Transparent color glass coating used for film coating

A technology of stained glass and glass coating, applied in the direction of coating, etc., can solve the problems of poor adhesion, low hardness, poor uniformity of coating film, etc., and achieve the effect of strong adhesion, high hardness, uniform and complete coating film

Inactive Publication Date: 2018-02-02
TIANJIN CITY XINLIHUA COLOR MATERIAL
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Glass coating is a kind of coating. The glass surface is usually very smooth. Ordinary coatings are difficult to adhere to the glass surface. Good glass coatings form a stable and hard paint film on the glass surface, which will show high transparency and high gloss in appearance. At present, most of the colored glass coatings on the market have poor film uniformity, poor adhesion and low hardness.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0017] 60% silicone resin, 12% hexamethoxymethylmelamine formaldehyde resin, 3% alcohol-soluble pigments of various colors, 1% nano-silica, 0.4% nano-titanium dioxide, 6% ultra-fine talc, KH-560 silane coupling agent 1 %, organic bentonite 2%, Byk-310 1%, Byk-358 0.5%, Byk-052 0.5%, Byk-p104s 1%, propylene glycol methyl ether 5% and ethylene glycol ether acetate 5%.

specific Embodiment 2

[0018] 80% silicone resin, 20% hexamethoxymethylmelamine formaldehyde resin, 6% alcohol-soluble pigments of various colors, 2% nano-silica, 0.8% nano-titanium dioxide, 10% ultra-fine talc powder, 1.5 KH-560 silane coupling agent %, organic bentonite 5%, Byk-3103%, Byk-358 1.5%, Byk-052 1.5%, Byk-p104s 3%, propylene glycol methyl ether 10% and ethylene glycol ether acetate 15%.

specific Embodiment 3

[0019] 70% silicone resin, 16% hexamethoxymethylmelamine formaldehyde resin, 4.5% alcohol-soluble pigments of various colors, 1.5% nano-silica, 0.6% nano-titanium dioxide, 8% ultra-fine talc, 1.25 KH-560 silane coupling agent %, organic bentonite 3.5%, Byk-310 2%, Byk-358 1.0%, Byk-052 1.0%, Byk-p104s 2%, propylene glycol methyl ether 7.5% and ethylene glycol ether acetate 10%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a transparent color glass coating used for film coating. The glass coating comprises the following components in percentages by weight: 60 to 80% of organosilicon resin, 12 to20% of hexamethoxymethyl melamine formaldehyde resin, 3 to 6% of alcohol-soluble pigments with various colors, 1 to 2% of nanometer silicon dioxide, 0.4 to 0.8% of nanometer titanium dioxide, 6 to 10%of superfine talc powder, 1 to 1.5% of a silane coupling agent KH-560, 2 to 5% of organic bentonite, 1 to 3% of Byk-310, 0.5 to 1.5% of Byk-358, 0.5 to 1.5% of Byk-052, 1 to 3% of Byk-p104s, 5 to 10%of propylene glycol methyl ether and 5 to 15% of ethylene glycol monomethyl acetate. The transparent color glass coating provided by the invention has the advantages of excellent etching effect, goodtransparent effect, rapidness, high efficiency, uniform and complete film coating, strong adhesive force, high hardness and good popularization value.

Description

【Technical field】 [0001] The invention relates to a frosted glass coating, in particular to a transparent colored glass coating for film coating. 【Background technique】 [0002] Glass coating is a kind of coating. The glass surface is usually very smooth. Ordinary coatings are difficult to adhere to the glass surface. Good glass coatings form a stable and hard paint film on the glass surface, which will show high transparency and high gloss in appearance. At present, most of the colored glass coatings on the market have poor film uniformity, poor adhesion and low hardness. For this purpose, we propose a transparent stained glass paint for coating. 【Content of invention】 [0003] The main purpose of the present invention is to provide a kind of transparent colored glass paint for coating, which has good etching effect, good transparency effect, fast and efficient, uniform and complete coating film, strong adhesion and high hardness, and has good promotion value. Effective...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D161/32C09D7/61C09D7/62
CPCC09D183/04C08K2201/011C08L2201/10C08L61/32C08K13/02C08K3/36C08K2003/2241C08K3/34C08K3/346
Inventor 张崇亮赵洪庆廉海跃
Owner TIANJIN CITY XINLIHUA COLOR MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap