Organic silicon modified acrylate emulsion and preparation method thereof

An acrylate and organosilicon technology, applied in the field of organosilicon modified acrylate emulsion and its preparation, can solve the problems of poor water resistance, easy to become brittle, easy to stick, and achieve good emulsion stability, strong cohesion, The effect of reaction temperature saving

Inactive Publication Date: 2012-10-10
DONGHUA UNIV
View PDF9 Cites 45 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, acrylate emulsions have disadvantages such as poor water resistance, easy stickiness at high temperature, and easy brittleness at low temperature, which limit its wider application, so it is necessary to modify it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic silicon modified acrylate emulsion and preparation method thereof
  • Organic silicon modified acrylate emulsion and preparation method thereof
  • Organic silicon modified acrylate emulsion and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] The application examples given below can synthesize the core-shell emulsion described in this patent, and the ratio of experimental raw materials is listed in Table 1.

[0050] ⑴ Pre-emulsification

[0051] ① Pre-emulsification of the core layer: add a part of the composite emulsifier, a part of deionized water, the acrylate mixed monomer of the core layer, and vinyl polysiloxane prepolymer into the pre-emulsification kettle a in sequence, and the temperature rises to 45±0.2 ℃, with a rotation speed of about 1000r / min, stir mechanically for 30-45 minutes to prepare the core layer pre-emulsion, pour it into the core layer pre-emulsion dripping kettle, and set aside.

[0052] ② Shell pre-emulsification: add a part of composite emulsifier, a part of deionized water, shell acrylate mixed monomer, hydrophilic monomer and cross-linking monomer into the pre-emulsification tank b in sequence, and the temperature is raised to 45 ±0.2°C, stir mechanically for 30 minutes at a rot...

Embodiment 2

[0064] The preparation method is the same as in Example 1, and the reaction temperature, mechanical stirring speed, heat preservation time, etc. can be appropriately changed, wherein the experimental raw material proportioning is listed in Table 2.

[0065] Table 2 Components of silicone-modified acrylate emulsion with core-shell structure

[0066]

[0067] Note: 1) The emulsifier is divided into two parts, and the mass fraction of the core-shell layer is 63.00% and 37.00% respectively.

Embodiment 3

[0069] Preparation method is with embodiment 2, and wherein experimental raw material proportioning is listed in table 3.

[0070] Table 3 Components of silicone-modified acrylate emulsion with core-shell structure

[0071]

[0072] Note: 1) The emulsifier is divided into two parts, and the mass fraction of the core-shell layer is 66.00% and 34.00%, respectively.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to organic silicon modified acrylate emulsion and a preparation method thereof. A core-shell structure synthesis method is adopted for preparation, a core layer / shell layer glass transition temperature is designed to be -30- -25 DEG C / 0-5 DEG C and lower than conventional core-shell emulsion. The emulsion comprises core-shell emulsion monomers, initiator accounting for 0.4-0.6% of the total mass of the monomers, composite emulsifier accounting for 2.5-4.5% of the total mass of the monomers, pH (potential hydrogen) buffering agent accounting for 0.4-0.6% of the total mass of the monomers and the balance deionized water. The emulsion preparation method includes (1) pre-emulsifying, (2) core-layer emulsion preparation, and (3) core-shell emulsion preparation. The emulsion which is aqueous emulsion is environment-friendly and high in stability, bonding power and tensile strength, has functions of softening, smoothening and the like for surface treatment of fabrics and the like, and is widely applicable to the fields of spinning, papermaking, leather, painting, water-based ink and the like.

Description

technical field [0001] The invention belongs to the field of acrylate water-based emulsions, in particular to an organosilicon-modified acrylate emulsion and a preparation method thereof. Background technique [0002] Acrylate emulsion has many outstanding advantages, such as excellent weather resistance, light resistance, acid and alkali corrosion resistance, good adhesion, and then has excellent decoration and durability, smooth coating surface, good stain resistance, construction range Wide range, low cost, high cost performance and other characteristics, it is widely used in textile, coating and other fields. However, acrylate emulsion has disadvantages such as poor water resistance, easy stickiness at high temperature, and brittleness at low temperature, which limits its wider application, so it is necessary to modify it. [0003] On the one hand, due to its low surface energy, high and low temperature resistance, and water resistance, silicone prepolymers or high poly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F283/12C08F220/18C08F212/08C08F220/14C08F220/06C08F220/56C08F220/28C08F220/32C08F222/14C08F222/20C08F4/40C08F2/26C08F2/30
Inventor 徐小刚杜鹃罗艳钟毅汪娇宁
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com