC / ABS alloy pellets are made of 85 parts of PC, 60 parts of ABS, 3.5 parts of polyethylene grafted maleic anhydride, 3.5 parts of modified sepiolite fiber, 0.8 part of inorganic filler, 0.7 part of antistatic agent, 0.3 part of dispersant and 0.3 part of antioxidant are mixed uniformly and then placed in a twin-screw screw machine through melt extrusion and granulation; the modified sepi...

Embodiment 3

[0045] A riot helmet, comprising an inner helmet body and an outer helmet body sheathed on the inner helmet body, the shape of the inner helmet body and the outer helmet body are the same, and the size of the outer helmet body is slightly larger than that of the inner helmet body, and the inner helmet body It is bonded together with the outer helmet body by an adhesive, the outer helmet body is made of PC / ABS alloy pellets melted and then injection molded, and the inner helmet body is made of multi-layer aramid fiber fabric layers impregnated with modified phenolic resin Molded and shaped; the PC / ABS alloy pellets are made of 90 parts of PC, 65 parts of ABS, 5 parts of polyethylene grafted maleic anhydride, 4 parts of modified sepiolite fiber, 1 part of inorganic filler, 1 part of antistatic agent, 0.4 part of dispersing agent and 0.4 part of antioxidant are mixed uniformly and then placed in a twin-screw screw machine through melt extrusion and granulation; the modified sepiol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
weightaaaaaaaaaa
Login to View More

Abstract

The invention discloses an antiriot helmet and a preparing method thereof. The antiriot helmet comprises an inner helmet body and an outer helmet body arranged on the inner helmet body in a sleeving mode. The inner helmet body and the outer helmet body are attached together through an adhesive. The outer helmet body is prepared through injection molding after melting of PC / ABS alloy aggregates. The inner helmet body is prepared through molding of multiple layers of aramid fiber fabric layers dipped with modified phenolic resin. The antiriot helmet effectively resists the attacks of bullets, edge tools, clubs, non-explosive projectiles and chemical liquid and effectively protects the head, face and neck of a human body.

Description

technical field [0001] The invention relates to the technical field of military helmets, in particular to an anti-riot helmet and a preparation method thereof. Background technique [0002] Anti-riot helmets are the protective equipment that individual soldiers must wear in the process of performing anti-riot tasks, and have always been valued by the armies of various countries. Anti-riot helmets are mostly made of metal materials and are used to resist the attacks of sharp weapons, sticks, non-explosive projectiles and chemical liquids, so as to effectively protect the head, face and neck of the human body. Now under the new anti-terrorism and anti-riot situation, the Equipment Development Department of the Central Military Commission has put forward higher requirements for anti-riot helmets, requiring anti-riot helmets to have a certain bullet-proof function, that is, to protect the 97-1 shotgun from launching the 97-type 18.4mm Capability of killing bullets. [0003] At...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A42B3/06A42B3/04A42B3/00C08L69/00C08L55/02C08L51/06C08K13/06C08K9/02C08K7/10C08K3/34C09J4/06C09J4/02D06M17/00D06M15/41F41H1/08D06M101/36
CPCA42B3/003A42B3/0406A42B3/06C08L69/00C08L2205/03C09J4/00C09J4/06D06M15/412D06M17/00D06M2101/36F41H1/08C08L55/02C08L51/06C08K13/06C08K9/02C08K7/10C08K3/34
Inventor 王烺烺
Owner FUJIAN QUANZHOU HAIBIN PROTECTIVE ARMANMENTS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com