Novel fire retardant anticorrosion fiber bamboo material

A fiber and new technology, applied in the field of flame retardant and anti-corrosion fiber bamboo materials, can solve the problems of poor stability, poor corrosion resistance, environmental pollution, etc., and achieve the effect of high stability and excellent flame retardant and anti-corrosion performance.

Inactive Publication Date: 2017-11-21
WUXI BODA BAMBOO & WOOD INDAL
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing fiber bamboo materials are generally flammable, poor in stability, easy to mold in a humid environment, poor in corrosion resistance, overall not environmentally friendly, and easy to cause environmental pollution and energy waste

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of novel flame-retardant and anti-corrosion fiber bamboo material of the present invention, by weight, it comprises following components,

[0027] (1) 62 pieces of shredded bamboo made from raw bamboo;

[0028] (2) 28 parts of guanidinourea hydroxymethyl phosphate;

[0029] (3) 25 parts of boric acid;

[0030] (4) 16 parts of diammonium hydrogen phosphate;

[0031] (5) 9 parts of ammonium sulfate;

[0032] (6) 4 parts of antifungal agent;

[0033] (7) 4.5 parts of carboxymethyl cellulose;

[0034] (8) 2.3 parts of nano titanium dioxide;

[0035] (9) 1.2 parts of modified bentonite;

[0036] (10) 0.4 part of perlite powder;

[0037] Its preparation method includes:

[0038] (1) Mix and soak the above raw materials evenly;

[0039] (2) Dry the bamboo silk after the flame-retardant and anti-corrosion treatment at a temperature of 68°C until the absolute moisture content does not exceed 15%;

[0040] (3) Send the dried bamboo filaments into the carbonizatio...

Embodiment 2

[0046] A kind of novel flame-retardant and anti-corrosion fiber bamboo material of the present invention, by weight, it comprises following components,

[0047] (1) 73 pieces of shredded bamboo made from raw bamboo;

[0048] (2) 34 parts of guanidinourea hydroxymethyl phosphate;

[0049] (3) 29 parts of boric acid;

[0050] (4) 17 parts of diammonium hydrogen phosphate;

[0051] (5) 8 parts of ammonium sulfate;

[0052] (6) 5 parts of antifungal agent;

[0053] (7) 4.6 parts of carboxymethyl cellulose;

[0054] (8) 2.8 parts of nano titanium dioxide;

[0055] (9) 1.4 parts of modified bentonite;

[0056] (10) 0.6 part of perlite powder;

[0057] Its preparation method includes:

[0058] (1) Mix and soak the above raw materials evenly;

[0059] (2) Dry the bamboo filaments treated with fire-retardant and anti-corrosion treatment at a temperature of 75°C until the absolute moisture content does not exceed 15%;

[0060] (3) Send the dried bamboo filaments into the carbo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a novel fire retardant anticorrosion fiber bamboo material. The novel fire retardant anticorrosion fiber bamboo material comprises 55-78 parts of bamboo filaments made from raw bamboo, 24-36 parts of hydroxymethyl amidinourea phosphate, 22-30 parts of boric acid, 15-18 parts of diammonium hydrogen phosphate, 5-10 parts of ammonium sulfate, 3-6 parts of a mildew preventive, 4-5 parts of carboxymethylcellulose, 2-3 parts of nanometer titania, 1-2 parts of modified bentonite and 0.3-0.7 part of crushed crude pearlite. A preparation method of the novel fire retardant anticorrosion fiber bamboo material comprises the steps that raw materials are mixed and dried, dried bamboo filaments are fed into a carbonization pyrolytic kiln, cooled, then fed into the carbonization pyrolytic kiln again and finally subjected to gum dipping, drying after gumming, pressing, solidifying, body curing and slicing in sequence. The novel fire retardant anticorrosion fiber bamboo material is good in fire retardance, corrosion resistance and stability, and is environmentally friendly.

Description

technical field [0001] The invention relates to a bamboo material, in particular to a flame-retardant and anti-corrosion fiber bamboo material. Background technique [0002] Bamboo is the second forest resource in our country. It is a renewable resource. Once it becomes a forest, it can be used sustainably as long as it is properly managed. Existing fiber bamboo materials are generally flammable, have poor stability, are prone to mold in humid environments, have poor corrosion resistance, are not environmentally friendly as a whole, and are likely to cause environmental pollution and energy waste. Contents of the invention [0003] Purpose of the invention: the purpose of the present invention is to overcome the deficiencies in the prior art and provide a novel flame-retardant and anti-corrosion fiber bamboo material with good flame-retardant and anti-corrosion performance, good stability and environmental protection. [0004] Technical solution: In order to solve the abo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27K3/04B27K3/52B27K5/04B27K9/00B27M1/06B27N1/02B27N3/04B27N3/08B27N3/12
CPCB27K3/52B27K3/04B27K5/04B27K9/002B27K2240/20B27M1/06B27N1/02B27N3/04B27N3/08B27N3/12
Inventor 孙国强
Owner WUXI BODA BAMBOO & WOOD INDAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap