High-hardness metal protective layer wear-resistant cutting pick

A metal protective layer, high hardness technology, applied in the field of pick processing, can solve the problems of damage and failure of picks, non-wear-resistance of pick shanks, and inability to fully utilize the efficiency of mining machinery.

CN107604356AInactive Publication Date: 2018-01-19太湖县众瑞精密铸造有限公司
2 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
Publication Date
2018-01-19
Estimated Expiration
Not applicable · inactive patent
Patent Text Reader

Abstract

The invention discloses a wear-resistant pick with a high-hardness metal protective layer, which comprises a pick body. A high-hardness metal protective layer is clad on the head of the pick by using a plasma cladding method on the head of the pick body; The high-hardness metal protective layer is composed of 60-90 parts of diamond, 30-50 parts of recovered wax, 5-15 parts of stearic wax, 5-20 parts of paraffin wax, 2-10 parts of borax, and quartz powder in parts by weight. 8‑20 parts, 1‑2 parts of iron oxide, 1‑2 parts of calcium oxide. Due to the rational use of diamond, recycled wax, and stearic wax in the present invention, the obtained metal protective layer has the characteristics of high hardness, good toughness, wear resistance and impact resistance, etc., which protects the head of the pick tooth body well and reduces the head of the pick. The wear speed of the inner tooth body is controlled, so that the tooth body and the alloy head wear synchronously to achieve the best fit, greatly improving the wear resistance and service life of the pick.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to the field of pick processing, in particular to a wear-resistant pick with a high-hardness metal protective layer. Background technique

[0002] The pick is one of the vulnerable parts in coal mining and tunneling machinery. It is the main tool for coal falling and crushing. Its performance directly affects the production capacity, power consumption, working stability and stability of coal mining machinery. The service life of other related parts. The general structure is to inlay the hard alloy cutter head on the quenched and tempered low alloy structural steel cutter body.

[0003] At present, although the hard alloy pick head used has better wear resistance than steel, it still cannot meet the service life requirements, and due to the poor life of this kind of pick, it leads to frequent replacement of picks, making The efficiency of mining machinery cannot be fully utilized. At the same time, because the pick shank is made...

Examples

Embodiment 3

[0038] A wear-resistant pick with a high-hardness metal protective layer of the present invention comprises a pick body, and a high-hardness metal protective layer is clad on the head of the pick by adopting a plasma cladding method on the head of the pick body; The above-mentioned high-hardness metal protective layer is made of the following raw materials in parts by weight:

[0039] Diamond: 90 parts, recycled wax: 50 parts, stearin wax: 15 parts, paraffin wax: 20 parts, borax: 10 parts, quartz powder: 20 parts, iron oxide: 2 parts, calcium oxide: 2 parts.

[0040] The cladding method of the above-mentioned high-hardness metal protective layer comprises the following steps:

[0041] a mixing the above-mentioned raw materials to obtain a metal composition;

[0042] b Press the metal composition above to obtain a green body, and bake it at a temperature of 350°C for 60 minutes;

[0043] c The baked green body is isostatically sintered under anaerobic conditions, the sinterin...