High-strength unmanned aerial vehicle wing, wing processing system and wing processing method

A processing system and machining technology, which is applied in the direction of wings, unmanned aircraft, motor vehicles, etc., can solve the problems of easy fading and breaking of wings

Active Publication Date: 2021-07-06
天和无人机科技溧阳有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a wing to solve the technical problem that the traditional UAV wing is easy to fade and break

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength unmanned aerial vehicle wing, wing processing system and wing processing method
  • High-strength unmanned aerial vehicle wing, wing processing system and wing processing method
  • High-strength unmanned aerial vehicle wing, wing processing system and wing processing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] figure 1 A schematic diagram of the structure of the wing is shown.

[0044] like figure 1 As shown, Embodiment 1 provides a wing 1a, and the wing 1a is suitable for being made of a polypropylene microporous foam sheet.

[0045] Further, the wingtip 2a of the wing 1a is bent upwards, and a flap installation position is provided on the outer wing of the wing 1a. When the flap 3a is installed in the flap installation position, it is controlled by the steering gear, and the The bottom surface of the wing is provided with a steering gear placement groove 4a.

[0046] And the bottom surface of the wing is also provided with a reinforcing rib insertion groove 5a, and the reinforcing rib insertion groove can also be used as a wiring groove simultaneously.

[0047] After the wing is made of polypropylene microcellular foamed sheet, it has the advantages of lightness and toughness made of polypropylene microcellular foamed sheet, and makes the wing resistant to stretching, co...

Embodiment 2

[0051] Aiming at the technical problem of difficult mechanical processing of polypropylene microcellular foamed sheet, the first step of the present invention is to make the polypropylene microcellular foamed sheet meet the processing hardness required for mechanical processing, and then perform mechanical processing by a numerical control machining center.

[0052] figure 2 is the top view of the wing processing system;

[0053] like figure 2 As shown, on the basis of Embodiment 1, Embodiment 2 provides a wing processing system.

[0054] The wing processing system includes:

[0055] Soaking tank, soaking polypropylene microporous foam board;

[0056] A drying device for drying the soaked polypropylene microcellular foamed sheet to harden it; and

[0057] Numerical control machining center, the polypropylene microporous foam plate after hardening is mechanically processed into the wing as described in embodiment 1; And

[0058] The grasping and conveying mechanism is us...

Embodiment 3

[0072] Present embodiment 3 provides a kind of wing processing method, namely

[0073] The polypropylene microcellular foamed sheet is used as a raw material, and is machined into a wing as described in Example 1.

[0074] The working method is described below by taking the wing as an example.

[0075] Figure 4 Shown is a flow chart of a method for preparing a wing using a polypropylene microporous foam board as a raw material.

[0076] Concretely, adopting polypropylene microporous foam board material as raw material to prepare the method for wing comprises the following steps:

[0077] Step S1, increasing the processing hardness of the polypropylene microcellular foamed sheet;

[0078] Step S2, cutting the polypropylene microcellular foamed sheet by the numerical control machining center described in embodiment 1, to form the semi-finished product of the wing; and

[0079] Step S3, performing thermocompression molding on the semi-finished airfoil.

[0080] Further, as ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-strength wing, a wing processing system and a processing method thereof, wherein the wing is suitable for being made of a polypropylene microporous foam plate, and the wing is made of a polypropylene microporous foam plate After completion, it has the advantages of lightness and toughness made of polypropylene microcellular foam board, and improves the tensile, compression, torsion and impact resistance of the wing, prolonging the service life of the drone.

Description

technical field [0001] The invention relates to the field of unmanned aerial vehicles, in particular to a high-strength wing made of microporous foam plates, a wing processing system and a wing processing method. Background technique [0002] Polymer microporous foam material specifically refers to a polymer porous foam material with a cell size of less than 100 μm and a cell density greater than 1.0×106 cells / cm 3 . Due to its light weight, high strength, and material saving characteristics, microcellular foam materials have broad application prospects. Among many polymer microcellular foam materials, polypropylene (PP) microcellular foam materials have good mechanical properties, high heat distortion temperature, chemical resistance and other properties, and the cells are interconnected. Open-cell polypropylene microporous foam materials can be used in fields such as filtration, separation, sound absorption and ventilation. [0003] Therefore, this material is widely use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B64C3/00B29D99/00
CPCB64C3/00B29D99/0025B64U10/25
Inventor 戎海龙刘阳居竹青
Owner 天和无人机科技溧阳有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap